Composite multilayer material for plain bearings

Details Composite multilayer material for plain bearings Composite multilayer material for plain bearings

2000-12-26

2002-12-10

Zimmerman, John J. (Department: 1775)

Stock material or miscellaneous articles

All metal or with adjacent metals

Composite; i.e., plural, adjacent, spatially distinct metal...

C428S675000, C384S912000

Reexamination Certificate

active

06492039

ABSTRACT:

DESCRIPTION
1. Technical Field
The invention relates to a composite multilayer material for plain bearings, comprising a backing layer, a bearing metal layer, a first intermediate layer of nickel and a second intermediate layer of tin and nickel together with an overlay consisting of copper and tin.
2. Related Art
Composite multilayer materials with the structure comprising steel backing/lead-bronze/overlay of lead, tin and copper have proven very reliable and to have a high mechanical load carrying capacity. Such composite multilayer materials are described in
Glyco
-
Ingenieurberichte
1/91, for example.
The electrodeposited overlay in particular is a multifunctional material, which, inter alia, takes on the following tasks:
embeddability with respect to foreign particles
running-in or conformability of sliding counterparts
corrosion protection for the lead-bronze
emergency running properties in the case of an oil shortage.
The bearing metal also contains certain emergency running reserves in case the overlay is completely worn away. However, these bearing designs, which have proven effective for decades, today still contain quantities of lead, principally in the overlay. A common alloy consists, for example, of PbSn10Cu2, a nickel intermediate layer being provided as a diffusion barrier between the bearing metal and the overlay.
These known layers exhibit low hardnesses of around 12-15 HV, and therefore exhibit good embeddability and are insensitive to scuffing. However, for the same reason they have only limited load carrying capacities and are often no longer suitable for the loads imposed by new engine developments, particularly in the field of diesel engines. The layers are also unsatisfactory because of the environmental significance of the heavy metal lead.
Hard layers are also being used in ever increasing numbers in heavily loaded bearing systems, such as for example aluminum-tin layers with hardnesses of around 80 HV deposited by PVD methods. These methods make such layers substantially more costly, however. The bearings are highly wear resistant, but are scarcely embeddable and are therefore generally combined with counter-shells in the form of soft, lead-containing layers.
Pure tin is not suitable as an overlay, since, with a hardness of around 10 HV, it is even softer than the conventional lead alloys and thus is incapable of absorbing the loads which arise in main and connecting rod bearings. Alloys containing copper have therefore already been proposed, to make tin layers more resistant by increasing hardness.
DE 197 28 777 A1 relates to the production of a lead-free bearing with an overlay of SnCu, the copper content varying from 3-20 wt. %. With the aid of a methylsulfonic acid electrolyte with grain-growth inhibiting additives, a layer is produced which has at least the properties of conventional standard lead-based ternary layers. In order to produce a further improvement in wear resistance, it is intended that hard material particles dispersed in the bath be incorporated into the layer.
DE 197 54 221 A1 proposes to deposit cobalt in addition to tin and copper, in order to achieve a further increase in mechanical load carrying capacity and to prevent embrittlement of the coupling layer between overlay and nickel diffusion barrier layer, since the cobalt reduces the tendency of the tin to diffuse into the nickel. However, this addition of cobalt to the alloy complicates the deposition process, which may reduce process reliability.
It is therefore the object of this invention to provide a composite multilayer material with a tin-copper-based overlay, which material simultaneously
exhibits a higher specific load carrying capacity and lower wear than conventional lead-based layers
is conformable and allows the embedding of dirt particles
does not require co-deposition of further components or dispersoids
and is more economic to produce than the materials produced by PVD methods.
SUMMARY OF THE INVENTION
This object is achieved with a composite multilayer material, the overlay of which comprises a tin matrix into which tin-copper particles are incorporated, which consist of 39 to 55 wt. % copper, the rest being tin.
Studies have shown that, with this layer structure, the bearing stabilizes itself after running-in on the initially still soft layer through heating during operation and forms a surface with good fatigue strength.
The particles are intermetallic phases, which have previously been deemed disadvantageous in overlays and consequently avoided. It has been shown, however, that these tin-copper particles markedly reduce wear on account of their hardness, wherein it has surprisingly emerged that, at temperatures from approximately 120° C., increased tin diffusion occurs into the tin-nickel layer underneath. Through migration of the tin out of the overlay, the tin-copper particles become increasingly concentrated. The thus changing overlay exhibits a high load carrying capacity and high wear resistance.
It has emerged that, at high temperatures and after very long operating periods, for example after 1000 hours, the tin content is so markedly reduced that the tin-copper particle fraction predominates in the overlay.
The content of particles per unit area, relative to any cross-sectional area, is preferably 5 to 48%. This content increases over a lengthening service life as a result of tin migration and may amount to up to 95% after a service life of more than 1000 hrs. If the particle content is below 5%, the properties of the overlay are determined solely by the tin, which does not perform adequately alone. Above 48%, the formation of relatively large conglomerates of particles can no longer be avoided, and these finally take over the role of the matrix, which then no longer exhibits sufficient embeddability and conformability in the running-in phase owing to the high level of hardness.
The diameter of the particles preferably amounts to 0.5 to 3 &mgr;m. Particles which are too large, having an average diameter of over 3 &mgr;m, result in non-homogeneous layer properties, which influence the properties of a plain bearing made from the multilayer material, particularly in the running-in phase. Particles which are too fine, having an average diameter of below 0.5 &mgr;m, increase the initial hardness too markedly, hinder the supply of tin to the tin-nickel layer and thus further stabilization of the bearing and exhibit reduced corrosion resistance with regard to hot engine oil.
It has additionally emerged that the second intermediate layer should be so adjusted, with regard to both layer thickness and tin content, that it is able to absorb tin migrating from the overlay. The migration rate of the tin and thus the modification of the wear resistance and load carrying capacity of the overlay as a function of time may be adjusted by means of the thickness and tin content of the second intermediate layer.
It is preferable for 30 to 40 vol. % of the second intermediate layer to be nickel and the rest to be tin, which corresponds approximately to an atomic ratio of 1:1. The thicker is the tin-nickel layer, the more tin may be absorbed from the overlay. The wear resistance of the overlay increases relatively rapidly in this instance.
A ratio of from 2 to 4 has emerged as the preferred ratio of the overlay thickness to the thickness of the second intermediate layer.
The layer thickness of the overlay is preferably from 5 to 25 &mgr;m. The overlay may be applied by electrodeposition.
The layer thickness of the second intermediate layer is preferably between 2 and 7 &mgr;m.
The layer thickness of the first intermediate layer of pure nickel is preferably from 1 to 4 &mgr;m. The nickel layer also contributes to the equilibrium-determined growth of the tin-nickel layer, in that the latter is not only fed with tin from the overlay thereabove, but also with nickel from the first intermediate layer. In this way, the 1:1 ratio of tin to nickel in the tin-nickel layer is maintained. The bearing metal may be selected at will. It has emerged that the bearing metal layer does

Affiliated with

Also associated with

Rating

Composite multilayer material for plain bearings does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Composite multilayer material for plain bearings, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composite multilayer material for plain bearings will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2981261