Copper activated thermoluminescence dosimeter and method

Details Copper activated thermoluminescence dosimeter and method Copper activated thermoluminescence dosimeter and method

1996-07-25

1997-07-29

Bell, Mark L.

Glass manufacturing

Processes

With chemically reactive treatment of glass preform

501 54, 2523014R, C03C 1500, C03C 306, C09K 1108

Patent

active

056518048

ABSTRACT:
A novel copper activated thermoluminescence dosimeter comprising a glass composition having: about 94-97 weight percent SiO.sub.2 ; about 0.4 to 2 weight percent Al.sub.2 O.sub.3 ; about 0.02 to 1 weight percent M.sub.2 O, where M comprises Na.sup.+ or K.sup.+ ; about 2 to 6 weight percent B.sub.2 O.sub.3 ; and Cu(I), where Cu(I) is present at a level between about 10.sup.18 to 10.sup.19 ions/cm.sup.3 ; method of making the same.

REFERENCES:
patent: 3779781 (1973-12-01), Baak et al.
patent: 3855144 (1974-12-01), Barber et al.
patent: 4248731 (1981-02-01), Takenaga et al.
patent: 4303547 (1981-12-01), Brownlow
patent: 4798681 (1989-01-01), Overslvizen et al.
patent: 4814105 (1989-03-01), Overslvizen et al.
patent: 5071793 (1991-12-01), Jean et al.

Affiliated with

Also associated with

Rating

Copper activated thermoluminescence dosimeter and method does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Copper activated thermoluminescence dosimeter and method, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Copper activated thermoluminescence dosimeter and method will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-630561