ABSTRACT:
A composition consisting essentially of 60.0-70.0 mol % TiO.sub.2, 14.3-20.0 mol % Nd.sub.2 O.sub.3, 11.0-16.7 mol % BaO, 1.0-8.0 mol % ZrO.sub.2 and 0.05-0.30 mol % CeO.sub.2. This composition is useful for forming densified ceramic dielectric bodies having a dielectric constant of at least 65 and which meet COG specifications, and multilayer capacitors that contain such dielectric bodies.
REFERENCES:
patent: 4500942 (1985-02-01), Wilson
patent: 4522927 (1985-06-01), Koshima
patent: 4535064 (1985-08-01), Yoneda
patent: 4713726 (1987-12-01), Sasazawa
patent: 4753906 (1988-06-01), Nishigaki et al.
patent: 4757037 (1988-07-01), Columbet et al.
patent: 4855266 (1989-08-01), Burn
patent: 4866017 (1989-09-01), Okawa
Bruno Salvatore A.
Burn Ian
Dixon Jr. William R.
E. I. Du Pont de Nemours and Company
Schull Leo M.
LandOfFree
COG dielectric with high K does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with COG dielectric with high K, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and COG dielectric with high K will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-419524