Copper alloy and process for obtaining same

Metal treatment – Process of modifying or maintaining internal physical... – With casting or solidifying from melt

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C148S681000, C148S682000, C148S685000

Reexamination Certificate

active

06436206

ABSTRACT:

BACKGROUND OF THE INVENTION
There is a variety of copper base alloys that are used in connector, lead frame and other electrical applications because their special properties are suitable for these applications. However, there is a need for copper base alloys that can be used in applications that require high yield strength in the order of 80-100 KSI, together with good forming properties that allow one to make 1800 badway bends with a R/T ratio of 1 or less plus good electrical conductivities of 30% or better, plus low relaxation of stress at elevated temperatures and freedom of stress corrosion cracking. These represent a highly desirable combination of properties. Alloys presently available do not meet all of these requirements or have high costs that make them less economical in the marketplace or have other significant drawbacks. It is highly desirable to develop a copper base alloy satisfying the foregoing goals.
Beryllium copper generally has very high strength and conductivity along with good stress relaxation characteristics; however, these materials are limited in their forming ability. One such limitation is the difficulty with 180° badway bends. In addition, they are very expensive and often require extra heat treatment after preparation of a desired part. Naturally, this adds even further to the cost.
Phosphor bronze materials are inexpensive alloys with good strength and excellent forming properties. They are widely used in the electronic and telecommunications industries. However, they tend to be undesirable where they are required to conduct very high current under very high temperature conditions, such as for example under conditions found in automotive applications for use under the hood. This combined with their high thermal stress relaxation rate makes these materials less suitable for many applications.
High copper high conductivity alloys also have many desirable properties, but generally do not have mechanical strength desired for numerous applications. Typical of these alloys include but are not limited to copper alloys 110, 122, 192 and 194.
Representative prior art patents include U.S. Pat. Nos. 4,666,667, 4,627,960, 2,062,427, 4,605,532, 4,586,967 and 4,822,562.
Accordingly, it is highly desirable to develop the copper base alloys having a combination of desirable properties making them eminently suitable for many applications.
SUMMARY OF THE INVENTION
In accordance with the present invention, it has been found that the foregoing objective is readily obtained.
Copper base alloys of the present invention consist essentially of tin in an amount from 1 and up to 4%, and preferably in an amount greater than 2.5% up to 4.0%, phosphorous from 0.01 to 0.2% and particularly from 0.01 to 0.05%, iron from 0.01 to 0.80% and preferably 0.05 to 0.8% and particularly from 0.05 to 0.25%, zinc from 0.1 to 12% and preferably 0.3 to 5.0%, and the balance essentially copper. It is particularly advantageous to include nickel and/or cobalt in the alloy in an amount from 0.001 to 0.5% each. It is desirable and advantageous to provide particles of iron phosphide and/or iron nickel phosphide and/or iron magnesium phosphide and/or magnesium nickel phosphide and/or magnesium phosphide or a combination thereof, uniformly distributed throughout the matrix. The phosphide particles have a particle size of 50 Angstroms to 0.3 microns and generally and advantageously include a finer component and a coarser component. The finer component has a particle size of 50-250 Angstroms preferably from 50-200 Angstroms, and the coarser component has a particle size generally from 0.075 to 0.3 microns and preferably from 0.075 to 0.125 microns.
Percentage ranges throughout this application are percentages by weight.
The alloys of the present invention have been found to enjoy a variety of excellent properties making them eminently suitable for use as connectors, lead frames, springs and other electrical applications. The alloys have an excellent and unusual combination of mechanical strength, formability, thermal and electrical conductivities, and stress relaxation properties.
The process of the present invention comprises: casting a copper base alloy having a composition as aforesaid; homogenizing at least once for at least one hour at from 1000-1450° F.; rolling to final gauge including at least one process anneal for at least one hour at 650-1200° F. followed by slow cooling at 20-200° F. per hour; and stress relief annealing at final gauge for at least one hour at 300-600° F., thereby obtaining a copper alloy including phosphide particles uniformly distributed throughout the matrix with a size and distribution as aforesaid. Nickel and/or cobalt may be included in the alloy as above.
DETAILED DESCRIPTION
The preferred alloys of the present invention and the first embodiment includes tin from 2.5-4%, phosphorus from 0.01-0.20%, iron from 0.05-0.80%, zinc from 0.3-5%, balance essentially copper, with phosphide particles uniformly distributed throughout the matrix. These alloys of the present invention have a 0.2% offset yield strength of 80 to 100 KSI along with the ability of the alloys to make 180° badway bends at a radius no more than the thickness of the alloy strip. In addition, the alloys achieve an electrical conductivity of approximately 30% IACS or better which makes the alloys suitable for high current applications. The foregoing combined with a good thermal conductivity of 75 BTU/SQ FT/FT/HR/DEGREE F and a metallurgical structure that give the alloys a high stress retention ability, for example, over 60% at 150° C., after 1,000 hours with a stress equal to 75% of its yield strength, on samples cut parallel to direction of rolling, makes these alloys very suitable for the high temperature conditions under an automobile hood as well as other applications requiring a combination of high conductivity and high stress retention capabilities. Moreover, the present alloys do not require further treatment by stampers and are relatively inexpensive.
As indicated hereinabove, the alloys of the present invention preferably include tin in an amount greater than 2.5% and up to 4.0%, phosphorous is present in an amount from 0.01 to 0.2% and particularly 0.01 to 0.05%. Phosphorous allows the metal to stay deoxidized making it possible to cast sound metal within the limits set for phosphorous, and with thermal treatment of the alloys phosphorous forms a phosphide with iron and/or iron and nickel and/or iron and magnesium or combinations of these elements, if present, which significantly reduces the loss in conductivity that would result if these materials were entirely in solid solution in the matrix. It is particularly desirable to provide iron phosphide particles uniformly distributed throughout the matrix as these help improve the stress relaxation properties by blocking dislocation movement.
Iron in the range of 0.05 to 0.8% and particularly 0.05 to 0.25% increases the strength of the alloys, promotes a fine grain structure by acting as a grain growth inhibitor and in combination with phosphorous in this range helps improve the stress relaxation properties without negative effect on electrical and thermal conductivities.
Zinc in the range of 0.3 to 5.0% helps deoxidize the metal, helping the castings to be sound without use of excessive phosphorous that can hurt conductivities. Zinc also helps in keeping the metal oxide free for good adhesion in plating. It is desirable to restrict the upper zinc level under 5.0% and particularly under 2.5% in order to keep the conductivities high. Zinc in the lower amounts of this range will achieve even higher conductivities.
Nickel and/or cobalt in an amount from 0.001 to 0.5% each, and preferably 0.01 to 0.3% each, are desirable additives since they improve stress relaxation properties and strength by refining the grain and through distribution throughout the matrix, with a positive effect on the conductivity. Nickel is preferred.
One may include one or more of the following elements in the alloy combination: aluminum, silver, boron, beryllium, calcium, ch

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Copper alloy and process for obtaining same does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Copper alloy and process for obtaining same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Copper alloy and process for obtaining same will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2883468

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.