Specialized metallurgical processes – compositions for use therei – Processes – Producing or treating free metal
Reexamination Certificate
1999-12-08
2001-09-18
King, Roy (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Processes
Producing or treating free metal
C423S027000, C423S034000, C423S395000, C075S635000, C075S636000, C075S713000, C075S744000
Reexamination Certificate
active
06290747
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to the manufacture of silver metal and in particular to the preparation of silver metal with a very high degree of purity. More specifically, this invention relates to a novel multi-step process for converting impure silver halide containing ash to ultra-pure silver metal.
BACKGROUND OF THE INVENTION
Silver that is of very high purity has many important industrial applications including the manufacture of materials in the electronics industry and the preparation of silver nitrate for the photographic industry. Typically, the process for purifying silver relies on smelting, electrolysis or a combination of smelting and electrolysis.
Smelting is a pyrometallurgical process by which crude silver metal and or ionic silver containing compounds are heated in the presence of a flux. The silver ions are chemically reduced to silver metal and as a result of the extreme temperatures of the process, the silver metal melts and drops to the bottom of a reaction furnace. Meanwhile, base metals such as copper, iron, zinc, lead, nickel, etc., if present, remain oxidized and accumulate in the less dense slag waste stream. Finally, the molten silver is poured from the smelter and cooled in a casting. The process of smelting is inefficient with respect to mass balance and requires several days to complete. Furthermore, the precious metals, namely gold, palladium, platinum, rhodium, iridium, osmium and ruthenium remain in the purified silver and require separation during a secondary refining process such as electrorefining. Finally, sulfur and its congeners, selenium and tellurium, if not oxidized in the smelter, will be present in the purified silver and a second refining might be necessary.
Electrorefining also may be used to purify silver. Here, impure silver metal, typically pre-purified by smelting, is cast as an anode and is deposited as purified silver crystals at the cathode in an electrolytic cell. However, in this process silver ions are required to pass through an electrolyte, typically silver nitrate, that may contain an increased concentration of impurities from previously dissolved anodes. Frequent purges of the electrolyte are required to produce silver that is acceptable for use in applications that require high purity. Additionally, varying levels of sulfate, antimony, iron and sulfide are often found to be associated with electrorefined silver.
Hydrometallurgy is a less widely practiced method for refining silver. In practice, aqueous solutions of silver ions are reduced chemically to yield silver metal and, ideally, impurities are left in the aqueous phase. Depending on the identity of the impurities present in the silver matrix, it may be difficult to select a reducing agent of the appropriate strength. While the strength of the reducing agent or its propensity to reduce other species can be obtained from a table of thermodynamic electrochemical reduction potentials; it is not always possible to select a reducing agent that will selectively reduce silver ions to silver powder and leave all of the matrix impurities in a concentrated solid or in the aqueous phase.
The following are representative of the many references describing the purification of ionic silver or the preparation of silver powder from ionic silver solutions. For example, U.S. Pat. No. 5,749,940 describes a process for producing silver from de-copperized anode slime. The method relies on several leaching and separating steps and the one time addition of a reducing agent, dextrose, or hydrazine-a known carcinogen. GB 2,236,116 describes a process of producing silver powders of desired particle sizes from silver nitrate using formate and citrate in a one time addition. JP 61276907 describes the formation of monodisperse silver powders by treatment of aqueous silver nitrate in a gelatin solution with glucose. It also has been reported that crude silver chloride may be converted to silver oxide via the addition of caustic and subsequently reduced to silver metal by dextrose; but the final silver sponge requires secondary purification using electrorefining (Ackerman, John B.; Nordwick, Suzzann M.; Anderson, Corby G.; Krys. L. Ernst. Sunshine Min. Co. Kellog, ID, 83837, USA. Hydrometall. Proc. Milton E. Wadsworth Int. Symp., 4
th
(1993), 477-98. Editors: Hiskey, J. Brent; Warren, Garry W. Publisher: Soc. Min. Metall. Explor., Littleton, Colo.; Chpt. 30, pp 492-493).
RO 85165 describes a process of producing silver powder from silver nitrate using a one step addition of citric acid. Historically, metallic impurities are removed from aqueous silver ions by treating the matrix with a reagent to precipitate the impurities as metallic hydroxides. U.S. Pat. No. 2,543,792 describes the purification of aqueous silver nitrate with carbon, activated alumina and silver oxide. U.S. Pat. No. 2,614,029 describes the treatment of aqueous silver nitrate with silver oxide to maintain a pH of 6.1, the separation of the metal hydroxides which result from the solution, and the contact of the solution with a water insoluble porous solid absorbent such as activated alumina or magnesia. U.S. Pat. No. 3,554,883 describes a process of mixing silver nitrate with silver oxide to yield a pH of 5.1 to 5.8 causing the formation of a precipitate which is removed. The silver nitrate is subsequently treated with a second addition of silver oxide to yield a pH of 5.9 to 6.3 causing the formation of a second precipitate which is removed yielding a purified silver nitrate solution. Finally, U.S. Pat. No. 5,000,928 describes a process that yields ultra-pure silver nitrate from crude silver using a one time addition of sodium hydroxide to remove metal contaminates as hydroxy or oxy compounds; and a one time addition of sodium formate to yield silver metal which is subsequently converted to ultra-pure silver nitrate.
Even with all of the work which has been done around the purification of impure silver metal, there still remains a need for a less complex process to purify silver. Also needed is a process which has lower silver loss in the recovery stream. This must be accomplished while providing a silver purity level at least as high as that achieved by current technology.
SUMMARY OF THE INVENTION
This invention provides a method for preparing ultra-pure silver from a crude silver halide matrix containing metallic and/or non-metallic impurities, said method comprising;
roasting the crude silver halide matrix to substantially remove carbonaceous material;
treating the roasted crude silver halide matrix with ammonium hydroxide to dissolve the silver halides and form an ammonium hydroxide reaction mixture;
adding an initial reducing agent to the ammonium hydroxide reaction mixture to precipitate a crude silver powder mixture;
separating the crude silver powder mixture from the ammonium hydroxide reaction mixture
dissolving the crude silver powder mixture in nitric acid to form a crude silver nitrate solution;
adding a first selective reducing agent to the crude silver nitrate solution to precipitate a silver/contaminant matrix and form a partially purified silver nitrate solution;
separating the partially purified silver nitrate solution from the precipitated silver/contaminant matrix;
adding a second selective reducing agent to the partially purified silver nitrate solution to precipitate pure silver powder; and
isolating the pure silver powder.
This invention is particularly useful when the first and second selective reducing agents are both sodium formate.
The method of the invention has numerous advantages. The inventive process produces silver that is of high enough purity for direct use in the production of photographic quality silver nitrate. The process is simple and employs inexpensive and commercially available reagents for the preparation of the ultra-pure silver metal. The by-products of the silver metal forming reaction are benign and the platinum group metal impurities are collected and concentrated in the first reduction-fraction and can be refined further or sold. The process has lower silver lo
Cleary Brian P.
Kiehl Gary G.
White Weimar W.
Eastman Kodak Company
King Roy
McGuthry-Banks Tima
Meeks Roberts Sarah
LandOfFree
Conversion of impure silver halide to ultra-pure silver metal does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Conversion of impure silver halide to ultra-pure silver metal, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Conversion of impure silver halide to ultra-pure silver metal will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2549790