ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a new composite material and more particularly to a pressure-sintered material comprising hexagonal boron nitride and a second material comprising at least one metal nitride. In a further aspect, this invention relates to a composite material, which is particularly useful for the manufacture of refractory pieces, which are submitted to severe corrosion and temperature conditions such as refractory pieces for the metallurgic industry, in particular for the steel industry. In particular, this material is especially suitable for the manufacture of side dam plates for strip casting process.
BACKGROUND OF THE INVENTION
In this type of continuous casting, called “strip casting” or “twin-roll casting” for the casting of steel strip of approximately from 2 to 10 mm in thickness, the lateral containment of the liquid metal in the casting space defined by the rolls is provided by plates which are applied against the plane extremities of the rolls, called “ends”, by a suitable device. These plates are usually termed “sidewall” or “side dam” plates. Their central part intended to be in contact with the liquid metal is made of refractory material, as is, in general, their periphery which rubs frictionally against the rolls, progressively wearing out the side dam plates. It is absolutely essential that these side dam plates be in contact with the rolls in as sealed a manner as possible, since infiltrations of liquid metal into their contact area would have disastrous effects on the dimensional quality of the cast strip. Parts of the strip would then run the risk of separating from the rest of the strip and remain stuck to the rolls. If this sticking were to persist during one complete revolution of the rolls and if the fragments of edges were thus to penetrate into the casting space, this could give rise to serious damage to the surfaces of the rolls and, by way of consequences, to the strip itself. At worst, these infiltrations of metal could reach as far as the outside of the machine, which would dictate stopping the casting immediately.
Such problems may have many causes, among them being the following:
distortions of the rolls and of the side dam plates, due to mechanical and thermal stresses which they are exposed to, in particular at the very start of casting when a thermal regime is imposed on them;
progressive (mechanical and chemical) wear of the side dam plates or of the rolls, which is not always uniform over all their contact areas; and
instantaneous wear of the side dam plates caused by the passage of an infiltration of solidified metal.
Thus a need exists for a material that would combine resistance to mechanical and thermal stresses and have excellent resistance against chemical or mechanical wear.
A pressure-sintered polycrystalline mixed material is already known from U.S. Pat. No. 4,885,264. This document discloses materials with a base of boron nitride, oxides and carbides in which the hexagonal boron nitride fraction is from about 30 to about 85% by weight. The oxide fraction is selected from the group comprising zirconium oxide and magnesium oxide and is from about 10 to about 50% by weight. The carbide fraction is selected from the group comprising silicon carbide, titanium carbide and zirconium carbide and is from about 5 to about 20% by weight. This material has a density higher than 94% of the theoretically possible density (based on the boron nitride/oxide/carbide mixture). According to U.S. Pat. No. 4,885,264, this material is resistant to liquid metals, wear resistant and thermal shock resistant and therefore, suitable for use as detachment or break rings in the horizontal continuous casting of steel and non-ferrous metals.
However, it has been observed that, mainly due to a high thermal expansion coefficient, this material does not exhibit sufficient thermal shock resistance. The chemical resistance to liquid metal also needs to be improved.
Another material is known from U.S. Pat. No. 5,389,587 which discloses an ordinary pressure sintered ceramic material comprising at least 50% by weight of hexagonal boron nitride and from 1 to 50% by weight of two or more components selected from aluminium and silicon nitride and oxide. The mechanical resistance of this material is still far from the requirements of the steel industry, for example for the manufacture of side dam plates.
Thus, a need still exists for a material that would combine resistance to mechanical and thermal stresses and have excellent resistance against chemical or mechanical wear and especially, which would have an excellent chemical resistance to liquid metal.
SUMMARY OF THE INVENTION
According to the invention, one or more of these needs are achieved with a composite pressure-sintered material comprising a continuous phase of hexagonal boron nitride and, dispersed therein, a second material comprising:
(a) at least one metal nitride selected from the group consisting of silicon, aluminium or titanium nitride, and
(b) at least one stable metal oxide; the amount of metal oxide being such that the second material does not contain more than 35% by weight of oxygen.
It has been observed that this material possesses a relatively low thermal expansion coefficient and therefore exhibits good thermal shock resistance. Another characteristic of this material is its low wettability by molten steel which is thus responsible for improved resistance to liquid metal and reduces the occurrence of steel solidification thereon. Finally, it has been observed that this material exhibits exceptional mechanical wear resistance.
DETAILED DESCRIPTION OF THE INVENTION
The crystalline structure of hexagonal boron nitride is essentially constituted of planes which are supposed to play a role in the prevention of cracks propagation. Therefore, the composite material must contain a continuous phase of hexagonal boron nitride. It has been determined that an amount of at least 45% by weight of hexagonal boron nitride, and more preferably of at least 55% by weight of hexagonal boron nitride, allows to obtain a continuous phase of boron nitride.
On the other hand, material from hexagonal boron nitride alone is too soft and has unduly low mechanical strength with the result that the material has a high tendency to chipping and wearing. Therefore, the composite material should contain less than 80% by weight of hexagonal boron nitride and more preferably less than 70% by weight.
Therefore, the invention also relates to composite pressure-sintered material comprising from 45 to 80% by weight of hexagonal boron nitride and from 55 to 20% by weight of a second material comprising:
(a) at least one metal nitride selected from the group consisting of silicon, aluminium and titanium nitride, and
(b) at least one stable metal oxide in an amount such that the second material does not contain more than to 35% by weight of oxygen.
The best results have been obtained with materials comprising 57.5% by weight of hexagonal boron nitride.
According to the invention, the composite material comprises at least one metal nitride selected from the group consisting of silicon, aluminium and titanium nitrides. Advantageously, silicon nitride is used.
According to a preferred embodiment of the invention, the second material may contain at least one stable metal oxide in an amount such that the second material does not contain more than 35% by weight of oxygen.
Preferably, the second material contains at least 2.5% by weight of oxygen.
It is necessary that the selected stable metal oxides, if any, are able to form a solid solution into said metal nitride. This is generally the case when the atomic number of the heavier metal atom of said stable metal oxides is not higher than the atomic number of the heavier metal atom of said metal nitride.
Suitable stable metal oxides comprise, but are not limited to, oxides of aluminium, titanium, silicon and magnesium or mixtures thereof. Among these, aluminium oxide is preferred.
In a particular embodiment of the invention, use is made of Sialon as a second ma
Guillo Philippe
Hoggard Dale B.
Group Karl
Klemz, Jr. Robert S.
Vesuvius Crucible Company
Williams James R.
LandOfFree
Composite material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Composite material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Composite material will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3156610