Compositions – Vaporization – or expansion – refrigeration or heat or energy... – With lubricants – or warning – stabilizing or anti-corrosion...
Reexamination Certificate
2001-09-20
2004-11-30
Le, Hoa Van (Department: 1752)
Compositions
Vaporization, or expansion, refrigeration or heat or energy...
With lubricants, or warning, stabilizing or anti-corrosion...
C252S071000, C266S171000, C266S233000, C423S116000, C423S472000, C429S103000, C204S196070, C204S199000
Reexamination Certificate
active
06824702
ABSTRACT:
The invention relates to an apparatus and a process for the preparation of salt melts and mixtures thereof by means of a tubular reactor and a continuous stirred reactor, in which the starting materials are melted and brought to reaction, and the reaction products are subsequently passed through columns for purification.
Melts of salts, such as, for example, NaAlCl
4
, have various areas of application. Salt melts can be employed as storage medium in heat stores, as heat-transfer agents, for example in heating baths, for blanketing and purifying molten metals, for electrocoating of high-melting materials or as melt electrolyte in primary batteries, as described in CB 2,046,506. A further possible application of these salts is in rechargeable sodium batteries. The salts are employed in batteries which have operating temperatures of between 130° C. and 200° C. (K. M. Abraham, D. M. Pasquarielio, J. Electrochem. Soc., Vol. 137, 1189-1190 (1990)).
DE 3419279 describes an electrochemical cell in which the cathode matrix is impregnated with a sodium/aluminium halide salt melt electrolyte.
A relatively new area of application is the “ZEBRA battery”. This high-temperature cell consists of an electrode of liquid sodium, a beta-aluminium electrolyte and an electrode of transition-metal chloride in an NaAlCl
4
melt (B. Cleaver, V. S. Sharivker, J. Electrochem. Soc., Vol. 142, 3409-3413 (1995)).
DE 3718920 describes the preparation of salt melts by adding a pure metal and an alkali metal halide to the melt. The reaction cell is operated above the melting point of the salt melt. In the working example, the alkali metal halide is NaCl, the molten alkali metal Is sodium, and the separator is beta-aluminium oxide. Owing to the use of pure sodium, special safety precautions, such as working under a protective-gas atmosphere, must be taken. The reactions must take place in separate cells, since poisoning of the separator by the by-product AlHal
3
formed must be prevented.
All the processes disclosed hitherto for the preparation of salt melts operate batchwise. A batch procedure has some severe disadvantages compared with a continuous preparation process. During a batch change, the apparatus must be opened. The product can then be contaminated by the oxygen from the ambient air, water and dust. The batch change results in down times of the plant and thus in a reduced space-time yield. An effective discontinuous process requires large apparatuses. The start-up process requires correspondingly more energy and time. It is been found that, in particular during start-up of the plants, impurities can be introduced into the process. FR 2168912 describes a complex purification process for alkali metal halogen aluminates. The 2-step purification process consists of oxygen treatment for degrading the organic impurities and aluminium treatment for precipitating iron and heavy metals. The aluminium treatment must be carried out under a nitrogen or argon atmosphere.
For the preparation of the alkali metal halogen aluminates, the reaction of corresponding aluminium halides and alkali metal halides in a sealed tube is described (Friedman, Taube, J. Am. Chem. Soc., 72, 2236-2243 (1950)). In this process, an increase in pressure to 6-7 atmospheres is observed, which results in problems (FR 2168912). The apparatuses must be fitted with the appropriate safety precautions.
For continuous processing of the salts, basically tubular reactors and continuous stirred reactors are suitable.
Tubular reactors are ideal reactors for the continuous processing of liquid media. The residence-time distribution here is very narrow, which means that all particles have approximately the same residence time, and a very narrow quality distribution is thus produced. A high surface area/volume ratio and turbulent flow mean that a tubular reactor is highly suitable for heat transfer. For use for a solid, however, the prerequisite of flowability is lacking. In addition, heat transfer for melting a salt mixture is very poor owing to the poor thermal conduction of the granular starting materials, which results in very long residence times.
Another possibility for carrying out reactions continuously is the continuous stirred reactor. Here, the granulated starting materials can be metered into the stirred melt. This facilitates convective heat transfer, which considerably accelerates heating of the starting materials. In particular if subliming salts are to be used as starting materials, a temperature below the sublimation temperature is necessary in order to avoid an excess pressure in the system. A severe disadvantage of the continuous stirred reactor is the residence-time distribution. This results in a significant proportion of unreacted starting materials always being present in the product discharge stream.
The object of the invention is to provide a continuous process for the preparation of pure salt melts which excludes the disadvantageous effects of the environment, minimizes the energy requirement and facilitates an optimum space-time yield. A further object is to make large amounts of salt melts available in the shortest possible time.
The object according to the invention is achieved by an apparatus for the preparation of salt melts, and mixtures thereof, of the general formula
MDX
4
(I)
in which
M is Li, Na, K, Rb or Cs,
D is Al, Ga, in or Tl, and
X is F, Cl, Br or I,
essentially consisting of a heatable stirred reactor (
1
) and a downstream tubular reactor (
4
), where the stirred reactor (
1
) contains a zone which, owing to the tank geometry, cannot contain solids, and the tubular reactor (
4
) or its feed line extends into this solid-free zone.
The invention furthermore relates to a process for the preparation of salt melts, and mixtures thereof, of the general formula (I) by reacting a metal halide of the formula DX
3
(II) with an alkali metal salt of the formula MX (III) in the abovementioned apparatus.
The process products are suitable for use as melt electrolyte in electrochemical cells, as storage medium in heat stores, as heat-transfer agent, for example in heating baths, for blanketing and purifying molten metals, for electrocoating of high-melting materials or as melt electrolyte in rechargeable sodium batteries and primary batteries.
Surprisingly, it has been found that a suitable combination of a continuous stirred reactor and a plurality of tubular reactors allows a salt melt of the desired quality to be produced continuously.
The process can be carried out using all continuous and heatable stirred reactors which appear suitable to the person skilled in the art. For the task of stirring, use can be made of all suitable stirrers, such as propeller, inclined blade, disc, impeller, cross-blade, gate or blade stirrers. The stirrer should facilitate good heat transfer between the reactor wall and the salt or melt.
Stirred reactors are usually made of steel. The aggressive salt melts can attack this material in a corrosive manner.
It has been found that stirred reactors whose main components are made of nickel alloys are particularly suitable for the processing of salts and salt melts. The relatively low mechanical stress on the reactor shell means that nickel can also be used as the tank material. It is also possible to employ reactors made of class. It has furthermore been found that the metal parts of the stirred reactor which come into contact with the salts or salt melts can be protected against corrosive and abrasive damage by surface coatings with materials known to the person skilled in the art, such as PTFE/PFA, enamel or ceramic materials.
In order to improve the efficiency of the stirred reactor, it is necessary that no solid enters the reactor overflow. Surprisingly, it has been found that this object can be achieved by means of a settling zone in the reactor. This settling zone is designed in such a way that it has a feed line for the mixture from below and is sufficiently large What the solid in the inflowing mixture can settle out.
Similar demands are made of the material of the downstre
Brzezinski Susanne
Ohrem Hans Leonhard
BASF - Aktiengesellschaft
Le Hoa Van
Millen White Zelano & Branigan P.C.
LandOfFree
Device and method for producing molten salts and use thereof does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Device and method for producing molten salts and use thereof, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Device and method for producing molten salts and use thereof will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3314014