Coated body with nanocrystalline CVD coating for enhanced...

Stock material or miscellaneous articles – Web or sheet containing structurally defined element or... – Including a second component containing structurally defined...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C428S698000, C428S701000, C428S702000, C428S697000

Reexamination Certificate

active

06620498

ABSTRACT:

BACKGROUND OF THE INVENTION
Coated bodies for use in the cutting of metal are well-known. Typically, the bodies are made of a cemented carbide, cermet or ceramic and the coatings are one or more of a Group VIB metal carbide, nitride, oxide or mixtures thereof. For example, bodies of a cemented carbide coated with layers of TiC, Al
2
O
3
and TiN are widely used. There are many variations in layer composition and thickness. The layers are applied by various methods such as CVD (chemical vapor deposition), both conducted at normal temperatures of from about 900 to 1250° C. and medium temperature chemical vapor deposition (MTCVD) conducted at temperatures of from about 700 to 900° C., and PVD (physical vapor deposition).
CVD TiC coatings are usually composed of equiaxed grains with the grain size being from about 0.5 to 1.0 microns. CVD TiN as well as MTCVD Ti(C,N) coatings are composed of columnar grains with the length of the grains approaching the coating layer thickness. The morphology of CVD coatings can be slightly modified by process adjustments. The MTCVD coatings are, however, very difficult to modify by conventional process adjustments.
The hardness of polycrystalline materials in general (including coating layers as well) obey the Hall-Petch equation: H=H°+C/✓d where H is the hardness of a polycrystalline material, H° is the hardness of a single crystal, C is a material constant and d is the grain size. As may be seen from this equation, the hardness of a material can be increased by decreasing the grain size. Nonetheless, conventional CVD and MTCVD coatings have grain sizes of at least 0.5 microns and above. MTCVD coatings are particularly characterized by the presence of large columnar grains with the length of the crystals approaching the thickness of the coating layer.
The use of a dopant such as a tetravalent titanium, hafnium and/or zirconium compound in the formation of an Al
2
O
3
layer to promote the formation of a particular phase is shown in U.S. Reissue Pat. No. 31,526. Also, the use of a dopant selected from the group consisting of sulfur, selenium, tellerium, phosphorous, arsenic, antimony, bismuth and mixtures thereof to increase the growth rate of Al
2
O
3
applied by CVD as well as to promote even layers of the coating is disclosed in U.S. Pat. No. 4,619,886.
CO
2
has been used as part of the coating process as well. In particular, it has been used in oxidizing processes where it reacts with H
2
to form H
2
O, the oxidizing gas. See, for example, U.S. Pat. No. 5,827,570.
OBJECTS AND SUMMARY OF THE INVENTION
It is an object of this invention to avoid or alleviate the problems of the prior art.
It is further an object of this invention to provide a coating layer of significantly smaller grain size and concomitant hardness.
In one aspect of the invention there is provided a coated body having as a coating layer, a layer of Ti(C,N,O) having a grain size of 25 nm or less.
In another aspect of the invention there is provided a method of forming a coated body of Ti(C,N,O) comprising contacting a body with a gas containing titanium halide, a nitrogen compound, a carbon compound, a reducing agent and a dopant addition of CO and/or CO
2
sufficient to form the Ti(C,N,O) in a size less than 25 mm.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION
It has now been found that the grain size of coatings applied by MTCVD can be refined to much smaller grain size levels and to an equiaxed shape by adding small amounts of a dopant of CO or CO
2
or mixtures thereof, preferably CO, to the coating gas during the MTCVD process. In order to obtain a grain size of the resulting coating in the order of 25 nm or less, preferably 10 nm or less, the amount of CO in the MTCVD gaseous mixture should be from about 5 to 10%, preferably from about 7 to 9%, of the total gaseous mixture. When CO
2
is used, it should be present in an amount of from about 0.5 to 1.0%, preferably 0.4 to 0.6% of the total gaseous mixture. The CO and/or CO
2
dopant can be added at anytime throughout the reaction, continuously or in the interrupted mode. When CO
2
and/or CO/CO
2
mixtures are used, care should be taken within the skill of the artisan to avoid the formation of Magnelli phases.
While the dopant addition can be made to the reactant gas admixture used for various coating layers, it has found particular utility in the formation of a Ti(C,N,O) layer which would have been a Ti(C,N) layer in the absence of the dopant. In the Ti(C,N,O) layer, the ratio of constituents generally has been as follows: O/Ti from 0.10 to 0.40, preferably 0.20 to 0.30, C/Ti from about 0.40 to 0.60, preferably 0.50 to 0.60, and N/Ti from about 0.15 to 0.35, preferably 0.20 to 0.30. While a Ti (C,O,N) layer is preferred, the method of the present invention can be applied to form a Ti(C,O) layer which would have been a TiC layer in the absence of the dopant.
The nanocrystalline layer may be applied as the outermost layer or as an inner layer. As will be shown below, the nanocrystalline coatings are harder but exhibit at higher temperatures (at higher cutting speeds) grain boundary sliding leading to plastic deformation. Due to the extremely fine grain size of this coating, the surface smoothness is increased and friction coefficient is reduced. Consequently, nanocrystalline coatings obviously are acting as friction reducing/lubricating layers and should be consequently deposited atop of the existing coating structure. However, new coatings of MTCVD/CVD with alternating nanocrystalline layers (doping switched ON/OFF during MTCVD/CVD process, nanolayered structures of MTCVD
anocrystalline layers are possible) should exhibit outstanding
ew properties. The nanocrystalline layers could also be used in combination with other coating materials like alumina (kappa or alpha), or other oxides or TiN forming a nanolayered structure being composed of layers of MTCVD and nanograined coatings. Very thin nanocrystalline layers inserted in the MTCVD coatings can be used to control the grain size of the MTCVD coating when a coating composed of mainly Ti(C,N) is preferred. When used as the outermost layer, the nanocrystalline layer may be applied onto an Al
2
O
3
layer, which itself can be applied onto one or more other layers such as, for example, TiC. The Al
2
O
3
layer can be an alpha phase, a kappa phase or a mixture of alpha and kappa phase Al
2
O
3
. The nanocrystalline layer may also be applied onto a TiN layer.
Similarly, when the nanocrystalline layer is applied as an inner layer, there may be other layers such as Al
2
O
3
, TiC, Ti(C,N), TiN or the like applied atop the nanocrystalline layer.
These various other inner and/or outer layers may be applied by CVD, MTCVD or PVD.
By equiaxed, it is meant that the grains have essentially the same dimension in all directions.
The invention is additionally illustrated in connection with the following Examples which are to be considered as illustrative of the present invention. It should be understood, however, that the invention is not limited to the specific details of the Examples.


