Corrosion and grain growth resistant aluminum alloy

Details Corrosion and grain growth resistant aluminum alloy Corrosion and grain growth resistant aluminum alloy

2000-07-13

2003-01-07

Wyszomierski, George (Department: 1742)

Alloys or metallic compositions

Aluminum base

Zinc containing

C420S551000, C420S553000

Reexamination Certificate

active

06503446

ABSTRACT:

FIELD OF THE INVENTION
The present invention is directed to a corrosion and grain growth resistant aluminum alloy, and particularly to an alloy composition and article having controlled levels of iron, manganese, zinc, zirconium, vanadium, titanium and other elements that is particularly adapted for use in heat exchanger applications.
BACKGROUND ART
In the prior art, aluminum alloys are the alloys of choice for heat exchanger applications. These alloys are selected for their desirable combination of strength, low weight, and good thermal and electrical conductivities. Some aluminum alloys may also exhibit another characteristic such as improved brazeability. Other alloys may have better formability, while others yet may exhibit good extrudability or have desirable corrosion resistance.
When an aluminum alloy component is in a corrosive environment, a common practice is to coat the aluminum alloy component with zinc for corrosion protection. This zinc is applied using a plasma spraying technique. When the alloy is in the form of a flat tube as shown in
FIG. 1
, it is preferred to employ the plasma spraying technique; round tubing does not lend itself to good zinc coverage when sprayed due to its curved surface.
No matter how the zinc is applied, zinc in the workplace presents a number of environmental and safety problems. When applying zinc using plasma techniques, the guns employed for such purposes are extremely loud and cause considerable noise pollution. Further, since cooling is a part of the zinc coating process, contamination of the cooling water with zinc is inevitable, and a considerable water pollution problem then exists. Zinc is also a health hazard, and OSHA has strict regulations concerning the handling of zinc and levels of zinc dust/fumes present in the workplace.
Besides the problems of zinc itself, zinc-coated aluminum products can also be problematic if the zinc coating is not uniform or is compromised. For example, a non-uniform coating or surface scratches creates local sites where the aluminum metal is exposed. These exposed local sites or cells may then corrode in a more accelerated manner than if the aluminum was not coated at all, and premature failure may occur during service.
The zinc coating processes are also expensive and contribute to the overall cost of the product being manufactured in terms of both material and operating costs. In addition, if the zinc processing equipment fails, the entire production line may be halted. As a result, productivity of the entire manufacturing line is compromised. As such, a need exists to eliminate zinc coating and provide adequate corrosion resistance in the base material itself.
Typical applications for the aluminum alloys discussed above include automotive heater cores, radiators, evaporators, condensers, charge air coolers, and transmission/engine oil coolers. One particular application that requires demanding properties is flat tubing that is employed in heat exchangers. In these applications, fin stock is arranged between stacked tubing that carries the cooling media. The tubing is situated between headers which redirect the cooling media flow between layers of tubing and which also can contain inlets and outlets. Typically, the fin stock is clad with a brazing material and the entire assembly is brazed together in a controlled atmosphere braze (CAB) process using a brazing flux. The flat tubing may be extruded as a multi-channel tubing, commonly referred to as micro-multivoid tubing (MMV tubing).
FIG. 1
shows a partial cross sectional view of a typical MMV tubing designated by the reference numeral
10
. The portion of the MMV tubing depicted has sidewalls
1
, each joined together by endwalls
3
(one shown). The tubing is separated into a series of voids
5
by walls
7
extending between the sidewalls
1
. In certain applications, the MMV tubing is extruded at extremely light gauges, often times with sidewall thicknesses below 0.020 inches (0.51 mm).
Typically, these types of tubing are made from AA1000 series alloys such as AA1100, as well as AA3000 series alloys like 162 and 171.
One significant problem with this type of tubing is an increased number of failures in service due to corrosion. When this tubing is used in heat exchanger manufacture, stacked tubing is arranged with two sided braze clad fin stock positioned therebetween and the assembly is brazed together. During the brazing cycle, the tubing may see temperatures near its melting point and severe grain growth effects are prevalent.
Referring to
FIG. 2
, a cross sectional portion
9
of the MMV tubing of
FIG. 1
is shown with an exemplary post-braze grain structure
20
. As described above, when the MMV tubing is subjected to brazing temperature, significant grain growth can occur such that a single grain
11
can extend across the sidewall
1
. With the formation of a single grain across the sidewall
1
, a single grain boundary
13
can extend from the outer surface
15
of the sidewall to the inner surface
17
in one of the voids
7
. The grain boundary
13
becomes an easy path for corrosion to occur through the tubing sidewall
1
. This is more pronounced because the grain body is relatively much more corrosion resistant. Hence, the grain boundary is the weaker link for corrosion.
As noted above, a myriad of problems also exist in this field of aluminum alloys and heat exchanger applications when zinc is used as a coating agent.
Accordingly, a need has developed to provide an improved material for heat exchanger use, particularly MMV tubing, which overcomes the drawbacks to the prior art problems noted above. The present invention solves this need by providing an aluminum alloy composition having controlled amounts of iron, manganese, zinc, zirconium, vanadium, titanium, and other elements that effectively inhibit excessive grain growth in thin wall structures when exposed to brazing temperatures, while still maintaining extrudability and corrosion resistance.
SUMMARY OF THE INVENTION
Accordingly, it is a first object of the present invention to provide an improved aluminum alloy composition that is ideally suited for use in heat exchanger applications.
Another object of the present invention is a composition having controlled amounts of iron, manganese, zinc, zirconium, vanadium, titanium, and other elements to inhibit grain growth when the composition is exposed to brazing temperatures while still maintaining extrudability and corrosion resistance.
A still further object of the present invention is a method of brazing which utilizes an aluminum alloy composition as extruded and bare or uncoated tubing for heat exchanger applications.
Yet another object of the invention is an aluminum alloy base material that has adequate corrosion resistance but without the presence of a zinc coating.
One other object of the present invention is a method of making extruded MMV tubing using the inventive aluminum alloy composition.
Other objects and advantages of the present invention will become apparent as a description thereof proceeds.
In satisfaction of the foregoing objects and advantages, the present invention provides a novel aluminum alloy composition consisting essentially of, in weight percent;
between about 0.05 and 0.5% silicon;
up to 0.7% copper;
less than 0.01% nickel;
less than or equal to 1.0% magnesium;
up to 0.5% chromium, and
when iron is between zero and 0.09%, the composition consists essentially of:
an amount of manganese between 0.05% and 0.50%, an amount of zinc between 0.10 and 0.50%, and an amount of zirconium between 0.05 and 0.40%, and
additional amounts of one of (a), (b), or (c), wherein:
(a) is an additional amount of manganese up to 0.70%, or an amount of vanadium between 0.05 and 0.50%;
(b) is either an additional amount of manganese up to 0.70% and an amount of titanium between about 0.10 and 0.40%, or an additional amount of manganese up to 0.70% and an amount of vanadium between 0.05 and 0.50%; and
(c) is an additional amount of manganese up to 0.70%, and an amount of titanium between 0.10 and 0.40%, and an am

Affiliated with

Also associated with

Rating

Corrosion and grain growth resistant aluminum alloy does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Corrosion and grain growth resistant aluminum alloy, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Corrosion and grain growth resistant aluminum alloy will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3026249