Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Processes of preparing a desired or intentional composition...
Reexamination Certificate
2000-03-14
2001-05-29
Acquah, Samuel A. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Processes of preparing a desired or intentional composition...
C528S272000, C528S296000, C528S298000, C528S303000, C528S308000, C528S308600
Reexamination Certificate
active
06239200
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates in general to preparation of a high molecular weight polyester. More particularly, it relates to a composition and a process for preparing a high molecular weight polyester.
2. Description of the Related Arts
High molecular weight polyesters (polyesters having high intrinsic viscosity) are required for a variety of industrial uses. Such polyesters are commonly produced from low molecular weight polyesters of the same composition, in the form of particles or pellets, by solid state polymerization. However, the manufacture is time- and energy-consuming and necessitates a marked increase in manufacturing costs.
In the solid state polymerization of a polyester prepolymer, the polymerization is carried out at an elevated temperature which is below the melting point of the polyester resin. Such polymerization is normally conducted in the presence of a stream of inert gas or under a vacuum to remove volatile reaction byproducts such as ethylene glycol. This removal of the byproduct promotes the polycondensation polymerization through both the esterification and transesterification reaction mechanisms.
There have been attempts to accelerate the solid state polymerization by reducing the size of the pellets of polyester prepolymers to favor the removal of the byproduct. However, only a trivial improvement is achieved, not to mention the requirement of additional pulverizer equipment.
As further background for increasing the reaction rate of solid state polymerization, attention is directed to U.S. Pat. Nos. 4,150,214 and 5,714,262; and World Patent Application No. 9622320.
SUMMARY OF THE INVENTION
It is therefore an object of the invention to solve the above-mentioned problems and provide a composition and a process for preparing a high molecular weight polyester which may increase the solid state polymerization reaction rate.
The present invention attains the above object by utilizing chemical modification methodology. According to a feature of the invention, a copolymer having multifunctional reactive groups is employed to promote polymerization and branching reaction so as to accelerate the polymerization and increase the intrinsic viscosity (I.V.) of the polyester. According to another feature of the invention, a particular heat stabilizer which can catalyze the solid state polymerization is employed to suppress pyrolysis and oxidization of the polyester at an elevated temperature.
According to the invention, the composition suitable for use as a starting material for preparing a high molecular weight polyester comprises:
(a) a dicarboxylic acid or diester thereof;
(b) a glycol;
(c) 0.1-5 mol %, relative to the component (a), of a multifunctional acid and/or alcohol; and
(d) 0.05-5 wt %, based on the weight of the polyester, of a hindered phenolic aromatic phosphate.
The present process for preparing a high molecular weight polyester comprises the steps of:
(1) preparing a polyester prepolymer having an intrinsic viscosity about 0.55-0.65 by melt polymerization of: (a) a dicarboxylic acid or diester thereof; (b) a glycol; (c) 0.1-5 mol %, relative to the component (a), of a multifunctional acid and/or alcohol; and (d) 0.05-5 wt %, based on the weight of the polyester, of a hindered phenolic aromatic phosphate; and
(2) solid state polymerizing the prepolymer to produce a polyester having an intrinsic viscosity of at least 0.7.
DETAILED DESCRIPTION OF THE INVENTION
In the composition according to the present invention, a dicarboxylic acid or diester thereof is used as the component (a). Especially preferred are aromatic diacids including such as terephthalic, isophthalic and naphthalaic dicarboxylic acid, or combinations thereof.
In the composition according to the present invention, a glycol is used as the component (b). Especially preferred are alkane diols of 2-10 carbon atoms including such as ethylene glycol, butylene glycol, diethylene glycol, 1,3-propanediol, dimethyl-1,3-propanediol, cyclohexanediol, 2-ethyl-2-butyl-1,3-propanediol, or combinations thereof.
In the composition according to the present invention, a copolymer having multifunctional reactive groups such as a multifunctional acid and/or alcohol is employed as the component (c). The multifunctional copolymer used herein promotes polymerization and branching reaction, thereby increasing the reaction rate and the I.V. of the polyester.
Illustrative of multifunctional acids used in the present invention include such as trimellitic anhydride (TMA) and pyromellitic dianhydride (PMDA). A particularly preferred multifunctional acid is trimellitic anhydride. Illustrative of multifunctional alcohols include such as trimethylol propane (TMP) and pentaerythritol. A particularly preferred multifunctional alcohol is trimethylol propane. The multifunctional copolymer is present in an amount of 0.1-5 mol %, and preferably 0.1-3 mol % based on the molar proportion of the dicarboxylic acid reactant, e.g., the component (a).
In the composition according to the present invention, a high molecular weight hindered phenolic aromatic phosphate is employed as the component (d). The hindered phenolic aromatic phosphate herein is used as a heat stabilizer and a polymerization catalyst as well. It serves to protect the polyester from pyrolysis and oxidization during the solid state polymerization process and also serves to catalyze the solid state polymerization. The hindered phenolic aromatic phosphate is present in an amount of 0.05-5 wt %, and preferably 0.1-2.5 wt % based on the weight of the polyester. A particularly preferred hindered phenolic aromatic phosphate is IRGANOX 1425 manufactured by Ciba Geigy.
Other conventional additives for polyester resins can be present in the composition of the invention. Such additives include stabilizers and inhibitors of oxidative, thermal, and ultraviolet light degradation; lubricants; colorants including dyes and pigments; fillers; flame retardants; nucleating agents, etc.
The general process of the present invention for preparing a high molecular weight polyester will be described below.
In the process of the invention, a polyester prepolymer having an I.V. of about 0.55-0.65 is first prepared by a conventional melt polymerization process from the components (a), (b), (c), and (d). Then the polyester prepolymer is subjected to solid state polymerization to produce a high molecular weight polyester having an I.V. of at least 0.7.
Examples of polyesters include polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyethylene naphthalate (PEN), copolymers of PET, copolymers of PBT and copolymers of PEN. A particularly preferred polyester is PET.
It is often desirable to carry out the melt polymerization in two stages, that is, esterification and polycondensation. The polyester prepolymers can be produced by direct esterification of the acid, or by ester exchange with the esters of the acids, and followed by polycondensation. For example, PET may be formed from ethylene glycol by direct esterification with terephthalic acid, or by ester exchange between ethylene glycol and dimethyl terephthalate, and followed by polycondensation.
The esterification of the dicarboxylic acid and/or the esters thereof and the glycol can be carried out at a temperature ranging from 200° C. to 250° C. The reaction, either the direct esterification or ester interchange, is normally carried out in the absence of oxygen-containing gas. The polycondensation is usually carried out at a temperature ranging from 260° C. to 300° C. and at a low pressure of about 0.1 torr. The polycondensation reaction continues until the desired intrinsic viscosity of about 0.55 to 0.65 is reached.
The prepolymer is then solidified, pelletized and transferred to a solid state polymerization reactor to complete the polycondensation reactions. Solid polymer particles are heated above the glass transition temperature (Tg) of the polymer but below the melting point temperature (Tm). This is done under vacuum or flow of inert gas, such as nitrogen, to
Chan Szu-Yuan
Chen Lee-Hua
Kao Hsin-Ching
Wong Jinn-Jong
Wu Chi-Lang
Acquah Samuel A.
Industrial Technology Research Institute
Sughrue Mion Zinn Macpeak & Seas, PLLC
LandOfFree
Composition and process for preparing high molecular weight... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Composition and process for preparing high molecular weight..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composition and process for preparing high molecular weight... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2446887