REFERENCES:
patent: RE31526 (1984-02-01), Smith et al.
patent: 4619866 (1986-10-01), Smith et al.
patent: 5503912 (1996-04-01), Setoyama et al.
patent: 5700551 (1997-12-01), Kukino et al.
patent: 5712030 (1998-01-01), Goto et al.
patent: 5827570 (1998-10-01), Russell
patent: 5915162 (1999-06-01), Uchino et al.
patent: 5972495 (1999-10-01), Ishii et al.
patent: 6221469 (2001-04-01), Ruppi
patent: 6251508 (2001-06-01), Ruppi
patent: 0 600 115 (1994-06-01), None
patent: 0 678 594 (1995-10-01), None
patent: 0 701 982 (1996-03-01), None
patent: 0 816 531 (1998-01-01), None
patent: 5-345976 (1993-12-01), None
patent: 6-279990 (1994-10-01), None
Patent Abstracts of Japan, vol. 018, No. 203 (M-1590), Apr. 11, 1994, & JP 06 008010 A (Mitsubishi Materials Corp), Jan 18, 1994.
Patent Abstracts of Japan, vol. 1996, No. 04, Apr. 30, 1996, & JP 07 328810 A (Mitsubishi Materials Corp), Dec. 19, 1995.
Patent Abstracts of Japan, vol. 1997, No. 02, Feb. 28, 1997, & JP 08 269719 A (Mi

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Coated body with nanocrystalline CVD coating for enhanced... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Coated body with nanocrystalline CVD coating for enhanced..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Coated body with nanocrystalline CVD coating for enhanced... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3098822

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.