Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
1998-03-20
2001-01-16
Sellers, Robert E. L. (Department: 1712)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C428S413000, C428S417000, C428S418000, C522S049000, C522S062000, C522S064000, C522S146000, C528S026000, C528S027000, C528S029000
Reexamination Certificate
active
06174967
ABSTRACT:
BACKGROUND OF THE INVENTION
There has been considerable interest in the development of coating compositions with reduced amounts of volatile organic compounds (VOCs), particularly in light of regulations on VOC content. Ultraviolet (UV) curable coating compositions have emerged as one type of coating with reduced VOC content. Furthermore, many UV curable coating compositions offer the advantages of fast curing speed, high energy efficiency, and low capital investment and space requirements. These coatings are especially suitable for the wood/plastics coating (e.g., furniture), metal decorating, and paper printing industries.
The curing reaction of many UV curable coatings takes place at nearly ambient temperatures and, typically, no solvent or water evaporation is involved. There are two principle mechanisms for polymerizing UV coatings; free radical and cationic. In free radical initiated polymerization, free radicals are generated using either unimolecular photoinitiators (benziketals) or bimolecular photoinitiators (thioxanthones). Multi-functional acrylate esters are often used in this type of polymerization. Free radical polymerization, however, often exhibits oxygen inhibition of propagating radicals and acrylate monomers also represent odor and health hazard problems.
For cationic UV polymerization, typical initiators are salts which generate super acids or Bronsted acids under UV irradiation. Typical monomers/oligomers for the cationic coatings include, for example, vinyl ethers, propenyl ethers, and compounds having epoxide functional groups. These compounds can homopolymerize to form a coating.
Epoxide-containing compounds have fast cure response and the resulting cured coating is resistant to hydrolysis. In addition, aliphatic epoxide-containing compounds have excellent photostability. Epoxide-containing compounds, however, typically polymerize to form hard, brittle coatings. To increase the impact resistance, toughness, and flexibility of the cured coating, polyols have been added to the curable coating composition. The epoxide-containing compounds react with the polyols during the polymerization process.
Polyols act as reactive diluents in these curable coating compositions. Reactive diluents function as solvents to dilute viscous oligomers and reduce the overall viscosity of the curable coating composition. Reactive diluents also co-react with the monomer and oligomers to form integral films. Reactive diluents are typically compounds with relatively low molecular weights and multiple reactive functionalities. There is a need for the development of reactive diluents for use with epoxide-containing compounds to provide desired properties to films formed using UV curable coating compositions.
SUMMARY OF THE INVENTION
Generally, the present invention relates to epoxy-based curable coatings. More particularly, the present invention is related to epoxy-based curable coatings having a reactive diluent that includes an organosilane compound. One embodiment of the invention is directed to a curable composition having an epoxy component and an organosilane component. The epoxy component includes at least one epoxy compound having two or more epoxide functional groups. The organosilane component includes at least one organosilane compound having two or more silyl ether groups.
Another embodiment of the invention relates to a polymeric composition formed by the reaction, in the presence of a photoinitiator, between an epoxy component and an organosilane component. The epoxy component has at least one epoxy compound with two or more epoxide functional groups. The organosilane component has at least one organosilane compound with two or more silyl ether groups.
Yet another embodiment of the invention provides a reactive diluent for a curable composition. The reactive diluent includes a compound having the formula:
where R
36
-R
3
are alkyl or cycloalkyl, R
39
is alkylene, Y is —C(O)—R
40
—, —C(O)—R
41
—C(O)—R
42
or —R
43
—, R
40
—R
43
are alkylene, n and m are integers, n is 1 or more, and m is 2 or more. This reactive diluent is a suitable example of an organosilane compound with two or more silyl ether groups.
A further embodiment of the invention relates to a coated substrate including a substrate and a coating on at least one surface of the substrate. The coating includes a product of a reaction, in the presence of a photoinitiator, between a) an epoxy component having at least one epoxy compound with two or more epoxide functional groups and b) an organosilane component having at least one organosilane compound with two or more silyl ether groups.
Another embodiment of the invention provides a method for coating a substrate that includes coating a surface of the substrate with a coating composition. The coating composition includes a) an epoxy component having at least one epoxy compound with two or more epoxide functional groups, b) an organosilane component having at least one organosilane compound with two or more silyl ether groups, and c) a photoinitiator. The coating composition is cured after application to a substrate surface to form a coating.
