Corrosion resistant alloy

Specialized metallurgical processes – compositions for use therei – Processes – Free metal or alloy reductant contains magnesium

Patent

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

75126K, 75128P, C22C 3806

Patent

active

045810664

DESCRIPTION:

BRIEF SUMMARY
TECHNICAL FIELD OF THE INVENTION

The present invention relates to a corrosion resistant alloy.


BACKGROUND OF THE INVENTION

As general corrosion resistant materials there are stainless steels containing at least 11.00% of Cr, and in JIS G 4304 they are classified, depending upon their metallic structures, into five varieties, that is, austenitic, austeniteferritic, ferritic, martensitic and precipitation hardenable stainless steels. Among them ferritic stainless steels are relatively inexpensive and have enhanced workability and elongation, and therefore relatively large quantites of such steels are commercially used. Of the ferritic stainless steels, nine species of hot rolled sheets and ten species of hot rolled strips are standardized. Ten species of cold rolled sheets and strips are also standardized. Regarding the content of P of these standardized ferritic stainless steel sheets and strips, the standard prescribes 0.030% or less of P for two species of SUS 447 J1 and SUS XM 27 and 0.040% or less of P for other species.
A ferritic stainless steel has a crystalline structure of a body-centered cubic lattice which inherently leads to a reduced toughness and workability of the material. In addition, Cr contained in the material in an amount as high as at least 11.00% to provide the corrosion resistance also inherently acts to further reduce the toughness and workability of the material. Accordingly, regarding impurities which adversely affect the toughness and workability of the material, in particular P, the standard prescribes the strict provision of 0.040% or less of P.
In the production of thin products having a thickness of 4.0 mm or below, it has now been found according to the inventors' research that an adverse effect of P in excess of 0.040% upon the toughness of the products may be obviated by controlling amounts of Cr, C and sol. Al within appropriate ranges, respectively, and thus, it is possible to inexpensively supply corrosion resistant materials without sacrificing the corrosion resistance and mechanical properties of the products.
In producing stainless steels individual companies utilize their respective processes which basically involve melting of iron scraps, iron alloys and other materials in a electric furnace, refinining and adjustment of components in VOD, converter-VOD or AOD and casting of slubs and ingots. On the other hand, from a view point of productivity and saving energy, is also considered a process for producing stainless steels using an installation for the manufacture of ordinary steels wherein pig iron from a blast furnace is fed to a converter together with various subsidiary materials such as Fe-Cr alloys, in which converter refining and component adjustment are carried out. The pig iron normally contains substantial amounts of impurities such as P and S, and in particular 0.08 to 0.15% of P. In order that the product should contain a reduced level of P as low as 0.040% or below as in the standardized stainless steels, it is necessary to carry out a preliminary removal of P before the pig iron is fed to the converter or to carry out a special treatment for the removal of P in operating the converter, leading to a reduction of the productivity. If such treatments for removing P may be obviated, the productivity will be enhanced and the manufacturing costs will be reduced, rendering the process inexpensive. Accordingly, it can be understood that if the burden of controlling P prescribed in the standard of stainless steels may be lightened, it is possible to produce corrosion resistant alloys reduced in cost.


DESCRIPTION OF THE INVENTION

As a result of extensive research and consideration, the inventors have found that if Cr and C are restricted to from 10.00 to 18.00% and up to 0.05%, and if 0.005 to 0.50% of sol. Al is added, the presence of P in excess of the level required in the standardized ferritic stainless steels does not adversely affect the toughness of the materials. It has also been found that the enrichment of P proposed herein does not adversely af

REFERENCES:
patent: 2897078 (1959-07-01), Nishikiori

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Corrosion resistant alloy does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Corrosion resistant alloy, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Corrosion resistant alloy will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2064062

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.