Stock material or miscellaneous articles – All metal or with adjacent metals – Surface feature
Reexamination Certificate
1999-03-24
2001-02-13
Jones, Deborah (Department: 1775)
Stock material or miscellaneous articles
All metal or with adjacent metals
Surface feature
C052S660000, C072S199000, C072S252500, C072S366200, C072S379600, C072S700000, C160S113000, C160S166100, C160S236000, C428S156000, C428S161000, C428S162000, C428S174000, C428S179000, C428S187000, C428S216000, C428S220000, C428S335000, C428S339000, C428S542600, C428S542800, C428S577000, C428S587000, C428S923000
Reexamination Certificate
active
06187455
ABSTRACT:
BACKGROUND OF THE INVENTION
a. Field of the Invention
This invention relates to a process of roll-patterning and then painting a surface of a metal strip or sheet, particularly an aluminium strip or sheet used to form vanes or head or bottom rails for window covering assemblies, such as venetian blinds, or to form architectural panels for ceilings or wall coverings. This invention particularly relates to a painted metal strip or sheet with a decorative pattern on at least one surface, made by the process, and to a window covering assemblies and architectural panels made from the strip or sheet.
b. Background Art
Elongated vanes or slats of the type used in horizontal and vertical blinds are well known and commercially available. Such slats are formed, for example, by continuous casting of aluminium strips or sheets, subsequent milling and, if necessary, cutting to width to provide coils of aluminium strips having the desired thickness and width. Subsequently, the strips or sheets are painted (optional), then roll-formed and cut into slats of the desired length. Likewise, it is well known to roll-form and cut such strips or sheets into head and bottom rails and architectural panels.
Since window coverings and architectural products are frequently decorative, different colours and laminated or painted patterns are often provided on their exterior surfaces, particularly on the visible surfaces of slats and head and bottom rails of window coverings. In this regard, coiled strip, used to make blind slats, is normally covered with paint or lacquer in a coil-coating process in order to give it a decorative pattern before it is roll-formed into slats.
A pattern can then be rolled into the painted strip surface, so that the resulting indentations in the strip surface give it a fabric-like appearance. An example of a process and apparatus for providing such a pattern in a painted strip surface for foldable metal drape panels for vertical blinds is described in U.S. Pat. No. 4,362,039 (Toti). In the process of his patent, a rotary die is used to produce continuous patterns of scribe lines in painted surfaces of strips. The scribe lines assist in subsequently forming a preselected cross-sectional profile of the metal drape panels. Another rotary die is used for subsequently forming patterns of embossments in the strips between the scribe lines, in order to begin to stretch and work the metal between the scribe lines, so as to make it easier thereafter to form a weave pattern. Two additional rotary cutting die stations then cut the male and female hinges of the drape panel, and then, a rotary weave die station produces weave patterns between the scribe lines. The weave patterns comprise relatively deep cuts which slice through the metal at the edges of the pattern and provide a raised area which imitates the ins and outs of woven threads of cloth. Unfortunately, these cuts tend to damage the paint on the strip surface and can result in premature corrosion of the metal.
U.S. Pat. No. 4,499,938 (Toti) also describes a process and apparatus for making a metal blind slat by providing a relatively deeply embossed rib pattern in a painted strip material. The depth of the pattern is described as 0.015 inch (0.381 mm) in a strip of 0.008-0.010 inch (0.20-0.254 mm) thickness. This means that the depth of the pattern is more than the thickness of the strip, and so, the strip has been corrugated. Unfortunately, such an embossed pattern also inevitably tends to damage the paint on the strip and produce premature corrosion of the metal.
BRIEF SUMMARY OF THE INVENTION
In accordance with this invention, a decorative roll-patterned metal strip or sheet, preferably an aluminium strip or sheet, is provided that has a thickness of about 0.05-1.0 mm, preferably about 0.1-0.8 mm, with a surface having a plurality of indentations of a depth of about 0.001-0.05 mm, preferably about 0.02-0.035 mm, and optionally having a layer of a paint of a thickness of about 3-30 microns, preferably about 10-15 microns, on the surface and within its indentations; the ratio of the depth of the indentations to the thickness of the strip or sheet being in the range of about 1:5 to about 1:100. Preferably, the indentations form a pattern which covers substantially the entire surface of the strip or sheet and which is visible to the naked eye, even though the paint is within and atop the indentations.
Also in accordance with this invention, a process is provided for making the decorative roll-patterned metal strip, comprising the steps of:
cold-rolling a metal strip or sheet, preferably an aluminum strip or sheet, at a temperature of about 40-175 C to reduce the thickness of the strip or sheet by about 15-40%, preferably about 20-30%, to about 0.05-1.0 mm, preferably about 0.1-0.8 mm, using a milling roll with a surface pattern thereon, to form a roll-patterned strip or sheet having, in a surface, a plurality of indentations corresponding to the surface pattern of the milling roll and with a depth of about 0.001-0.05 mm, preferably 0.02-0.035 mm; the ratio of the depth of the indentations to the thickness of the strip or sheet being in the range of about 1:5 to about 1:100; and then optionally
painting the surface of the roll-patterned strip or sheet with a thickness of about 3-30 microns, preferably about 10-15 microns, of paint on the surface and within its indentations.
Preferably, the cold-rolling step using the milling roll with the surface pattern is carried out in a last stand of a multi-stand cold-roll mill, and only the last stand has at least one of its milling rolls with the surface pattern. Subsequent painting of the strip or sheet is preferably carried out in a separate machine for coil-coating.
Further in accordance with this invention are provided vanes and head and bottom rails for window covering assemblies, such as venetian blinds, and architectural panels for ceilings or wall coverings made from the decorative roll-patterned strip or sheet of the invention.
Further aspects of the invention will be apparent from the detailed description below of particular embodiments and the drawings thereof.
REFERENCES:
patent: 3956915 (1976-05-01), Saunders et al.
patent: 4362039 (1982-12-01), Toti
patent: 4499938 (1985-02-01), Toti
patent: 5215245 (1993-06-01), Moyer
patent: 5311814 (1994-05-01), Kierson
patent: 5552235 (1996-09-01), Bastawros et al.
patent: 1944295 (1971-04-01), None
patent: 3117936 (1982-11-01), None
patent: 676251 (1995-10-01), None
patent: 2075428 (1981-11-01), None
patent: WO 95/07775 (1995-03-01), None
Dorsey & Whitney LLP
Hunter Douglas International N.V.
Jones Deborah
Koehler Robert R.
LandOfFree
Decorative roll-patterned strip and process of making same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Decorative roll-patterned strip and process of making same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Decorative roll-patterned strip and process of making same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2588358