Doped lithium manganese oxide compounds and methods of...

Details Doped lithium manganese oxide compounds and methods of... Doped lithium manganese oxide compounds and methods of...

1999-11-19

2002-03-26

Bos, Steven (Department: 1754)

Chemistry of inorganic compounds

Oxygen or compound thereof

Metal containing

C423S594120, C423S596000, C423S598000, C429S224000

Reexamination Certificate

active

06361756

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to lithium manganese oxides for use in rechargeable lithium and lithium-ion secondary batteries and to methods of making lithium manganese oxides.
BACKGROUND OF THE INVENTION
Rechargeable lithium and lithium-ion secondary batteries are presently used in portable electronics applications and are potential long-term candidates for powering emission-free vehicles. At present, LiCoO
2
, LiNiO
2
and LiMn
2
O
4
are considered to be the most attractive cathode (positive electrode) materials for use in lithium and lithium-ion batteries. LiNiO
2
and LiCoO
2
both have high theoretical capacities of about 275 mAh/g. However, the full capacity of these compounds cannot be achieved in practice and only about 140-150 mAh/g can be utilized. Further removal of lithium from LiNiO
2
and LiCoO
2
further decreases the cycleability of these compounds and causes exothermic decomposition of the oxide. This decomposition releases oxygen at elevated temperatures thus producing safety hazards. LiNiO
2
, in particular, raises safety concerns because it exhibits a sharper exothermic reaction at a lower temperature than LiCoO
2
. In addition to these problems, both cobalt and nickel are relatively expensive thus increasing the cost of using these compounds.
LiMn
2
O
4
is often considered a desirable alternative to LiNiO
2
and LiCoO
2
because it is cheaper and because it is believed to be safer on overcharge. In particular, LiMn
2
O
4
generally has no removable lithium to plate the anode when it is overcharged. Moreover, the end of charge member, MnO
2
, is believed to be more stable than CoO
2
and NiO
2
, the end of charge members of LiCoO
2
and LiNiO
2
, respectively. Nevertheless, the theoretical capacity of LiMn
2
O
4
is only 148 mAh/g and typically no more than about 115-120 mAh/g can be obtained with good cycleability.
LiMnO
2
has traditionally been of great interest for use as a positive electrode material because it has a large theoretical capacity (280 mAh/g). Furthermore, LiMnO
2
has a stable end of charge member (MnO
2
) and is a relatively inexpensive compound to produce. Typically, LiMnO
2
is present in an orthorhombic crystalline form. When cycled in a rechargeable lithium or lithium-ion battery, this orthorhombic form converts into a spinel form having a 4V plateau (cubic phase) and a 3V plateau (tetragonal distorted spinel phase). Unfortunately, however, this spinel form loses capacity rapidly when it is cycled through both plateaus. Therefore, this form has not found much utility in lithium and lithium-ion batteries.
In order to provide a LiMnO
2
compound that is suitable for lithium and lithium-ion batteries, there have been attempts to produce LiMnO
2
with a layered crystalline structure analogous to the layered structure of LiCoO
2
and LiNiO
2
. For example, a LiMnO
2
phase has been produced through ion exchange that has the same layered cation distribution as LiCoO
2
. See A. Armstrong and P. G. Bruce,
Nature
381, 499 (1996). The crystalline structure of this layered phase is monoclinic because of the Jahn Teller effect. The stability of the material is poor, however, and the capacity diminishes within only tens of cycles.
Recently, Jang et al. described a layered compound LiMn
1−x
Al
x
O
2
having a monoclinic crystalline structure and prepared in a solid state reaction at temperatures exceeding 900° C. See Y. Jang et al.,
Electrochemical and Solid
-
State Letters
1, 13 (1998). The aluminum-doped material produced by Yang et al. was shown to have better cycleability than layered LiMnO
2
and was able to sustain more than 20 cycles. But the reversible capacity of this material is only about 110 mAh/g, far below the theoretical capacity. Moreover, after only a few cycles, this material converts to the spinel form having separate plateaus at 3 V and 4 V and thus loses capacity quickly through cycling.
SUMMARY OF THE INVENTION
The present invention includes lithium manganese oxide compounds of the formula:
LiMn
1−x
[A]
x
O
2
wherein 0<x<0.5, [A] is a combination of two or more dopants, and the average oxidation state N of the dopant combination [A] is +2.8≦N≦+3.2. For these compounds, N is preferably about +3.0 and 0<x≦0.4. Preferably, at least one of the dopants is either titanium or zirconium.
In one embodiment of the invention, x=a and [A]
x
is A
1
a/2
A
2
a/2
. According to this embodiment, A
1
is Ti, Zr, or a combination thereof; and A
2
is Mg, Ca, Sr, Zn, Ba, or a combination thereof. More preferably, A
1
is Ti, A
2
is Mg and 0<a≦0.4.
In a second embodiment of the invention, the lithium manganese oxide compound of the invention has the formula LiMn
1−b
Ni
c
A
0
d
A
1
e
A
2
f
O
2
, wherein A
0
is Cr, Co, or a combination thereof; A
1
is Ti, Zr, or a combination thereof; A
2
is Mg, Ca, Sr, Zn, Ba, or a combination thereof; b=c+d+e+f; 0.1≦b≦0.5; 0.1≦c≦0.3; 0d≦0.4; 0≦e≦0.2; 0≦f≦0.2, and the average oxidation state N of the dopant combination [Ni, A
0
, A
1
, A
2
] is +2.8≦N≦+3.2. Preferably, in this embodiment, A
0
is Cr, A
1
is Ti, A
2
is Mg, and N is about +3.0.
The present invention also includes lithium and lithium-ion secondary batteries that include the above lithium manganese compounds as the positive electrode material. In addition, the present invention includes dilithiated forms of the lithium manganese oxide compounds of the invention having the formula Li
1−z
Mn
1−x
[A]
x
O
2
, wherein 0≦z≦1.
The present invention further includes methods of preparing lithium manganese compounds having the formula LiMn
1−x
[A]
x
O
2
wherein 0<x≦0.5, [A] is a combination of two or more dopants, and the average oxidation state N of the dopant combination [A] is +2.8≦N≦+3.2. The methods of the invention forms these compounds by first mixing together source compounds containing lithium, manganese and [A] in amounts corresponding to the formula LiMn
1−x
[A]
x
O
2
wherein 0<x≦0.5, [A] is a combination of two or more dopants, and the average oxidation state N of the dopant combination [A] is +2.8≦N≦+3.2. The mixture of source compounds is then fired (heated) at a temperature of greater than 700° C., and preferably between 800° C. and 1000° C. to produce the LiMn
1−x
[A]
x
O
2
compound.


