ABSTRACT:
A new type of aromatic polyamide powder including a large number of fine coalescible particles which have an average size of from 0.1 to 10 .mu.m, which include at least one aromatic amide polymer including 40 to 100 molar % of recurring m-phenylene isophthalamide units and 0 to 60 molar % of at least one other type of additional recurring aromatic amide units, for example, m-phenylene terephthalamide units, and which coalesce with each other to form porous agglomerates having an average size of from 10 to 400 .mu.m and a surface area of from 1 to 20 m.sup.2 /g, and can be compression molded, optionally in mixture with a reinforcing additive, for example, aromatic polyamide fibers having a length of 3 mm or less, at a temperature of 200.degree. to 400.degree. C. under a pressure of 300 to 1000 kg/cm.sup.2 for 20 minutes to 5 hours, to produce shaped articles having excellent mechanical properties and appearance.
REFERENCES:
patent: 3413394 (1968-11-01), Jordan
patent: 3925323 (1975-12-01), Turnbull
patent: 3955236 (1976-06-01), Turnbull
patent: 4036907 (1977-07-01), Turnbull
patent: 4283361 (1981-08-01), Longworth
Fujie Hiroshi
Matsui Hideo
Noma Takashi
Foelak Morton
Teijin Limited
LandOfFree
Compression moldable aromatic polyamide powder and process for p does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Compression moldable aromatic polyamide powder and process for p, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Compression moldable aromatic polyamide powder and process for p will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2219804