Radiation imagery chemistry: process – composition – or product th – Radiation modifying product or process of making – Screen other than for cathode-ray tube
Reexamination Certificate
1999-04-09
2001-10-30
McPherson, John A. (Department: 1756)
Radiation imagery chemistry: process, composition, or product th
Radiation modifying product or process of making
Screen other than for cathode-ray tube
C205S091000, C205S092000, C205S124000, C205S157000
Reexamination Certificate
active
06309782
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a color filter used for color sensors and for various display elements such as a CCD camera and liquid crystal display elements and to a formation technology of the color filter, as well as to a method for manufacturing of a color layer and a black matrix. In particular, the present invention relates to a novel method for manufacturing a color filter in which a color layer and a black matrix with high resolution can be simply formed without using a photolithographic process, to an apparatus used in this method and to a highly smoothed color filter having a transparent semiconductor film therein.
2. Description of the Related Art
Presently known methods for the manufacturing of a color filter include (1) a dyeing method, (2) a pigment dispersion method, (3) a printing method, (4) an ink jet method and (5) an electrodeposition method.
(1) The dyeing method involves forming an aqueous polymer to be dyed on a glass substrate, forming a desired pattern on the substrate through photolithographic steps and in succession dipping the substrate in a dye solution to obtain a colored pattern. These processes are repeated three times to obtain R. G. and B. (Red, Green and Blue) color filter layers. The resulting color filter has high transmittance and a great variety of hues and reaches a high technological level of perfection. Therefore, recently, this method has been used very often in making color solid charge coupled devices (CCD). However, the resulting color filter has deteriorated light resistance because a dye is used and this method involves many manufacturing steps. Hence, recently, the pigment dispersion method has been used instead of the dyeing method especially for making liquid crystal display elements (LCD).
(2) The pigment dispersion method has recently been the dominant method for manufacturing color filters. First, a resin layer is formed in which a pigment is dispersed on a glass substrate. A pattern is formed on the substrate thorough photolithographic steps. This procedure is repeated three times to obtain R. G. and B. color filter layers. This manufacturing method, while attaining a high level of technological perfection, requires many manufacturing steps and hence entails high cost.
(3) The printing method involves dispersing a pigment in a heat-curable resin and repeating printing three times to paint separately with R. G. and B., followed by heating to cure the resin, thereby preparing color filter layers. This method, while requiring no photolithographic steps, gives rise to a problem in terms of resolution and uniform film thickness.
(4) The ink jet method involves forming an ink acceptable layer of an aqueous polymer on a substrate and performing hydrophilic and hydrophobic treatments of the ink acceptable layer, followed by spraying ink using an ink jet method on a portion which has been made hydrophilic, painting separately with R. G. and B., thereby preparing color filter layers. This method also requires no photolithographic steps in the formation of R. G. and B. layers. However, it imparts inferior resolution. It is also inferior in positional accuracy because small droplets of ink scatter when spraying on an adjacent filter layer, with a high probability of color mixture.
(5) The electrodeposition method involves applying a voltage about as high as 70 V onto. a transparent electrode that has been patterned in advance, in an electrolyte wherein a pigment is dispersed in an aqueous polymer, to form an electrodeposition film and thereby perform electrodeposition coating. These processes are repeated three times to obtain R. G. and B. color filter layers. This method, however, requires forming a pattern in advance on a transparent electrode by means of photolithography, and using this transparent electrode as the electrode for electrodeposition. The shape of the pattern on the electrode is limited. Therefore, this method cannot be used for a TFT liquid crystal.
The present inventors have studied such an electrodeposition technology itself based on its principle and as a result, have perceived that there are, among aqueous color molecules, those which exhibit greatly different solubilities in water under different conditions, namely, oxidation conditions, neutral conditions and reduction conditions.
Examples of compounds having such properties are as follows. At a pH of 4 or more, Rose Bengale and eosin, which are fluorescein type dyes, are in a reduction condition so are soluble in water, but, below pH 4, these compounds are in a neutral condition so these compounds precipitate/sediment. It is also known that dye materials having a carboxyl group greatly vary in solubility according to the hydrogen ion concentration (pH), even without any structural changes. Specifically, ink jet dyes that are improved in water resistance are soluble in water at a pH of 6 or more, but precipitate below this pH. When these dyes are dissolved in pure water and an electrode is dipped in the solution to apply voltage, electrodeposition films consisting of these dye molecules are formed on the anode. An aqueous acrylic resin, which has a carboxyl group and is a type of polymer, is also soluble in water at a pH 6 or more, but precipitates below that pH. When an electrode is dipped in a solution, in which a pigment is dispersedin this polymer, to apply voltage, the pigment and the polymer precipitate on the anode to form an electrodeposition film wherein the pigment is mixed with the polymer. These electrodeposition films can be resulted in aqueous solutions by applying reverse voltage or by dipping these films in aqueous solutions whose pH is between 10 and 12. An oxazine type basic dye Cathilon Pure Blue 5GH (C.I. Basic Blue 3), which is a quinoneimine dye, and a thiazine type basic dye Methylene Blue (C.I. Basic Blue 9) are oxidized to develop a color at a pH of 10 or less, but a above this pH, are reduced, becoming insoluble and thereby precipitatig. When these dyes are dissolved in pure water and electrodes are dipped in the solution to apply voltage, electrodeposition films consisting of these dye molecules are formed on the cathodes. These dye electrodeposition films are restored to their original states and resulted by applying reverse voltage or by dipping these films in aqueous solutions whose pH is 8 or less.
In conventional electrodeposition technologies, the voltage required for forming an electrodeposition film is about as high as 70 V. Applying such a high voltage causes a Schottky barrier between a semiconductor and an electrolyte to be broken, with the result that no image can be formed. In addition, there have not been any semiconductors that can be used for forming transparent and practical color filters. In view of this situation, the patterning of a transparent electrode is required in the aforementioned conventional method for the manufacturing of a color filter that makes use of electrodeposition coating. This causes the pattern of color filters to be limited in shape.
There are methods proposed in which a dye is used for doping or dedoping of electroconductive polymers to form an image using light. In this case, it is possible to form an electroconductive film using only a dye without using an electroconductive polymer. However, the voltage required for forming an electrodeposition film using only a dye is larger than that in the case of using an electroconductive polymer as well. Meanwhile, the photovoltaic force is in order of about 0.6 V even in common Si. The photovoltaic force alone is insufficient to form an image. Accordingly, it is possible to consider applying bias voltage to raise the power. However, the Schottky barrier between a semiconductor and a solution, which is necessary for the creation of the photovoltaic force, is broken above a fixed voltage (the voltage is dependent on the bandgap of the semiconductor used). This limits applicable bias voltage. Therefore, the formation of an image in an aqueous solution using photovoltaic force is limited to using a
Akutsu Eiichi
Ohtsu Shigemi
Pu Lyong Sun
Tsuchiya Motohiko
Fuji 'Xerox Co., Ltd.
McPherson John A.
Oliff & Berridg,e PLC
LandOfFree
Color filter and method for manufacturing the same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Color filter and method for manufacturing the same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Color filter and method for manufacturing the same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2559512