Composite zeolite membranes

Details Composite zeolite membranes Composite zeolite membranes

2000-06-15

2002-12-17

Kim, John (Department: 1723)

Liquid purification or separation

Filter

Supported, shaped or superimposed formed mediums

C210S488000, C210S489000, C210S490000, C210S500260, C210S503000, C210S504000, C210S506000, C210S510100

Reexamination Certificate

active

06494326

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates generally to membranes containing molecular sieves, and to new techniques for fabrication thereof.
BACKGROUND OF THE INVENTION
Molecular sieves are nanoporous solids which possess small (typically <10 Å) pores which are intrinsic to their molecular structure. These pores can be used to selectively control rates of diffusion of various chemicals through a molecular sieve. Selectivity can be induced and controlled through the size and shape of the pore (i.e., simple “key-in-lock” steric hindrance effects), and/or by including moieties which interact with the chemicals involved in manners which add to the selectivity of the pore. Such materials are used routinely in bulk form for separation of different gases, and for dehydration of a working atmosphere. They also have potential large-scale commercial applications in, e.g., high-temperature separation and selection of intermediate reaction products.
A particularly important subclass of molecular sieves are the zeolites. Zeolites are nanoporous inorganic alumino-silicates with pore diameters typically in the 3-7 Å range.
The crystalline nature of zeolites means that the pores are well defined in size, without variation—an intrinsic property of the crystal structure. That is, if a crystallographically oriented layer of zeolite crystals is grown, the pores thereof will share a common orientation relative to the growth surface. An orientation of particular interest is one in which the pores provide direct (if not exactly normal) paths through such a layer.
Zeolites are archetypal molecular sieves, partially because they are available with a wide range of pore diameters, and partially because they can be found naturally as a component of certain clays. Statements and claims made concerning zeolites generally apply to a broader range of molecular sieves.
However, the use of bulk zeolites is neither efficient nor effective for most chemical separation procedures. As the material is bulk, separation occurs because the difference in diffusion rates through the nanopores of the zeolite causes a large amount of one of the chemicals being separated to become temporarily trapped in the zeolite pores. This restricts one to use of batch or semi-batch separation processes, which are generally not compatible with a properly functioning continuous flow synthesis process, as is usually desirable for very large scale synthesis.
An example of the areas in which such membranes are potentially useful, if the fabrication limitations can be overcome, lies in the area of large-scale organic synthesis. A common situation is where an intermediate step in the synthetic process produces a variety of isomers, only one of which can be used as feedstock for the next step in the synthesis. This situation is often met by taking the typically high-temperature (perhaps 300-500 C.) intermediate product mixture, cooling it to liquid nitrogen temperatures, and then separating the isomers using fractional distillation, a slow and expensive technique. The desired isomer is then heated back to the processing temperature, and the synthetic process proceeds.
The cost of this separation step in energy alone is several tens of millions of dollars per year for a single plant, and the need for the additional apparatus to support the cooling, distillation, and reheating steps can represent a significant portion of the capital cost of the synthesis plant. Clearly there is a need for a substitute process with increased energy efficiency and lower capital cost. Thin film zeolite membranes could fill this role, if suitably defect-free and robust membranes could be fabricated.
One approach toward relieving the processing constraints involved with use of bulk zeolites for separation is to somehow make membranes which comprise zeolites, in which the zeolites can still function effectively as separators (i.e., active zeolites). Although it is in principle possible to create nanoporous materials from source materials which are not naturally porous (e.g., porous silicon, or acid-etched alloy sheets), present fabrication techniques therefor usually do not provide product with adequate selectivity for most practical applications.
Traditional approaches toward synthesis of thin film membranes comprising zeolites generally fall into three main classes. Self-supporting membranes can be made, essentially using sintering techniques. However, such membranes are not durable, and are difficult to adhere to a supportive substrate. Alternately, it is possible to grow single crystal zeolite films on suitable substrates. Unfortunately, such films are highly defective when made in sizes suitable for industrial applications.
The most intensively pursued approach toward fabricating thin film membranes which comprise active zeolites is to grow defective zeolite films (usually polycrystalline in structure), and attempt to fill in the defects using secondary growth of zeolites atop the original layer, or by depositing carbonaceous material in the defects. The result to date has been thick films with blocked flow channels leading to poor penetration flow rates, which have limited thermal stability and problems in adhering to suitable substrates.
Specific attempts to make satisfactory zeolite membranes deserve some description, as such point out the intractable practical problems which have appeared in past work. The publications discussed below are included in the Information Disclosure Statement for the instant application.
The zeolite most studied in the quest for robust selective membranes is ZSM5, which is an orthorhombic crystal type. The chemical formula is Na
n
[Al
n
Si
96−n
O
192
] with about 16 H
2
O of hydration, and n<27. The pores are aligned along the [010] and [100] crystallographic directions, and have sizes just over 5 Å. The equivalent material with n=0 is sometimes called silicalite.
Chiou et al. (Journal of Materials Science Letters 15, 952-954 (1996)) describe a technique to fabricate continuous zeolite films and membranes. Continuous ZSM-5 films were hydrothermally grown on anodic alumina substrates. The hydrothermal crystal growth process is commonly used in this area of endeavor. The technique used by Chiou et al. is a typical one, although the results of such growth can depend strongly on the growth parameters chosen.
Chiou et al. carry out hydrothermal growth of ZSM-5 by forming a growth solution of tetraethylorthosilicate (TEOS), sodium hydroxide, tetrapropylammonium bromide (TPABr), and de-ionized water so as to obtain the molar ratios 5Na
2
O :10TPABr:100SiO
2
:10000H
2
O. This growth solution and an anodic alumina substrate were sealed in a teflon-coated stainless-steel autoclave. Film growth was then induced by heating the autoclave to 180-200 C. for 1-4 days under autogenous pressure without stirring. The samples were then cooled, washed, and dried.
The result found by Chiou et al. was growth of a thick (about 30 microns) and nominally continuous layer of randomly oriented ZSM-5 crystallites. The lack of crystallite orientation and the extreme thickness makes such a layer inappropriate for use in chemical separation. The arrangement of crystallites makes it likely that large numbers of large pores, cracks, and other interstitial defects exist in these films—again destroying any potential for significant chemical selectivity in these materials.
C. Bai et al. (Journal of Materials Science 105, 79-87 (1995)) reported growth of chemically selective silicalite membranes on &ggr;-alumina substrates. The layers, with thicknesses of about 5 microns, were grown from a gel on the surface of a tube.
The gel used in the growth process was prepared as follows. 0.95 grams of NaOH, 2.1 grams of TPABr, and 10 grams of finely divided silica were dissolved in 125 grams of distilled water. This solution was then mixed thoroughly and allowed to age for a day before being transferred to and sealed within a &ggr;-alumina tube. The tube was placed in an autoclave, and heated to 180

Affiliated with

Also associated with

Rating

Composite zeolite membranes does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Composite zeolite membranes, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composite zeolite membranes will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2944227