ABSTRACT:
TECHNICAL FIELD
The present invention relates to a cathode ray tube glass coated with a water-soluble coating film, a method for producing the cathode ray tube glass, and a method for cleaning the cathode ray tube glass.
BACKGROUND ART
For avoiding or removing contaminants attached to a surface of a cathode ray tube glass such as a panel glass, a funnel glass and so on during manufacture, processing, storage and transportation of it, there have been practiced: (1) a method for cleaning the atmosphere around such glass; (2) a method for preventing such glass from the contact with a container for storage and so on; (3) a method for preventing the deposition of contaminants due to material existing around such glass; and (4) a method for removing contaminants by a washing treatment having a physical or chemical effect before a necessary operation. Further, as a new cleaning method utilizable generally for glass, there has been proposed such a method that a coating film is formed by applying previously a water-soluble salt on a glass surface so that contaminants which may be attached onto the coating film are dissolved and removed together with the coating film by washing (JP-A-6-340865).
Various surface treatments such as coating of a fluorescent material, coating of an electric conductive graphite, coating of an antireflection film and so on are conducted to a surface of the cathode ray tube glass. In this case, when a slight amount of contaminants are attached to the surface, water repellency is effected to thereby cause difficulty in conducting the normal coating operations. Even though the coating operations have been completed, there is still a danger of inducing a defect in patterning a fluorescent material or an insufficient electric strength owing to remaining contaminants. Therefore, an extremely high cleanness is required for the cathode ray tube glass in comparison with a glass product for another usage.
The cathode ray tube glass comprises generally a panel glass and a funnel glass.
FIG. 1
shows a construction of the cathode ray tube glass wherein reference numeral
1
designates a funnel glass, numeral
2
a panel glass, numeral
3
a funnel portion, numeral
4
a neck tube portion, numeral
5
a seal edge portion, numeral
6
a pin, numeral
7
an anode button, and numeral
8
a face portion. Hereinbelow, a body formed by sealing the neck tube portion to the funnel portion is simply referred to as the funnel glass.
Generally, glass products such as panel glass, funnel portions, neck tube portions and so on, after having been shaped and processed, are transported to and stored in a warehouse or the like for a predetermined term until they undergo joining and sealing operations or surface treatments. Accordingly, it is very difficult to completely avoid contamination due to a slight amount of contaminants which may be attached to a glass surface of them even though care is taken for cleaning the atmosphere around the glass products or choosing a suitable wrapping material in order to avoid such contamination.
Further, once the contaminants have attached to the glass surface, reactions occur on the glass surface with a lapse of time to increase an adhesive force. Accordingly, in many cases, the contaminants on the glass surface can not be removed by simply washing operations. It is, therefore, necessary to conduct washing with a strong acid or alkali such as hydrofluoric acid or sodium hydroxide or the like, or to use above-mentioned washing with another washing operation utilizing a physical effect. However, these forcible washing operations are troublesome in use; an increase of cost is invited and there is a danger of causing an additional defect on the glass surface which have been finely processed. Further, these forcible operations cause difficulty in draining a waste solution from the standpoint of environmental protection.
The technique disclosed in JP-A-6-340865 does not mention in a concrete manner such means for providing an excellent cleaning performance required for the cathode ray tube glass or eliminating an adverse effect, to a TV characteristic, caused by a water-soluble material which may remain on the glass surface.
It is an object of the present invention to provide a cathode ray tube glass, a method for producing the cathode ray tube glass and a method for cleaning the cathode ray tube glass, wherein contaminants inevitably attached onto a surface of the cathode ray tube glass during manufacturing, processing, transporting and storing can easily and effectively be removed.
DISCLOSURE OF INVENTION
In accordance with the present invention, there is provided a cathode ray tube glass which comprises a clean cathode ray tube made of glass and a coating film composed of at least one water-soluble material selected from the group consisting of water-soluble salts, acids being solid at room temperature, monosaccharides and polysaccharides (hereinbelow, referred to simply as the water-soluble coating film), which is formed on a glass surface of the cathode ray tube in an amount of 0.01-100 &mgr;g/cm
2
.
In the present invention, it is important that an amount of a coating film attached to the glass surface (in a dried state) is 0.01-100 &mgr;g/cm
2
in order not to cause any defect in the water-soluble coating film and not to damage the transparency of the glass. A precise analysis to an amount of the attached coating film in accordance with an ESCA surface analysis revealed to be 0.1-200 nm when the amount of the attached coating film is converted into a film thickness.
Therefore, in accordance with the present invention, there is provided a cathode ray tube glass which comprises a clean cathode ray tube made of glass and a coating film composed of at least one water-soluble material selected from the group consisting of water-soluble salts, acids being solid at room temperature, monosaccharides and polysaccharides, which is formed on a glass surface of the cathode ray tube to a film thickness of 0.1-200 nm.
In the present invention, it is important to previously form the water-soluble coating film in an optimum amount to obtain a defectless, uniform coating film on a glass surface of the cleaned cathode ray tube glass (hereinbelow, referred to simply as the glass surface). The presence of the coating film prevents contaminants, which are inevitably deposited on the glass surface during transportation and storage and so on, from adhering on the glass surface. Further, these contaminants can be removed together with the water-soluble coating film by conducting a simple washing treatment to the glass surface. As a result, even though the glass surface is stained with contaminants during storage and transportation, it is easy to restore a cleaned glass surface in the cathode ray tube glass.
REFERENCES:
patent: 4234669 (1980-11-01), Pearlman
patent: 5521292 (1996-05-01), Ueda et al.
patent: 5717281 (1998-02-01), Tong et al.
patent: 6280849 (2001-08-01), Miwa
patent: 6287651 (2001-09-01), Sasaki et al.
patent: 33 16 399 (1984-11-01), None
patent: 35 40 247 (1987-05-01), None
patent: 402124982 (1990-05-01), None
patent: 6-340865 (1994-12-01), None
patent: WO 95/34608 (1995-12-01), None
Patent Abstracts of Japan, Vol., 095, No. 003, Apr. 28, 1995, JP 06-340865, Dec. 13, 1994.
Rokudai Satoshi
Sasaki Mikio
Asahi Glass Company Ltd.
Miggins Michael C.
Oblon & Spivak, McClelland, Maier & Neustadt P.C.
Pyon Harold
LandOfFree
Cathode ray tube glass, a method for producing the cathode... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Cathode ray tube glass, a method for producing the cathode..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Cathode ray tube glass, a method for producing the cathode... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3270985