DESCRIPTION:
BRIEF SUMMARY
BACKGROUND
1. Field of the Invention
The present invention relates to a method of forming a semiconductor film such as a silicon film used in a thin-film semiconductor device, integrated circuit, solar cell, charge-coupled device, or other device. The invention also relates to a low-pressure chemical vapor deposition apparatus used to form a semiconductor film and also to a thin-film semiconductor device which employs a semiconductor film and can be applied to an active-matrix liquid crystal display.
2. Description of Related Art
In recent years, liquid-crystal displays having larger viewing screens and higher resolution have been manufactured. With this trend the driving method has shifted from the simple matrix method to the active-matrix method to provide a display having a larger amount of information. The active-matrix method permits the fabrication of a liquid-crystal display having hundreds of thousands of pixels. In this liquid-crystal display, a switching transistor is provided for each pixel. Molten quartz plates and transparent insulating plates made of glass or other material are used as the front and back plates of various liquid-crystal displays. The transparent insulating plates enable the fabrication of transmission-type display devices.
However, in order to increase the area of the viewing screen or to reduce the cost, it is essential to use cheap, normal glass as insulating plates or substrates. Therefore, there is a demand for a technique capable of forming thin-film transistors operating stably on inexpensive glass plates which activate an active-matrix liquid-crystal display while maintaining economical merit.
Usually, semiconductor films such as amorphous silicon films or polycrystalline silicon films are used as the active layers of thin-film transistors. When driver circuits are integrated with thin-film transistors, the use of polysilicon is advantageous, because it offers a high operating speed.
In order to make such devices, a technique is required for fabricating a thin-film semiconductor device having a normal glass plate on which an active layer consisting of a semiconductor film such as a polysilicon film is formed. Where normal glass plates are used, a great restriction is imposed on the process. In particular, the maximum temperature must be below about 600.degree. C., i.e., below the strain point of the glass. Therefore, there is a demand for a low-temperature processing technique for fabricating thin-film transistors capable of operating a liquid-crystal display and the active layer of thin-film transistors capable of operating driver circuits at a high speed.
One conventional LPCVD (low-pressure chemical vapor deposition) method of depositing such a semiconductor film uses an LPCVD system in which the lowest attainable base pressure is 10.sup.-3 to 10.sup.-4 torr. The deposition pressure is set above approximately 40 mtorr by the system. A semiconductor film such as a silicon film is deposited by elevating temperature to 610.degree.-640.degree. C. which is equal to or slightly higher than the strain point of the glass. Another LPCVD method makes use of an LPCVD system having a reaction chamber which is evacuated at an effective pumping speed of about 1 to 3 SCCM/mtorr or less. The deposition temperature is elevated to the maximum permissible temperature of approximately 600.degree. to 620.degree. C. at which the glass plates or substrates can be used. Monosilane (SiH.sub.4) is supplied as a raw material gas at a flow rate of about 10 SCCM (Standard Cubic Centimeters per Minute). The partial pressure of the monosilane is set to about several millitort. Under this condition, a semiconductor film such as a silicon film is deposited (see Solid State Devices and Materials, 1991, Extended Abstracts, p. 614).
A further method of forming a semiconductor layer acting as an active layer is described in Japanese Patent Laid-Open No. 307776/1988. In particular, a semiconductor film such as a silicon film which will become the active layer is deposited on an insulating substrate at
REFERENCES:
patent: 3670172 (1972-06-01), Golden
patent: 3924137 (1975-12-01), Alger
patent: 3924967 (1975-12-01), Harra
patent: 4475045 (1984-10-01), Holden et al.
patent: 4636401 (1987-01-01), Yamazaki et al.
patent: 4640844 (1987-02-01), Neppl et al.
patent: 4758529 (1988-07-01), Ipri
patent: 4842897 (1989-06-01), Takeuchi et al.
patent: 4868014 (1989-09-01), Kanai et al.
patent: 4900694 (1990-02-01), Nakagawa
patent: 4956204 (1990-09-01), Amazawa et al.
patent: 5026574 (1991-06-01), Economu et al.
patent: 5064779 (1991-11-01), Hasegawa
patent: 5091219 (1992-02-01), Monkowski et al.
patent: 5143018 (1992-09-01), Meakin
patent: 5234724 (1993-08-01), Schmidt
patent: 5298452 (1994-03-01), Meyerson
Leybold, Product & Vacuum Technology Reference book, 1991, p. 5.
Hatsumei Kyokai Open Technical Report No. 90-10440; Journal Of Technical Disclosure; vol. 15-34.
Donahue Et Al.; Nikkei Microdevices; Oct. 1985, pp. 79-87.
Preliminary Manuscripts For The 26th Applied Physics Relates Combination Lecture, (1979, Mar. 27).
Iscoff; Nikkei Microdevices; Apr. 1986, pp. 131-143.
Aoyama Et Al; "Crystallization Of LPCVD Silicon Films By Low Temperature Annealing": J. Electrochem. Soc., vol. 136, No. 4, Apr. 1989, pp. 1169-1173.
Serikawa et al.; "Electrical Characteristics Of High-Mobility Fine-Grain Poly-SI TFTS From Laser Irradiated Sputter-Depsoited SI Film": Japanese Journal Of Applied Physics, vol. 28, No. 11, Nov. 1989, pp. L1871-L1873.
Migliorato Et Al.; "Material Properties And Characteristics Of Polysilicon Transistors For Large Area Electronics"; Applied Surface Sciences 30 (1987); pp. 353-371.
Meakin Et Al; "Low Defect-Density Polycrystalline Silicon For High Performance Thin Film Transistors": Applied Surface Science 30 (1987) pp. 372-382.
Miyasaka Et Al.: "TFT and Physical Properties Of Poly-Crystalline Silicon Prepared By Very Low Pressure Chemical Vapor Deposition (VLPCVD)"; Extended Abstracts Of The 1991 International Conference On Solid State Devices And Materials, Yokohama, 1991, pp. 614-616.
Mitsutoshi Miyasaka et al., "TFT and Physical Properties of Poly-Crystalline Silicon Prepared by Very Low Pressure Chemical Vapour Deposition (VLPCVD)"; Japanese Journal of Applied Physics, vol. 30, No. 12B, Dec. 1991, pp. 3733-3740.
Mitsutoshi Miyasaka et al., "Transistor and physical properties of polycrystalline silicon films prepared by infralow-pressure chemical vapor deposition", J. Appl. Phys 74 (4), 15 Aug. 1993; pp. 2870-2885.
Meakin, D. et al, "The Growth of Polycrystalline Silicon Films By Low Pressure Chemical Vapour Deposition at Relatively Low Temperatures", Thin Solid Films, 163 (1988) 249-254.
Loisel, B. et al, "LPCVD Silicon For Active Devices", Journal De Physique,Colloque C5, supplement au n.degree.5, vol. 50, May 1989, C5-467-C5-477.
Ahmed, et al, "The Growth of Polycrystalline Silicon By Ultra Low Pressure Chemical Vapour Deposition", 445-456.
Beck Shrive
Seiko Epson Corporation
Tallot Brian K.
LandOfFree
CVD apparatus, method of forming semiconductor film, and method does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with CVD apparatus, method of forming semiconductor film, and method , we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and CVD apparatus, method of forming semiconductor film, and method will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2306788