Ceramic metal halide lamp having medium aspect ratio

Electric lamp and discharge devices – With gas or vapor – Having electrode lead-in or electrode support sealed to...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C313S638000, C313S643000

Reexamination Certificate

active

06555962

ABSTRACT:

BACKGROUND OF THE INVENTION
The present invention relates to an electric lamp having a ceramic discharge vessel enclosing a discharge space having a length L, a diameter D, and an aspect ratio L/D; a fill gas including xenon, mercury, sodium halide, and halides of rare earth metals; and a pair of electrodes for maintaining a discharge in the fill gas.
High wattage (over 150 W) metal halide lamps are presently available only with quartz discharge vessels, which are larger than ceramic vessels and have a lower (−200° C.) wall temperature. A smaller vessel is desirable because the smaller discharge vessel better approximates a point source. Higher temperatures are desirable to achieve a higher cold spot temperature T
C
on the vessel wall; this increases the vapor pressure of the salts in the fill gas. The term “ceramic” as used herein means metal oxide, such as sapphire or polycrystalline alumina (PCA), as well as nitrides such as AlN.
U.S. Pat. No. 5,973,453 discloses a ceramic discharge metal halide (CDM) lamp wherein EA/D>5, EA being the distance between electrode tips, the tips being spaced from the endwalls of the discharge space. The ionizable filling includes Xe as an ignition gas, and NaI and CeI
3
in a molar ratio between 3:1 and 7:1. In an embodiment having a rated power of 150 W and intended as a retrofit for a high pressure sodium installation operating at 80-100 volts, EA/D=8, the fill includes Hg, and the Xe fill pressure is 250 mbar (187 torr). This yields a color rendering index (CRI) of 58 at a color temperature of 3900° K., and a luminous efficacy of 130 lm/W. It is noted that a comparable HPS lamp has a lower luminous efficacy (110 lm/W) and considerably lower CRI (
21
), while a comparable high pressure mercury lamp has comparable CRI but much lower efficacy (60 lm/W).
In another 150 W embodiment disclosed in U.S. Pat. No. 5,973,453, the fill is free of mercury and the lamp is operated at 45 V, so it is not suited as a retrofit for HPS. The Xe fill pressure is 1250 mbar (938 torr), the efficacy is 145 lm/W, and the CRI is 53. In a 185 W embodiment, the lamp voltage is 53 V, the Xe fill pressure is 500 mbar (375 torr), and the CRI is 61. All embodiments use a ceramic tube with a wall thickness of 1.4 mm. All Hg-free embodiments are operated on a square wave voltage generated by an electronic ballast.
While U.S. Pat. No. 5,973,453 discloses a CDM lamp with high efficacy, and even suggests a possible retrofit for an HPS ballast, the color rendering is still less than desirable and would not be suitable for many applications.
U.S. Pat. No. 6,031,332 discloses a CDM lamp having a CRI over 90, and achieves a limited voltage crest factor, so that the lamp achieves a long useful life. Voltage crest factor V
CF
is the ratio of the reignition voltage to the arc voltage, i.e. the operating voltage. The reignition voltage is the voltage required to reignite the discharge when it extinguishes as the polarity of an AC supply voltage changes. V
CF
assumes a high value in particular when the lamp is operated on a sinusoidal voltage, which is typical of a magnetic ballast, and usually increases during lamp life.
U.S. Pat. No. 6,031,332 addresses the problem of increasing reignition voltage by including calcium iodide in the fill to a molar quantity of 30 to 50% of the total molar quantity of halides. The ratio EA/D is less than 1.0 and L/D is slightly greater than 1.0; the fill includes argon at a pressure of 140 mbar (105 torr) as the ignition gas. The lamp operates at 80 to 100 V but the power is only 70 W; as such it would not be suitable for retrofit in an HPS installation.
A well known problem in metal halide lamps is the occurrence of hydrogen iodide voltage spikes. HI spikes occur during run-up of metal halide lamps that have hydrogen contamination in the presence of free iodide. Typically, the hydrogen comes from water that is present in the fill gas, but it can also be present on the lamp parts and the salts. Special precautions are required to insure that the H
2
