Static structures (e.g. – buildings) – Lapped multiplanar surfacing; e.g. – shingle type
Reexamination Certificate
2000-03-27
2003-03-25
Tarazano, D. Lawrence (Department: 1773)
Static structures (e.g., buildings)
Lapped multiplanar surfacing; e.g., shingle type
C052S745190, C428S517000, C428S518000, C428S520000, C428S521000, C264S173160, C264S173190, C156S060000, C156S061000
Reexamination Certificate
active
06536177
ABSTRACT:
BACKGROUND OF THE INVENTION
I. Field of the Invention
This invention pertains to roofing materials. More specifically, the invention concerns a novel composition of a roofing material sheet.
II. Description of the Prior Art
Many types of roofing materials are available, and some of the more popular types include shake, shingles and tiles. Tiles are quite durable; however, their disadvantage is that they require a substantial amount of labor in their installation and can break on impact. Tiles tend to be excessively heavy and dangerous in earthquakes and high winds, and will fall through in the event of a fire. Because they are so heavy, tiles are also expensive to ship. Wood shakes and shingles are subject to breakage, rot and loss of coloration. Their cost is high and they are labor intensive to install. Furthermore, wood shakes and shingles can be relatively heavy, are flammable, porous, and cannot withstand relatively high wind velocity.
The inherent disadvantages of tiles and shakes have led to the development of alternative roofing materials such as plastic. Several different types of plastics are known in the art. However, many of the plastics have disadvantages, which typically may include poor insulating ability, poor ability to withstand the ultra violet (UV) radiation from the sun, and poor ability to withstand shock from an impact (such as from people walking on the roof or hail). Plastics tend also to be brittle and break with age.
Several prior art patents in the field of alternative roofing system include U.S. Pat. No. 5,525,413 issued to Daurer, et. al. entitled Industrial roofing fabric, U.S. Pat. No. 4,507,347 issued to Lupton, et. al. entitled Laminate and U.S. Pat. No. 4,307,552 issued to Votte entitled Synthetic roofing elements of the slate type and method of manufacturing same. However, none of the prior art teaches material having the features and structural composition as will be taught in the present invention.
The composition of the roofing material is highly important in order to maximize protection from the elements and chemical pollution. Chemical pollution results from chemicals contained in smog and other air pollution. These chemicals contribute to color loss, brittleness and other factors that decrease the durability of many types of roofing material.
Thus, it is a primary objective of the present invention to provide a composition of a roofing material that provides ultraviolet protection, flame and fire retardancy, insulation, weatherability, longevity and durability. Another objective of the present invention is to provide a composition of a roofing material that is lightweight and relatively inexpensive and provides maximum protection from the weather and chemical pollution.
SUMMARY OF THE INVENTION
The present invention is a novel composition of materials that can be extruded into sheets to form panels to create a roofing system wherein the panels are formed to interlock with like panels in order to provide a substantially weatherproof covering on a roof. The roofing panel has a sheet member made of a novel composition of matter. The sheet member has a top layer made of ASA (Acrylonitrile/Styrene/Acrylate polymer) and a bottom layer made of formulated PVC (Polyvinylchloride). The two layers are extruded and bonded by pressure or lamination or preferably coextruded. Then the bonded materials are thermoformed to resemble more popular types of roof coverings such as shakes, shingles or tiles.
The bottom layer is made of a proprietary formula of PVC. The present invention uses a specialized ASA with the present invention's proprietary formulation of PVC that is needed to meet roofing material performance such as impact and fire resistance.
The ASA used in the invention has been researched and tested to meet the requirements of the invention. Specifically, the specialized formulation of this ASA works in concert with the proprietary PVC compound that can be extruded and bonded or coextruded. This ASA has special characteristics that include tensile strength, elongation at break, modulus of elasticity in tension, impact strength, vicat softening temperature and density and is an impact modified, weatherable, copolymer with high thermal stability, good chemical resistance, and resistance to weathering, aging, and yellowing.
This ASA has high resistance to weathering because the elastomer component consists of an acrylate having a significantly higher resistance to UV radiation and attack by atmospheric oxygen than the butadiene rubber which is used, for example, in impact-modified polystyrene and ABS.
DESCRIPTION OF A PREFERRED EMBODIMENT
The panel comprises a sheet member having a top layer and a bottom layer. The top layer is made of ASA (Acrylonitrile/Styrene/Acrylate polymer) and the bottom layer is made of formulated PVC (Polyvinylchloride). The two layers are extruded and bonded or preferably coextruded.
The sheet member has a top surface exposed to the elements and a bottom surface that faces the surface of the roof when the panel is placed on the roof.
The bottom layer is made of a proprietary formula of PVC. The present invention uses a specialized ASA with the present invention's proprietary formulation of PVC that is needed to meet roofing material performance such as impact and fire resistance.
This ASA has a needed specialized compound that works in concert with the proprietary PVC compound that can be extruded and bonded or coextruded. The ASA is an impact modified weatherable, copolymer with resistance to weathering, aging, and yellowing, such as Luran® S 776 or 797 S/SE UV from BASF Corporation at 3000 Continental Drive-North, Mount Olive, N.J. 07828.
This ASA has special characteristics that include typical tensile strength of 40 MPa, typical elongation at break of 25%, typical modulus of elasticity in tension of 2,000 MPa, typical Izod notched impact strength of 60 kJ/m
2
, typical Vicat softening temperature of 92° F. and typical density of 1.07 g/cm
3
.
Further, the ASA used in this invention as described herein has specific additives that other ASA materials may not have. These additives are for resistance to UV, weathering, heat aging, high mechanical strength, impact resistance and corrosion resistance.
PVC has thousands of formulations with the common characteristic being the PVC resin base. Depending upon application, many other chemicals are added to the PVC resin base. Thus, resin is referred herein as a raw, unfinished material. In the present invention resin creates the base ingredient and other unique ingredients are added to form a novel compound. These other ingredients, generally called additives, assist in the molding of the invention, and add important properties to the finished product. These additives include impact modifiers, lubricants, heat stabilizers, pigments, flame retardant, plasticizers, and processing aids. The present invention uses a proprietary formulation of PVC that is needed to meet roofing material performance such as impact and fire resistance. The PVC is specially formulated with flame retardant to provide a substantially flame retardant and flame extinguishing material for the top layer of flammable ASA.
This present invention has created a unique polymer chain to create a PVC with certain desirable properties to bond with the ASA and have resistance to heat, toughness, and flexibility.
The present invention uses epoxidized soybean oil, plasticizers and heat stabilizers to prevent degradation caused by the heat of processing. Pigments are added to the present invention so that the finished product will be colored throughout. Flame retardant is added to provide a substantially flame retardant product. Flame extinguishing material is added to the PVC resin base specifically for the top layer of the flammable ASA. Processing aids and lubricants are used to assist in production and to improve the flow of resin in processing.
The unique and specific formula of PVC is compounded to interact with the specialized ASA to bond and be flame retardant. Most important is the ability of the pr
Italiane Frank Lane
Sciarra, III Joseph
Belasco Jacobs & Townsley LLP
Tarazano D. Lawrence
Townsley Norton R.
LandOfFree
Composition of a weatherproof roofing material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Composition of a weatherproof roofing material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composition of a weatherproof roofing material will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3074799