Cobalt metal agglomerates, a method of producing them and their

Specialized metallurgical processes – compositions for use therei – Compositions – Loose particulate mixture containing metal particles

Patent

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

75369, 75765, 75374, 75430, 419 13, 419 14, 419 18, 419 19, B22F 900

Patent

active

060154470

DESCRIPTION:

BRIEF SUMMARY
FIELD AND BACKGROUND OF THE INVENTION

The present invention relates to cobalt metal agglomerates consisting of peanut-shaped primary particles, to a process for the production thereof and to the use thereof.
Finely divided cobalt metal is mainly used as a binder in the production of hard metal and cutting tools based on various hard materials, such as for example WC, diamond, SiC and CBN. The cobalt metals used, for example, in the production of diamond tools must fulfil specific requirements. These include, in the first instance, that impurities such as Al, Ca, Mg, S and Si should be avoided as these elements readily form stabile oxides with the residual oxygen of the cobalt metal powder, so causing unwanted porosity in the segments.
It is also necessary, especially when producing segments with synthetic diamonds, to use only cobalt metal powders with very active sintering properties, as minimum densities of 8.5 g/cm.sup.3 are required in this case. These densities should be achieved at a sintering temperature range of as low as <900.degree. C. because the diamond may be converted into graphite at higher temperatures. If the sintering activity of the cobalt metal is inadequate, sufficient hardness is not achieved. Under the extreme stresses to which annular drilling bits or cutting tools are exposed, the abrasive action of stone dust leads to deep erosion and unwanted detachment of the diamonds or other hard materials and consequently a loss of cutting performance.
According to the prior art, cobalt metals are used, on the one hand, in the form of mixtures of atomised cobalt metal powders with hydrogen-reduced powders, as are disclosed in DE-A 4 343 594, on the other hand as ultra-fine and extra-fine grade cobalt metal powders.
Ultra-fine powders are differentiated by their FSSS value of <1.0 .mu.m from extra-fine powders which have FSSS values of between 1.2 and 1.4 .mu.m.
The small particle size and the resultant large surface areas of the described cobalt metal powders promote the absorption of atmospheric oxygen and moisture, which frequently leads to degradation of the flowability of the powders.
The object of the present invention was thus to provide a sintering active cobalt metal which does not exhibit the stated disadvantages, but does allow the production of segments with elevated density and hardness.
It has now proved possible to provide a cobalt metal powder which exhibits these required properties.


SUMMARY OF THE INVENTION

These are cobalt metal agglomerates consisting of peanut-shaped primary particles, characterised in that the primary particles have average particle sizes in the range from 0.1 to 0.7 .mu.m. These cobalt agglomerates are the subject matter of this invention. They preferably have a spherical secondary structure with average agglomerate diameters of 3 to 50 .mu.m, preferably of 5 to 20 .mu.m. By virtue of their spherical secondary structure they are distinguished by good flow properties.


BRIEF DESCRIPTION OF THE DRAWING

FIGS. 1, 2 show y-axis hardness and density values, respectively, vs. x-axis (sinter) temperatures of cobalt articles of the known extrafine and ultra-fine types and made according to the present invention; and
FIGS. 3, 4 (upper and lower parts of each) are scanning electron micrographs for articles produced per the present invention as described below.


DETAILED DESCRIPTION OF THE INVENTION

The irregularly elongated primary particles preferably have an average particle length of 0.5 to 1 .mu.m and, generally, a diameter of <0.5 .mu.m.
FIG. 3 shows 5000 and 15000 times magnification scanning electron micrographs of the cobalt metal powder agglomerates of the invention produced according to example 3.
The specific surface areas of the cobalt metal agglomerates according to the invention (determined using the nitrogen single point method to DIN 66 131) are preferably 2 to 6 m.sup.2 /g. These surface areas and the small particle sizes of the primary particles are responsible for the elevated sintering activity of the cobalt metal agglomerates a

REFERENCES:
patent: 4093450 (1978-06-01), Doyle et al.
patent: 4469505 (1984-09-01), Cheresnowsky et al.
patent: 4588572 (1986-05-01), Vincler et al.
patent: 4798623 (1989-01-01), Cheresnowsky
patent: 5594929 (1997-01-01), Muhammed et al.
International Preliminary Examination Report Translation received in corresponding International Application PCT/EP 96/02049 filed May 14, 1996.
PCT Search Report received in corresponding International Application PCT/EP 96/02049 filed May 14, 1996 and previously filed with the present application.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Cobalt metal agglomerates, a method of producing them and their does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Cobalt metal agglomerates, a method of producing them and their , we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Cobalt metal agglomerates, a method of producing them and their will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-560361

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.