O level inside the arc tube is as low as possible, preferably less than 0.5% of the fill gas.
One method to eliminate the HI spikes is given in U.S. Pat. No. 4,409,517, which discloses the use of Nb as a window to allow the rapid diffusion of H
2
out of the arc tube. U.S. Pat. No. 4,203,049 discloses a getter for the hydrogen.
The prior art does not disclose a high wattage CDM lamp with good color rendering, high efficacy, and high lumen maintenance which would be suitable for use with an existing magnetic ballast for an HPS lamp.
SUMMARY OF THE INVENTION
It is a primary object of the invention to provide a high wattage (over 150 W) CDM lamp which can be used with a magnetic ballast which was designed for use with a high pressure sodium (HPS) lamp. It is a related object to provide a CDM lamp which limits hydrogen iodide voltage spikes so they are within the voltage supplied by the ballast.
It is a further object to provide a CDM lamp which has a low voltage crest factor so that flicker is eliminated and long life is achieved using an HPS ballast.
It is a further object to determine a design space for the lamp that is within established material limits while providing the desired lamp efficacy and color properties.
These and other objects are achieved in a CDM lamp using xenon as a starting gas and having an aspect ratio in the range of 3 to 5. This is considered a medium aspect ratio, since most prior art CDM lamps have aspect ratios of about 1, and HPS lamps have aspect ratios on the order of 10.
The design space was determined by the use of designed experiments and the characteristic equations for each design parameter.
FIG. 1
shows the design space that was found for a 200 W CDM lamp. Four curves were plotted. The curve on the lower left represents a voltage crest factor V
CF
of 1.7, and the space above it represents lower V
CF
's. This is desirable because ballasts for HPS lamps have low sustaining voltages. The next curve represents a wall temperature T
W
of 1250° C., and the space above it represents lower wall temperatures. This is desirable because at higher temperatures the PCA is attacked by the salts and also evaporates, which darkens the outer envelope and shortens lamp life. Next are two intersecting curves which define the actual design space. One is the curve for a cold spot temperature of 1005° C.; the space above it represents lower temperatures. The other represents an efficacy of 90 lm/W; the space below it represents higher efficacies. The design space is limited by an inside diameter of 6.7 mm and an inside length of 33 mm (aspect ratio 4.9), and, at an inside diameter of 8 mm, lengths of 25 mm (aspect ratio 3.1) and 30 mm (aspect ratio 3.8). Longer lengths may be possible.
The design space for the discharge tube is also limited by the need to reduce or eliminate hydrogen iodide voltage spikes. It was found that the level of HI spike voltage during the first run-up of the lamp is dependent on both the volume V of the arc tube and the cold fill pressure P of the starting gas (also called buffer or ignition gas). In a series of experiments with Xe as the gas, the minimum HI spike voltage was measured and plotted against the product of P and the volume, as shown in
FIG. 4. A
curve fit to the data is described by the equation V
HI
=33654 PV
−1.185
, where P is in torr and V is in cubic centimeters. To minimize H
2
and H
2
O in these experiments, the arc tubes were made in an inert gas atmosphere dry box, the discharge tube was vacuum baked at 1300° for one hour, the electrodes were vacuum baked at elevated temperature, and the salts were contained in an inert gas atmosphere until dosed into the arc tube. In spite of these careful steps, HI spikes still form, but can be controlled by choice of P and V.
For a lamp to sustain on a ballast, the voltage spike must be below the available voltage supplied by the ballast. This voltage is typically 200 volts or more for lamps whose nominal lamp voltages are over 90 volts. The spike voltage should be les

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Ceramic metal halide lamp having medium aspect ratio does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Ceramic metal halide lamp having medium aspect ratio, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Ceramic metal halide lamp having medium aspect ratio will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3001148