Coating processes – Direct application of electrical – magnetic – wave – or... – Electrostatic charge – field – or force utilized
Reexamination Certificate
2000-05-08
2002-01-29
Dawson, Robert (Department: 1717)
Coating processes
Direct application of electrical, magnetic, wave, or...
Electrostatic charge, field, or force utilized
C523S410000, C523S412000, C525S327300, C525S375000, C525S386000
Reexamination Certificate
active
06342274
ABSTRACT:
The present invention relates to a transparent powder coating material which is particularly suitable as a coating for car bodies that are coated with waterborne coating material.
At present, liquid coating materials are preferably used for the coating of car bodies. These coating materials cause numerous environmental problems owing to their solvent content. This is true even when aqueous coating materials are employed.
For this reason, increased efforts have been made in recent years to use powder coating materials for the coating. The results to date, however, have been unsatisfactory; in particular, transparent powder coating materials still exhibit weaknesses in terms of chemical resistance and yellowing. Epoxy/carboxy-crosslinked transparent powder coatings exhibit a markedly poorer etch resistance relative to water, tree resin and sulphuric acid.
The object of the present invention is to provide a transparent powder coating material which relative to transparent powder coating materials known to date exhibits markedly better etch resistance and a reduced tendency towards yellowing after crosslinking. In this context, the transparent powder coating material should be able to be supplied for application in solid form.
This object is achieved by a transparent powder coating material comprising
a) at least one epoxy-containing binder with or without a content of from 20 to 45% of glycidyl-containing monomers and with or without a content of vinylaromatic compounds, preferably styrene,
b) tris(alkoxycarbonylamino)triazine and polycarboxylic acids, preferably straight-chain aliphatic dicarboxylic acids and/or carboxy-functional polyesters, as crosslinking agents, and
c) if desired, catalysts, auxiliaries, additives typical for transparent powder coating materials, such as degassing agents, levelling agents, UV absorbers, free-radical scavengers, antioxidants.
The content of glycidyl-containing monomers is preferably from 25 to 45%. Particular preference is given to from 30 to 45% by weight, in particular from 30 to 40%. From 30 to 35% are very particularly preferred. Utmost preference is given to from 26 to 35%, especially from 27 to 33%.
The following proportions are preferred in this context:
a) 60-80 parts
b) 15-30 parts
c) 3-10 parts
A suitable epoxy-functional binder for the solid transparent powder coating material comprises, for example, epoxy-functional polyacrylate resins which can be prepared by copolymerizing at least one ethylenically unsaturated monomer which contains at least one epoxy group in the molecule with at least one further ethylenically unsaturated monomer which contains no epoxy group in the molecule, at least one of the monomers being an ester of acrylic acid or methacrylic acid. Epoxy-functional polyacrylate resins of this kind are known, for example, from EP-A-299 420, DE-B-22 14 650, DE-B-27 49 576, U.S. Pat. No. 4,091,048 and U.S. Pat. No. 3,781,379.
Examples of ethylenically unsaturated monomers which contain no epoxy group in the molecule are alkyl esters of acrylic and methacrylic acid containing 1 to 20 carbon atoms in the alkyl radical, especially methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, 2-ethylhexyl acrylate and 2-ethylhexyl methacrylate. Further examples of ethylenically unsaturated monomers which contain no epoxy groups in the molecule are acid amides, such as acrylamide and methacrylamide, vinylaromatic compounds, such as styrene, methylstyrene and vinyltoluene, nitrites, such as acrylonitrile and methacrylonitrile, vinyl halides and vinylidene halides, such as vinyl chloride and vinylidene fluoride, vinyl esters, such as vinyl acetate, and hydroxyl-containing monomers, such as hydroxyethyl acrylate and hydroxyethyl methacrylate, for example.