The above summary of the present invention is not intended to describe each disclosed embodiment or every implementation of the present invention. The Figures and the detailed description which follow more particularly exemplify these embodiments.
REFERENCES:
patent: 3154597 (1964-10-01), McWhorter
patent: 3932339 (1976-01-01), McLeod
patent: 4283513 (1981-08-01), Mikami
patent: 4354013 (1982-10-01), Kimura
patent: 4585534 (1986-04-01), Pasternack et al.
patent: 4593051 (1986-06-01), Koleske
patent: 4874798 (1989-10-01), Koleske et al.
patent: 4977199 (1990-12-01), Koleske et al.
patent: 5077083 (1991-12-01), Lutz et al.
patent: 5155143 (1992-10-01), Koleske
patent: 5366768 (1994-11-01), Kasari et al.
patent: 5376420 (1994-12-01), Yamamoto et al.
patent: 5389727 (1995-02-01), Nakai et al.
patent: 5408001 (1995-04-01), Nakahata et al.
patent: 5492968 (1996-02-01), Nakai et al.
patent: 5525673 (1996-06-01), Nakahata et al.
patent: 5593731 (1997-01-01), Akagi et al.
patent: 5609918 (1997-03-01), Yamaguchi et al.
patent: 5684095 (1997-11-01), Morimoto et al.
patent: 5719234 (1998-02-01), Yabuta et al.
patent: 222582 (1987-05-01), None
patent: 2317386 (1996-03-01), None
patent: 3-190885 (1991-08-01), None
patent: 5-284098 (1995-04-01), None
patent: 855741 (1981-08-01), None
“Compliant Coatings Based on Cycloaliphatic Epoxides and TONE® Polyols”, Union Carbide Chemicals: 1-12 (1986).
“Cycloaliphatic Epoxide Systems”, Union Carbide Chemicals and Plastics Company Inc: 1-28 (1989).
“Cyracure® Cycloaliphatic Epoxides: Cationic UV Cure”, Union Carbide Chemicals and Plastics Company Inc.: 1-24 (Apr. 1992).
“Formulating Ultraviolet Light-Cured Cyracure® Cycloaliphatic Epoxide Coatings”, Union Carbide Chemicals and Plastics Company Inc.: 1-12 (1990).
“Tone® Polyol Reactive Diluents for High-Performance, Low-VOC Coatings”, Union Carbide Corporation: 1-15 (1993).
“Tone® Polyols for High-Performance Urethane Elastomers and Adhesives”, Union Carbide Corporation: 1-25 (1993).
Ali, K.M. et al., “Reactive Diluent Effect on Properties of UV-Cured Films”,Journal of Applied Polymer Science,54: 309-315 (1994).
Brennan, A.B. et al., “Structure-Property Behavior of Novel Ti/Poly (tetramethylene oxide) (PTMO) and Zr/PTMO Hybrid CERAMER Materials Prepared by the Sol Gel Method”,Journal of Inorganic and Organometallic Polymers,1(2): 167-187 (1991).
Crivello, J.V. et al., “The Synthesis and Study of the Photoinitiated Cationic Polymerization of Novel Cycloaliphatic Epoxides”,Journal of Polymer Science: Part A: Polymer Chemistry,33: 2463-2471 (1995).
Decker, C. et al., “Kinetic Study of the Cationic Photopolymerization of Epoxy Monomers”,Journal of Polymer Science: Part A: Polymer Chemistry,28: 3429-3443 (1990).
Huang, H.H. et al., “Ceramers: Hybrid Materials Incorporating Polymeric/Oligomeric Species with Inorganic Glasses by a Sole-Gel Process”,Polymer Bulletin,14: 557-564 (1985).
Koleske, J.V., “Copolymerization and Properties of Cationic, Ultr
Soucek Mark D.
Wu Shaobing
Merchant & Gould P.C.
NDSU--Research Foundation
Sellers Robert E. L.
LandOfFree
Composition of epoxy resin and (cyclo)alkoxy-substituted... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Composition of epoxy resin and (cyclo)alkoxy-substituted..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composition of epoxy resin and (cyclo)alkoxy-substituted... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2484445