Composition for inhibition of metal corrosion

Compositions – Water-softening or purifying or scale-inhibiting agents – Plant or organic material containing

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C252S391000, C252S392000, C507S090000, C507S117000, C507S118000

Reexamination Certificate

active

06620338

ABSTRACT:

TECHNICAL FIELD
This invention relates to a composition for inhibiting the corrosion of metals in carbon dioxide containing aqueous systems. More particularly, this invention relates to the use of compositions containing amino thiol or amino disulfide compounds and acidic amino acid polymers as corrosion inhibitors in carbon dioxide containing aqueous systems.
BACKGROUND OF THE INVENTION
Oil bearing geologic formations generally contain mixtures of crude oil and mineral laden waters, hereinafter referred to as formation waters. Oil wells produce a mixture of crude oil and formation water. As wells age, the natural pressures within the formation decrease, thus leading to decreased production of oil. Wells can be artificially pressurized to force the oil and formation water out of the well, however. In offshore oil platforms, sea water is pumped into the wells to displace the oil from the formation. The mixture of sea water and formation water that results from this process is referred to as “produced water.” In many cases, the oil bearing formations have very low levels of dissolved oxygen (anaerobic). Often, the formation waters are saturated with dissolved carbon dioxide (known as sweet wells) with or without dissolved hydrogen sulfide (sour wells), which both result in an acidic pH environment, wherein the pH can range from about 3 to about 6. The acidic, highly mineral laden waters produces an environment that is highly corrosive to metals, particularly to mild steel, which is the most common material of construction for well pipe lines and equipment, due to cost considerations.
Carbon dioxide induced corrosion differs from oxygen induced corrosion in that iron carbonates and other iron salts are the main corrosion products, as opposed to iron oxide formation (rust) in aerobic systems. Mineral scale formation, caused by temperature and pressure changes in the mineral laden formation and especially in produced waters can either stimulate or inhibit corrosion, depending on the type and physical form of the scale and the pH, temperature and other factors. The expense of cleaning and replacing miles of corrosion and scale damaged pipelines and other equipment on remote oil platforms, and the loss in revenues from diminished oil production can be enormous.
Chemical additives, known as inhibitors, are commonly added to prevent the formation of scale and to inhibit the corrosion process. The control of scale and corrosion in offshore oil production has traditionally required complex mixtures of corrosion and scale inhibiting compounds. Many types of corrosion inhibitors are also physically incompatible with scale inhibitors, however. This results in the need to apply these chemicals as separate treatments.
Many classes of chemicals, of widely varying structures, have been used for the inhibition of metal corrosion. See, for example, reviews on inorganic and organic corrosion inhibitors by Nathan, “Corrosion Inhibitors”
Kirk
-
Othmer Encyclopedia of Chemical Technology,
2
nd
Edition, Volume 6, John Wiley & Sons, New York pp. 317-346 (1965) and by Trabelli et al. “Mechanism and Phenomenology of Organic Inhibitors”
Advances in Corrosion Science and Technology,
Volume 1, Plenum Press, New York, pp.147-228 (1970). Many classes of corrosion inhibitors useful in oilfield applications are highly toxic and in some cases non-biodegradable. Many corrosion inhibitors interfere with the oil-water separation process, which interference results in relatively larger amounts of crude oil contaminants in the produced water that is discharged into the ocean after separation.
There is a growing concern regarding the environmental impact of scale and corrosion inhibitors, as well as the oil contaminants that are currently being released into sensitive marine ecosystems such as the North Sea through their use in the oil production industry.
Polyaspartates are biodegradable, low toxicity materials with known corrosion inhibiting activity. U.S. Pat. No. 5,607,623 to Benton et al. describes the use of polyaspartates to inhibit ferrous metal corrosion in carbon dioxide containing aqueous systems. Polyaspartates are useful corrosion inhibitors, affording 70 to 85% corrosion inhibition in carbon dioxide containing oilfield brines. In addition, U.S. Pat. Nos. 5,116,513 and 5,152,902 to Koskan et al. disclose the use of polyaspartates to inhibit the formation of mineral scale in aqueous systems. The combined effects of scale and corrosion inhibition in a single additive is a particularly useful feature of polyaspartates.
Amide derivatives of long chain amines have been proposed as environmentally acceptable corrosion inhibitors in oil production applications. See for example Darling et al., “Green Chemistry Applied to Corrosion and Scale Inhibitors”
CORROSION
98, Paper No. 207, National Association of Corrosion Engineers (1998). Unfortunately, such materials can be difficult to formulate and can adversely affect the oil water separation process. Thioglycolic acid (mercaptoacetic acid), which is relatively low in toxicity, is known to be an inhibitor of corrosion. Thioglycolic acid has been used as a corrosion inhibitor in oilfield applications, however it is only partially effective at inhibiting corrosion in a carbon dioxide saturated environment See, for example, U.S. Pat. No. 5,853,619 to Watson et al.
There is a need, therefore, for more environmentally acceptable, biodegradable and low toxicity inhibitors of metal corrosion in carbon dioxide containing aqueous systems where hydrogen sulfide also may be present. Further, there is a need for corrosion inhibitors that are compatible with scale inhibitors and that do not interfere with the oil—water separation process. The present invention satisfies these needs.
SUMMARY OF THE INVENTION
Ferrous metal corrosion in carbon dioxide containing aqueous systems can be effectively and efficiently achieved with environmentally acceptable materials. In particular, we have found that amino thiol or amino disulfide compounds of the structure:
wherein R
1
, R
2
, R
3
, R
4
, R
5
, R
6
, R
7
and R
8
are, independently of one another, members of the group consisting of hydrogen, carboxyl, C
1
to C
18
alkyl, and C
6
to C
10
aryl;
Z is a member of the group consisting of hydrogen and covalent bond;
m and n are, independently of one another, 1, 2 or 3; and
p is zero or 1, with the proviso that p is zero when
Z is hydrogen;
in relatively low concentrations are effective inhibitors of ferrous metal corrosion in mildly acid aqueous systems containing dissolved carbon dioxide. Preferred such compounds are cysteine, cystine, cysteamine, cystamine, and salts thereof.
The environmentally acceptable corrosion inhibitors of the present invention are useful for the inhibition of ferrous metal corrosion in aqueous systems that are corrosive due to the presence of dissolved carbon dioxide found in oil producing formations. In oil production terminology, such aqueous systems are referred to as “sweet” for carbon dioxide containing formations and “sour” for systems that contain hydrogen sulfide as well. Sweet and sour conditions are both common problems leading to corrosion in oil producing assets in offshore oil production.
The amino thiol and amino disulfide inhibitor compounds suitable for practicing the methods of the present invention are low in toxicity and provide effective corrosion control at concentrations in the range of about 0.1 ppm to about 1000 ppm. Some of the preferred corrosion inhibitors utilized in the methods of the present invention are naturally-occurring materials such as the common amino acids cysteine and cystine.
In another aspect of the present invention, the aforesaid inhibitor compounds are used together with an acidic amino acid polymer such as a polyaspartate and the like. The resulting corrosion inhibiting compositions have a very low environmental impact when released into ocean waters due to biodegradability and low toxicity. In addition, the resulting combined inhibitor compositions are effective for both corrosion inhibition and scale inh

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Composition for inhibition of metal corrosion does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Composition for inhibition of metal corrosion, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composition for inhibition of metal corrosion will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3112919

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.