Cut and puncture resistant laminated fabric

Adhesive bonding and miscellaneous chemical manufacture – Methods – Surface bonding and/or assembly therefor

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C156S192000

Reexamination Certificate

active

06818091

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to laminated materials and the process for their production. The laminates have a layer of polyethylene bonded to a layer of an ultra-high molecular weight polyethylene high performance fiber. More particularly, the present invention relates to a method of producing a laminate by bonding a layer of a thermoplastic film such as polyethylene or ethylene vinyl acetate (EVA) to a layer of a strong, lightweight fabric constructed of a high performance fiber such as long chain expanded polyethylene fibers.
BACKGROUND OF THE INVENTION
High performance fabrics have been used for a number of applications where tear-resistance, abrasion-resistance, cut- and stab-resistance, and chemical- and cold-resistance are important. As used herein, the term “high performance” refers to fabrics constructed from a group of fibers used to make cut-resistant, and abrasion resistant articles such as gloves and aprons. The high strength-to-weight ratios of these fabrics can provide properties having significant improvements in the performance characteristics stated above at a fraction of the weight of other alternatives. It would be desirable to combine the advantages of high performance fabrics with film-laminated fabrics currently used for applications such as cargo container covers and side curtains for side-access trucks. These items typically are constructed from vinyl-coated nylon or similar materials which do not exhibit these high performance characteristics. The vinyl coating is provided for the purpose of creating an impervious barrier to air and fluid penetration. The disadvantages of currently available vinyl-coated nylon or polyester fabric materials is their relative lack of durability and relatively higher weight per unit area. Thus, it would be desirable to take advantage of the high strength and low weight characteristics of high performance fabrics for these applications. An successful lamination process for these fabrics would enhance their abrasion resistance. It is believed that no successful process has been developed for the economical lamination of high performance fabrics with a thermoplastic film such as polyethylene or EVA to create a more durable, waterproof, cut and wear resistant laminate.
SUMMARY OF THE INVENTION
The present invention relates to the heat lamination of a thermoplastic films to fabrics constructed of arrangements of fabrics constructed of high performance fibers such as high tenacity, high modulus, ultrahigh molecular weight polyethylene fibers. Various applications and potential applications of fabrics constructed of high strength polyethylene fibers require a flexible, light weight coating to prevent the penetration of the fabric by fluids, chemicals and particles. These applications require the high strength-to-weight of the high performance, polyethylene fiber fabrics and consequently require a coating that is equally lightweight. In addition the coating must stretch with the fabric and is required to be tough, abrasion resistant chemically resistant, well adhered and durable. Previously, high strength polyethylene fibers have not been coated or laminated with conventional coatings or films due to their extremely low functionality and highly crystalline structure. There are no bonding sites to chemically bond adhesives or coatings.
The method of the present invention includes making a cut and puncture resistant laminated fabric comprising laminating a layer of thermoplastic film to a layer of fabric comprised of a high performance yarn. The laminating step is conducted at a temperature between about 230° F. and about 290° F. with a contact time of between about 5 minutes and about 4 to 8 hours with the application of a laminating pressure of between about 50 psi and about 500 psi. The thermoplastic film may be comprised of a material selected from the group consisting of high density polyethylene, low density polyethylene and ethylene vinyl acetate. The high performance fiber is comprised of a material selected from the group consisting of extended chain polyethylene, ultra high molecular weight polyethylene, and aramid.
Thus one aspect of the present invention is to provide an economical method for lamninating a high performance fabric.
Another aspect of the present invention is to provide a method for making a lightweight sheet material having superior wear characteristics.
These and other aspects of the present invention will become apparent to those skilled in the art after a reading of the following description of the preferred embodiments when considered in conjunction with the drawings.


REFERENCES:
patent: 3558423 (1971-01-01), Rossetti
patent: 3657042 (1972-04-01), Rerolle et al.
patent: 4424253 (1984-01-01), Anderson
patent: 4597818 (1986-07-01), Aoyama et al.
patent: 4894281 (1990-01-01), Yagi et al.
patent: 4957804 (1990-09-01), Hendrix et al.
patent: 4983433 (1991-01-01), Shirasaki
patent: 5160472 (1992-11-01), Zachariades
patent: 5160767 (1992-11-01), Genske et al.
patent: 5169697 (1992-12-01), Langley et al.
patent: 5248364 (1993-09-01), Liu et al.
patent: 5266390 (1993-11-01), Garland
patent: 5284540 (1994-02-01), Roth et al.
patent: 5286576 (1994-02-01), Srail et al.
patent: 5389448 (1995-02-01), Schirmer et al.
patent: 5443874 (1995-08-01), Tachi et al.
patent: 5445883 (1995-08-01), Kobayashi et al.
patent: 5460884 (1995-10-01), Kobylivker et al.
patent: 5547536 (1996-08-01), Park
patent: 5567498 (1996-10-01), McCarter et al.
patent: 5789327 (1998-08-01), Rousseau
patent: 4441842 (1995-06-01), None

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Cut and puncture resistant laminated fabric does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Cut and puncture resistant laminated fabric, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Cut and puncture resistant laminated fabric will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3350097

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.