Metal founding – Process – Shaping liquid metal against a forming surface
Reexamination Certificate
2001-03-09
2003-09-02
Lin, Kuang Y. (Department: 1725)
Metal founding
Process
Shaping liquid metal against a forming surface
C164S417000
Reexamination Certificate
active
06612364
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a continuous slab casting method, especially for thin slabs, in which a soft reduction is effected. More particularly this invention relates to a continuous casting method for slabs and especially thin slabs in which the path of the metal from below the mold includes a plurality of strand-guide segments with adjustable gaps between opposite sides, usually formed by roller pairs and whereby to reduce segregation and core porosity, the cast strand is subjected to a reduction in thickness in the region of residual solidification by appropriate adjustment of the opening between the opposite sides of the respective strand guide segment.
BACKGROUND OF THE INVENTION
In the method described in DE 41 38 740 A1 and U.S. Pat. No. 5,348,074, the strand is subjected to soft reduction in a portion of its path prior to full hardening, the slab entering that segment or zone before it is hardened through its thickness and leaving that zone when it is fully hardened. That requires particular care with respect to the casting velocity. In the region of final hardening, the thickness reduction, for example, for thin slabs is between 0.5 and 3 mm per meter of the slab length. The roller pair of the segments through which the strand passes are thus progressively more closely spaced in the soft reduction region so as to improve the internal quality of the strand in the residual hardening region.
EP 0 834 364 describes a method of and an apparatus for high speed continuous casting with a thickness reduction during hardening, whereby the melt is cast into an oscillating mold and the strand cross section is linearly reduced in thickness over a minimum length of the strand guide directly following the mold. Thereafter a further reduction in the thickness of the strand is effected over the remainder of the strand guide by soft reduction until the most immediately before final solidification or the liquidus tip. The liquidus tip or liquidus part is the point at which the liquid core ends and at which thereafter, the slab is fully solidified. In this system, the degree of deformation of the cross sectional reduction of the strand is such that the critical deformation of the strand shell (solidified material surrounding the liquid core) for a given high casting speed and steel quality, should not be exceeded.
EP 0 177 796 B1 discloses a method of guiding and straightening a cast strand in the straightening an outlet region of an arcuate continuous caster, whereby opposite rollers of the segments are biased by a spring force against the ferrostatic pressure within the strand, the rollers being spaced apart at a distance corresponding to the thickness of the strand as it emerges from the mold. This region of the guide is followed by a region in which the strand is compressed to a greater extent and over these regions the spring force is reduced. In this technique, the gap between opposite sides of the guide and thus the spacing of the opposite rollers can be adjusted in a stepless manner by hydraulic cylinders and servovalves using inductive displacement measurements based upon the computer-determined or measured location of the liquidus tip.
The slabs or billets resulting from the processes described and produced by continuous casting are starting materials for rolled products, especially for the production of strip or plates in the rolling mill.
In continuous casting and especially the continuous casting of thin slabs, the aforementioned soft reduction can reduce segregation in the strand and produce a relatively optimum lattice or grain structure in the solidified slab when the thickness reduction immediately upstream of the liquidus point is between 0.5 and 3 mm per meter of the strand. The upper yokes of the strand guide can thus have their rollers mounted with an inclination between the inlet and outlet sides so that the guides provided a smaller mouth width or clear opening at the outlet side than at the inlet side. In many cases, the already solidified edge portions of the strand are subjected to further reduction by the rollers of the strand guides. This can give rise to an unnecessary increase in the stressing of the rollers and their bearings without positively affecting the internal quality of the slab structure in the edge regions.
OBJECTS OF THE INVENTION
It is an object of the invention to provide a more effective method of improving the internal structure of a continuously cast slab and especially a continuously cast thin slab which is to undergo soft reduction in the manner described, but without the increased roller and bearing loading hitherto encountered.
Another object of the invention is to provide an improved method of continuously casting slabs and especially thin slabs which will allow the thickness reduction to act on the central part of the strand, sparing the already hardened edge regions from the thickness reduction action.
Still another object of this invention is to provide an improved method of producing continuously cast slabs in which soft reduction is used without the heavy wear of the rollers and bearings characterizing earlier systems.
SUMMARY OF THE INVENTION
These objects and others which will become apparent hereinafter are attained, in accordance with the invention in that the cast strand, upstream of the end of the soft reduction zone is permitted to bulge by a corresponding opening or gap between the opposite sides or rollers of a guide segment by ferrostatic internal pressure and the bulge is then completely or partly pressed back down in the soft reduction stretch to the slab thickness which is maintained in the residual solidification region.
More particularly, a continuous slab casting method can comprise the steps of:
(a) continuously casting a molten metal into a continuous casting mold and solidifying a shell of the metal around a liquid core in a solidifying strand emerging downwardly from the mold;
(b) passing the solidifying strand in succession through a plurality of strand guide segments each having an adjustable gap between opposite sides thereof thereby applying compression to opposite sides of the solidifying strand to reduce a thickness thereof by soft reduction to limit segregation and core porosity in the slab produced over a soft-reduction portion of a path of the strand immediately upstream from a liquid-core tip representing a boundary between full solidification and partial solidification of the strand;
(c) upstream of the soft-reduction portion of the path increasing the gap between the opposite sides of at least one of the strand guide segments from the gap between a more upstream strand guide segment to produce a bulge in the shell as a result of internal ferrostatic pressure on the shell; and
(d) pressing the bulge inwardly to a slab thickness in the soft-reduction portion of the path.
The bulging which is permitted, referred to here as targeted bulging since the extent thereof is controlled, is determined by the corresponding setting of the width of the guide upstream of the soft reduction zone and thus the mouth width or roller spacing in the bulging region. Only in the soft reduction zone is the bulge completely or partly pressed back to the strand thickness which prevails at residual solidification.
By comparison with the earlier approaches, for the same thickness reduction and core compaction, a reduced compaction force is required with the invention and the roller and bearing loading is reduced.
This allows the support structure for the guide segments to be less complicated and dimensioned so as to be smaller while enhancing strand quality in terms of reduction of segregation and core porosity. If a force similar to that used in earlier systems can be maintained, greater thickness reduction and core compaction can be achieved.
According to a feature of the invention, the cast strand prior to reaching the soft reduction zone is initially subjected to a compaction by reduction in the mouth width of a respective guide segment and while a substantial core of liquid is present in a for
Demag Aktiengesellschaft
Dubno Herbert
Lin Kuang Y.
LandOfFree
Continuous casting method with soft reduction does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Continuous casting method with soft reduction, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Continuous casting method with soft reduction will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3039322