The epoxy-functional monomers employed in the epoxy-functional binders are preferably glycidyl acrylate, glycidyl methacrylate and allyl glycidyl ether. The epoxy-functional polyacrylate resin normally has an epoxide equivalent weight of from 300 to 2500, preferably from 420 to 700, a number-average molecular weight (determined by gel permeation chromatography using a polystyrene standard) of from 2000 to 20,000, preferably from 3000 to 10,000, and a glass transition temperature (T
g
) of from 30 to 80, preferably from 40 to 70 and, with particular preference, from 40 to 60° C. (measured with the aid of Differential Scanning Calorimetry (DSC)). Very particular preference is given to about 50° C. Mixtures of two or more acrylate resins can also be employed.
The epoxy-functional polyacrylate resin can be prepared by common and well-known methods, by addition polymerization.
As component (b), tris(alkoxycarbonylamino)triazines in accordance with U.S. Pat. No. 4,939,213, U.S. Pat. No. 5,084,541 and EP 0 624 577 are employed. Such compounds are also known from DE 2509561 and also Patent Abstracts of Japan, Publ. No. 09194769 A. However, the tris(alkoxycarbonylamino)triazines are employed therein only for cationic electrodeposition coating materials.
In accordance with the invention, the tris(alkoxycarbonylamino)triazines are of the formula
in which R=methyl, butyl, ethylhexyl groups. Derivatives of these compounds can also be employed.
The invention prefers the methyl/butyl mixed esters. These have the advantage over the plain methyl esters of better solubility in polymer melts, and butyl-ethylhexyl mixed esters. The plain butyl esters are also preferred in accordance with the invention.
The tris(alkoxycarbonylamino)triazines and their derivatives can also, in accordance with the invention, be employed in a mixture with conventional crosslinking agents (component C). Here, blocked polyisocyanates different from the tris(alkoxycarbonyl amino)triazines are particularly suitable. Similarly, it is possible to employ amino resins, e.g. melamines. The tris(alkoxycarbonylamino)triazines can be present in amounts of from 1 to 10, preferably from 2 to 10% by weight.
In principle it is possible to employ any amino resin suitable for transparent topcoats, or a mixture of such amino resins.
Resins of this kind are well known to the person skilled in the art and are offered as commercial products by numerous companies. Amino resins are condensation products of aldehydes, especially formaldehyde, and, for example, urea, melamine, guanamine and benzoguanamine. The amino resins contain alcohol groups, preferably methylol groups, some or all of which in general are etherified with alcohols.
Further suitable crosslinkers are carboxylic acids, especially saturated, straight-chain, aliphatic dicarboxylic acids having 3 to 20 carbon atoms in the molecule. It is very particularly preferred to employ dodecane-1,12-dioic acid. In order to modify the properties of the finished transparent powder coating materials, other carboxyl-containing crosslinkers may be employed if desired. As examples of these mention may be made of saturated branched or unsaturated straight-chain di- and polycarboxylic acids and of polymers having carboxyl groups.
Suitability extends to transparent powder coating materials which comprise an epoxy-functional crosslinker and an acid-functional binder.
Examples of suitable acid-functional binders are acidic polyacrylate resins which can be prepared by copolymerizing at least one ethylenically unsaturated monomer containing at least one acid group in the molecule with at least one further ethylenically unsaturated monomer containing no acid group in the molecule.
The epoxy-functional binder and the carboxyl-functional crosslinker and, respectively, the carboxyl binder and epoxy crosslinker are normally employed in an amount such that there are from 0.5 to 1.5, preferably from 0.75 to 1.25, equivalents of carboxyl groups per equivalent of epoxy groups. The amount of carboxyl groups present can be determined by titration with an alcoholic KOH solution.
In accordance with the invention the binder includes vinylaromatic compounds, especially styrene. In order to limit the risk of cracking on exposure to weathering, however, their conte
Baumgart Hubert
Schwarte Stephan
Woltering Joachim
Aylward D.
BASF Coatings AG
Dawson Robert
LandOfFree
Clear powder coating does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Clear powder coating, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Clear powder coating will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2836134