Electrolysis: processes – compositions used therein – and methods – Electrolytic coating – Forming multiple superposed electrolytic coatings
Reexamination Certificate
1999-10-19
2001-07-17
Bell, Bruce F. (Department: 1741)
Electrolysis: processes, compositions used therein, and methods
Electrolytic coating
Forming multiple superposed electrolytic coatings
C205S175000, C205S322000, C205S332000
Reexamination Certificate
active
06261434
ABSTRACT:
FIELD OF THE INVENTION
The invention is directed to the anodization of porous valve-metal anode bodies used for the fabrication of electrolytic capacitors and, in particular, to a differential anodization of porous capacitor anode bodies which produces an anodic oxide film which is thicker on the outer surfaces and thinner within the bulk of the anode bodies.
BACKGROUND OF THE INVENTION
It has been known for many years that porous valve-metal capacitors employing the valve metal as one capacitor plate, the anodic oxide as the dielectric, and a solid-state electrolyte, such as manganese dioxide, as the second capacitor plate (typified by so-called “solid” tantalum capacitors) give more reliable service with respect to device short-circuit prevention when the field through the anodic oxide is relatively low, i.e. when the voltage applied to the device in service is significantly lower than that used to produce the anodic oxide dielectric film. As a consequence of this fact, manufacturers employ anodizing voltages that are 2 to 5 (or more) times as high as the service-rated voltage of the devices.
It has also been known for many years that the presence of a thicker anodic oxide film on the external surfaces of valve-metal anode bodies offers a good deal of protection from short-circuiting of the devices when the anodic oxide film thickness on the internal surfaces of the anode bodies is minimized for the purposes of minimizing the use of expensive anode materials, such as tantalum, or for maximizing the device capacitance for a given anode size. There are at least 3 contributing factors which combine to make thickness of the external oxide of greater importance with respect to device reliability than the interior oxide thickness:
1) The radius of curvature of the corners and edges of the anodes raises the electric field in these areas, making them more prone to short-circuit failure.
2) The voltage drop across the “solid” electrolyte (e.g. manganese oxide) is lowest on the outer surface of the anodes, making somewhat higher currents available to oxide flaws on the external anode surfaces.
3) The external anode surfaces, particularly corners and edges, of powder-metallurgy porous valve-metal anode bodies become damaged during bulk handling in the manufacturing process. Anodes abrade against each other, as well as against feeder bowl and vibratory track surfaces, etc. The abrasion encountered during bulk handling has been demonstrated to cause the passive oxide film (formed upon contact with the atmosphere after the sintering operation) to become imbedded in the external anode surfaces. This abrasively-imbedded passive film gives rise to flaws in the anodic dielectric film on abraded areas of the anode (described in U.S. Pat. No. 5,716,511). Although oxide “blisters” become readily apparent at anodizing voltages above about 100 volts, the incipient flaws are present at all film thicknesses and give rise to disproportionately high leakage currents with increasing field.
Several techniques for producing a thicker anodic oxide film on the external surfaces of anodized porous anode bodies are described in the patent literature.
U.S. Pat. No. 3,415,722 (Scheller, et al.) describes the method of anodizing porous capacitor bodies to form a uniform dielectric film throughout said anode bodies, impregnating the anode bodies with a solid, non-conducting material (wax, stearin, anthracene, etc.) removing the insulating solid from the external anode surfaces and anodizing at a voltage higher than the initial voltage of the external surfaces to form an oxide film on the external surfaces which is thicker than the internal anodic oxide. The insulating solid is then removed from the bodies of the anodes prior to processing into finished capacitors.
A somewhat similar process is described in U.S. Pat. No. 5,643,432 (Qiu). This patent describes the production of a thicker external oxide via the impregnation of an anodized porous body electrode with an electrolyte-insoluble, insulating liquid (benzene, xylene, etc.), evaporation of the insulating liquid from the external surfaces of the anode body, and formation of a relatively thick anodic oxide layer on the external surfaces of the anode bodies at a voltage higher than the initial anodizing voltage. The remainder of the solvent is evaporated prior to processing the anodes into finished capacitors.
A differential anodizing process (i.e., an anodizing process for porous valve-metal capacitor bodies producing a uniform internal anodic oxide thickness with a significantly thicker oxide on the external anode surface) is described in U.S. Pat. No. 4,131,520 (Bernard, et al.). This patent describes the production of a thicker external anodic oxide film on anodized porous anode bodies via the use of electrolytes consisting of aqueous solutions of the salts of weak acids (e.g. borax 0.01%-4.0% or ammonium pentaborate/boric acid). The flow of electric current gives rise to a partitioning of the electrolyte into an anion-rich portion inside the anodes and a cation-rich portion external to the anode bodies. The anion-rich electrolyte inside the anode bodies tends to undergo re-association to form the weak acid, giving a relatively high electrolyte resistivity inside the anodes and an associated much higher rate of anodic oxide formation on the external anode surfaces. Again, a higher anodizing voltage is used to produce the external anodic oxide film.
U.S. Pat. No. 4,131,520 also relates an additional method of achieving differential anodizing; the anodized porous valve metal anodes are dipped into a solvent which does not readily transport the anions of weak acid salts into the bodies of the porous anodes and the solvent-dipped anodes are then anodized at a voltage higher than the initial anodizing voltage to produce the thicker external anodic oxide.
More recently, another differential anodizing method is described in U.S. Pat. No. 5,837,121 (Kinard et at.), in which the non-thickness-limited anodizing capability of solutions of dibasic potassium phosphate in glycerine containing less than 0.1% water and operated above about 150° C. is employed to produce a relatively thick layer of anodic oxide on the external surfaces of anodes while producing relatively little oxide growth on the internal surfaces of the anode bodies (The non-thickness-limited anodizing process is also described in detail in the paper entitled: “The Non-Thickness-Limited Growth of Anodic Oxide Films on Valve Metals”, by Brian Melody, Tony Kinard, and Philip Lessner, which was published in
Electrochemical and Solid State Letters
, Vol. 1, No. 3, pages 126-129 , 1998).
All of the above methods of differential anodizing (i.e., anodizing which produces a thicker anodic oxide film on the external surfaces than on the internal surfaces of porous, value-metal anode bodies) have serious drawbacks in commercial capacitor production. The method described in U.S. Pat. No. 3,415,722 produces anodized anodes containing a waxy substance which is difficult to remove completely and which may interfere with the solid electrolyte impregnation process if incompletely removed.
The process described in U.S. Pat. No. 5,643,432 gives rise to the leaching of water insoluble liquid organic materials from the anodes during the second anodizing step. This gives rise to uncertain shielding of the internal portions of the anodes so-treated from the second anodization step electrolyte, resulting in unpredictable capacitance loss and electrolyte contamination.
The first process described in U.S. Pat. No. 4,131,520, that of employing an aqueous solution of the salt of a weak acid, is very sensitive to the presence of contamination; specifically, any phosphate, etc., remaining within the anode bodies from the initial anodizing step tends to defeat the differential nature of the anodizing process, resulting in the production of additional oxide film growth on the internal surfaces of the anode bodies with the loss of device capacitance. The second process described in U.S. Pat. No. 4,131,520, that of dipping the anodes
Kinard John Tony
Lessner Philip Michael
Melody Brian John
Banner & Witcoff , Ltd.
Bell Bruce F.
Kemet Electronics Corporation
Leader William T.
LandOfFree
Differential anodization process for electrolytic capacitor... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Differential anodization process for electrolytic capacitor..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Differential anodization process for electrolytic capacitor... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2558504