ABSTRACT:
BACKGROUND AND SUMMARY OF THE INVENTION
This application claims the priority of German Patent Application No. 197 33 204.8, filed Aug. 1, 1997, the disclosure of which is expressly incorporated by reference herein.
The present invention relates to a coating composed of a hypereutectic aluminum/silicon alloy and/or an aluminum/silicon composite material for manufacturing wear-resistant, low-friction layers as well as a method for manufacturing the coating, both of which are used in industry.
In automobile construction, at the present time, most of the gray cast iron crankcases of reciprocating engines that are dominant today (their share in 1994 in Germany was still a dominant 96% and 8 2% Europe-wide) are gradually being displaced by those made of lightweight metals in order to reduce the total weight of the vehicle and hence to improve fuel consumption. Diecasting of low-alloyed aluminum such as AlSi10 for manufacturing crankcases from lightweight metal will initially qualify for economic and technical reasons. However, such alloys, in contrast to the atmospheric casting of hypereutectic aluminum-silicon alloys such as ALUSIL™ (AlSi17) that have become established in engine-building but are much more expensive, exhibit unsatisfactory behavior regarding abrasion and wear when in contact with aluminum pistons and piston rings, and are therefore unsuitable as friction partners.
Therefore, the casting of tribologically suitable liners made of gray cast iron or hypereutectic aluminum-silicon cannot be eliminated in making future engines. To manufacture these liners in accordance with DE 43 28 619 C2 or DE 44 38 550 A1 for example, blanks are manufactured by the known Ospray method and then compacted mechanically. The semi-finished liner is placed in the mold before casting and then has molten aluminum cast around it. The typical wall thickness of such liners is 2 to 3 mm. Then the interior of the liner is coarse- and fine-turned, honed, and exposed. The alloys used contain copper so that, in particular, intermetallic phases such as Al
2
Cu are formed that are required for short-chipping machining of the layer surface. The use of these alloys containing copper poses particular problems in conjunction with certain fuels.
The spray-compacted blocks according to DE 43 28 619 C2 and EP 0 411 577 B1 are manufactured with copper-free aluminum/silicon alloys, but have not been used heretofore as cylinder liners because the surface of the cylinder liners cannot be machined by short-chipping and therefore do not constitute an economically feasible alternative.
Moreover, this liner solution involves disadvantages relating to design, manufacturing technology, and economics, such as limited adhesion of the AlSi10 melt to the liner surface, costly handling, and high price. In addition, the wall thickness of the liners influences the minimum cylinder spacing. The wall width, especially in future engines with a small size, should be as small as possible because it helps determine the minimum external dimensions of the engine.
Thermal spraying offers further opportunities to apply wear-resistant coatings to cylinders in crankcases. The basic principle of thermal spraying consists in a meltable or partially meltable material being melted in a high-speed hot gas stream to form small spray droplets and then being accelerated toward the surface to be coated (DIN 32530). Upon impact, the sprayed droplets solidify when they strike the relatively cold metal surface and form layer upon layer to create a coating. The advantage of this coating technique over electrodeposition, chemical or physical gas phase deposition, and the like is the high application rate that makes it possible to coat a cylinder economically in a few minutes. The methods of thermal spraying differ in terms of the way they are performed and in the properties of the high-speed speed hot gas stream.
In high-speed flame-spraying (HVOF), an acetylene-oxygen flame is produced in which the spray particles are accelerated to supersonic speed and are deformed when they impact the surface to be coated. The HVOF method has been used with an aluminum-bronze alloy (U.S. Pat. No. 5,080,056) and an iron-aluminum composite material (EP 0 607 779 A1), but produces excessive heat which frequently can be carried away only by expensive additional cooling of the crankcase (U.S. Pat. No. 5,271,967).
In plasma spraying, gases such as argon, helium, nitrogen, and/or hydrogen are fed through an electric arc in a plasma state in which the powdered (EP 0 585 203 A1 and U.S. Pat. No. 4,661,682) or wire-form (U.S. Pat. No. 5,442,153) spraying material is added laterally in order to be deflected there, moderately accelerated by comparison with HVOF, and melted. In this case the spray particles are heated to a higher temperature than in HVOF, so that they are in a molten state when they impact the substrate, which ensures an intimate material connection of the layer to the substrate. Powder plasma spraying has already been used for coating cylinder bores with a layer on an iron base (U.S. Pat. No. 3,991,240). Wire plasma spraying has been used for coating cylinder bores with an AISI 1045 steel (DE 195 08 687). Efforts to replace cylinder linings made of gray cast iron by those made of hypereutectic aluminum/silicon, however, indicate that an iron-based cylinder liner cannot meet the technical and tribological requirements of modern reciprocating engines.
The goal of the present invention is to develop a thermally sprayed, wear-resistant layer especially for building engines in terms of wear-resistance and lubricating oil consumption, and at the same time to reduce the danger of wear for components in contact with one another.
By using special, essentially copper-free aluminum/silicon spray powders for applying the coating according to the present invention by means of atmospheric thermal spraying methods, a heterogeneous layered structure made of aluminum mixed crystals, silicon precipitates and particles, intermetallic phases such as Mg
2
Si, and extremely finely divided oxides is produced during the layered formation of the coating. The formation and distribution of the oxides are attributed exclusively to the nonequilibrium properties of the atmospheric thermal spraying method. Surprisingly, the layer surface of a coating according to the present invention can be machined economically by short-chipping despite the absence of copper, which may be due to the finely divided oxides on the surface of the coating and preferably also inside the coating. In addition, the coating exhibits improved wear resistance.
To produce aluminum/silicon layers that can be machined by short-chipping and are essentially copper-free by means of atmospheric thermal spraying, atmospheric plasma spraying is preferred because of the good melting properties of the spray particles and the formation of finely divided oxides with good adhesion to the substrate and moderate heat transfer to the part. Moreover, this method offers the possibility of producing custom coatings so that preturning can be eliminated from the surface machining of the layer.
For economic and technical reasons, a coating is advantageous that ensures good machinability of its surface, especially by short-chipping. In order for this wear-resistant coating, machinable by short-chipping, to be usable for coating crankcases, in addition to reducing combustion residues by lowering lubricating oil consumption, it is desirable to use it for all types of fuels worldwide, for which reason the coating is copper-free, especially when used for the cylinder liners of internal combustion engines.
It is also advantageous that with the wear-resistant aluminum/silicon coating according to the present invention, following a diecasting process, for example, a cylinder liner in a diecast engine block made of lightweight metal such as aluminum or magnesium, the coating may be applied by a thermal spraying method, so that the previously conventional but expensive liner solution can be eliminated. In addition, the thickness of the actual tribo
Gasthuber Herbert
Haug Tilman
Heuberger Axel
Izquierdo Patrick
Pfeffinger Harald
Daimler-Chrysler AG
Evenson, McKeown, Edwards & Lenahan P.L.L.C.
Jones Deborah
Savage Jason
LandOfFree
Coating consisting of hypereutectic aluminum/silicon alloy... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Coating consisting of hypereutectic aluminum/silicon alloy..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Coating consisting of hypereutectic aluminum/silicon alloy... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2508297