REFERENCES:
patent: 4497726 (1985-02-01), Brule et al.
patent: 4507371 (1985-03-01), Thackeray et al.
patent: 4546058 (1985-10-01), Charkey et al.
patent: 4668595 (1987-05-01), Yoshino et al.
patent: 4749634 (1988-06-01), Sammells
patent: 4770960 (1988-09-01), Nagaura et al.
patent: 4956247 (1990-09-01), Miyazaki et al.
patent: 5028500 (1991-07-01), Fong et al.
patent: 5084366 (1992-01-01), Toyoguchi
patent: 5147738 (1992-09-01), Toyoguchi
patent: 5160712 (1992-11-01), Thackeray et al.
patent: 5169736 (1992-12-01), Bittihn et al.
patent: 5180574 (1993-01-01), Von Sacken
patent: 5196278 (1993-03-01), Idota
patent: 5244757 (1993-09-01), Takami et al.
patent: 5264201 (1993-11-01), Dahn et al.
patent: 5286582 (1994-02-01), Tahara et al.
patent: 5316877 (1994-05-01), Thackeray et al.
patent: 5370949 (1994-12-01), Davidson et al.
patent: 5478671 (1995-12-01), Idota
patent: 5478672 (1995-12-01), Mitate
patent: 5478673 (1995-12-01), Funatsu
patent: 5478674 (1995-12-01), Miyasaka
patent: 5487960 (1996-01-01), Tanaka
patent: 5494762 (1996-02-01), Isoyama et al.
patent: 5503930 (1996-04-01), Maruyama et al.
patent: 5506077 (1996-04-01), Koksbang
patent: 5518842 (1996-05-01), Fey et al.
patent: 5591543 (1997-01-01), Peled et al.
patent: 5595842 (1997-01-01), Nakane et al.
patent: 5605773 (1997-02-01), Ellgen
patent: 5609975 (1997-03-01), Hasegawa et al.
patent: 5620812 (1997-04-01), Tahara et al.
patent: 5626635 (1997-05-01), Yamaura et al.
patent: 5631105 (1997-05-01), Hasegawa et al.
pat

Affiliated with

Also associated with

Rating

Doped lithium manganese oxide compounds and methods of... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Doped lithium manganese oxide compounds and methods of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Doped lithium manganese oxide compounds and methods of... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2844438