Single-crystal – oriented-crystal – and epitaxy growth processes; – Apparatus – With means for treating single-crystal
Reexamination Certificate
2001-12-11
2004-06-01
Kunemund, Robert (Department: 1765)
Single-crystal, oriented-crystal, and epitaxy growth processes;
Apparatus
With means for treating single-crystal
C117S004000, C117S006000, C117S007000, C117S008000, C117S009000, C117S204000, C117S205000
Reexamination Certificate
active
06743294
ABSTRACT:
BACKGROUND OF THE INVENTION
This invention relates to the purifying of crystal material, the doping of the material and the growth of crystals.
Bridgeman, Bridgeman-Stockbarger, Czochralski and variations have been used for crystal growth. Depending on the crystal growth method, the crystal type and the crystal size, one has to overcome sets of problems. This invention relates to the purification of the crystal material and the crystal growth process itself.
Crystal size and the quality of the crystal starting material play important roles in the production of scintillation crystals. The starting material labeled “scintillation grade” is of five 9's purity 0.9999%. Often the starting material has poor stoichiometry ratio. Growing crystals in a closed type system that have large diameters and up to over 2000 pounds in weight result in crystals that have poor crystal quality. Crystal purity, dopant distribution, defect density and distribution and built-in stress imposed on the crystal during the crystal growth process and the crucible removal may be at unacceptable levels. With the exception of small crystal portions grown at the beginning of the crystal growth, crystals may have lower purity than the starting material. Dopant concentration varies dramatically. That in turn creates uneven light output and decreases the energy resolution of scintillation crystals. When handling large size crystals during the hot transfer, the crystals release large portions of iodine and thallium iodine vapors. Exposure to ambient temperature creates various defects and defect densities in the hot crystals.
The current practices where large barrel-shaped crystals are grown for all applications, regardless of the fact that most applications use rectangular shapes, makes the yields rather low. Scaling up crystal plate sizes from 0.5-1 inch thick slabs cut perpendicular to the crystal length of a barrel-shaped crystal requires large financial investments. At the same time increasing slab geometry increases the crystal production cost by decreasing the growth rate and lowers the crystal quality and yield.
Existing purification methods include supplying a gaseous medium to a surface of a melt carried in a crucible. Those methods require extended times for purification, up in the range of 96 hours. Those methods also ineffectively cure the melt, as lower portions of the melt are never purified.
During melt purification, impurities react with the gas molecules and exit the melt in a gaseous phase. Some impurities react and precipitate from the melt as a sludge. Other reacted impurities float to the surface.
Needs exist for purification systems that remove impurities faster and more efficiently.
These problems and many more remain in the present practices. Needs exist for new approaches for crystal material purification and the crystal growth processes.
Purifying of crystals by reactant gas contact in current systems results in delays and adds significant times to the crystal growth process.
SUMMARY OF THE INVENTION
Reactive gas is released through a crystal source material or melt to react with impurities and carry the impurities away as gaseous products or as precipitates or in light or heavy form. The gaseous products are removed by vacuum and the heavy products fall to the bottom of the melt. Light products rise to the top of the melt. After purifying, dopants are added to the melt. The melt moves away from the heater and the crystals formed. Subsequent heating zones re-melt and refine the crystal, and a dopant is added in a final heating zone. The crystal is divided, and divided portions of the crystal are re-heated under pressure for heat treating and annealing.
The invention provides multi zone plate crystal growth and purifying.
The new continuous feed multi-zone crystal grower is capable of growing crystals with very large dimensions under reactive atmospheres. The invention produces high purity crystals with very uniform doping concentrations regardless of the crystal size. The dopant level and the residual impurities are controlled in situ within the crystal feed chamber and during the crystal growth process. Crystal applications include nuclear medicine, high energy physics, optics and others where economical production of high purity and large size crystals are required.
The invention provides horizontal (or inclined under some angle) continuous crystal growth process for plates of any dimensions.
Reactive gas permeates start-up material, crystal powder or polycrystalline material or a crystal melt.
Stoichiometry control or “repair” of start-up material is achieved using the present invention.
Multi-zone traveling, stationary immersed and non-immersed heaters, resistive and RF heating elements, or other type heaters are used. This allows controlled gradient crystal growth of any size crystals.
A traveling crucible or crystal slab can be used if the heaters are stationary.
The present invention can be attached as a module to heaters for in situ purification and dopant control.
Dopant concentration control can be achieved by adding dopant in solid or gaseous form. If excess dopant has to be controlled, the excess is either neutralized via chemical reaction or by dilution with pure melt.
For very high purity crystals or crystals with very large sizes, residual impurities control can be achieved by removing the melt from one of the molten zones via vacuum suction and melt draining.
High temperature and high pressure annealing of the plates in final sizes enhances the crystal quality properties.
The invention eliminates cutting of at least one dimension of the crystal before further processing.
A preferred continuous crystal plate growth apparatus has a source of starter material. A valve supplies material from the starter material source. A first, hot zone communicates with the valve for heating the material. A dopant source and a dopant controller are connected to the hot zone for supplying dopant into the material in the hot zone. A second reduced heat zone beyond the hot zone reduces heat in the material, which forms a solid plate. A receiver receives the solid plate from the second, reduced heat zone and advances the solid plate. A lowered temperature heating zone adjacent the receiver lowers temperature of the solid crystal plate on the receiver. An enclosure encloses the zones and the solid crystal plate in a controlled gaseous environment.
A large heater overlies the small heater. The large heater has first and second zones, and the small heater has the first hot and second reduced heat zones. Baffles separate the first and second zones of the heaters.
The first zone of the small heater produces a crystal melt temperature higher than a crystal melting temperature in the material. The second zone of the small heater produces a temperature lower than the melting temperature. The temperature in the material at the small heater baffle is about the melting temperature. The large heater first zone provides heat below the melting temperature, and the large heater second zone provides a lower heat.
Preferably the receiver is a conveyor which moves at a speed equal to a crystal growth rate.
A second source of starter material and a second valve are connected to the hot zone for flowing material from the second source to the hot zone.
The crystal melt or starter material is purified in a chamber having a bottom and sides. A lid covers the chamber. An opening introduces liquid or solid material into the chamber. An outlet near the bottom of the chamber releases crystal melt or starter material from the chamber. A shut-off valve opens and closes the outlet. A source of reactive gas is connected to the chamber and extends into a bottom of the chamber. A reactive gas release barrier near the bottom of the chamber slowly releases reactive gas into the crystal starter material. A gas space is located at the top of the chamber above the crystal melt or starter material. An exhaust line is connected to the space at the top of the chamber for withdrawing gas from the top of the chamber. A heater adja
Creighton Wray James
Kunemund Robert
Narasimhan Meera P.
Optoscint, Inc.
LandOfFree
Continuous crystal plate growth process and apparatus does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Continuous crystal plate growth process and apparatus, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Continuous crystal plate growth process and apparatus will most certainly appreciate the feedback.