Cathode for aluminum producing electrolytic cell

Electrolysis: processes – compositions used therein – and methods – Electrolytic coating – Utilizing fused bath

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C205S385000, C205S394000, C205S396000, C204S243100, C204S290010, C204S291000

Reexamination Certificate

active

06719889

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates to electrolytic production of aluminum and more particularly, it relates to an improved cathode suited for use in a low temperature electrolytic cell for the production of aluminum.
In the electrolytic production of aluminum, there is great interest in utilizing a cathode that is highly conductive and does not react with molten aluminum deposited thereon. Carbon cathodes which are traditionally used in the Hall-Heroult cells have the problem that they are not readily wettable with molten aluminum. The carbon cathode surface reacts with the molten aluminum and forms aluminum carbide. Thus, the cathode is depleted at about 2 to 5 cm/yr. during operation of the cell. Or, the carbon cathode has the problem that it permits formation of cyanides, presenting a disposal problem. Thus, the carbon cathode has been replaced or modified with materials to improve its performance.
For example, U.S. Pat. No. 5,961,811 discloses an improved carbonaceous material suitable for use as a cathode in an aluminum producing electrolytic cell, the cell using an electrolyte comprised of sodium containing compounds. The carbonaceous material is comprised of carbon and a reactive compound capable of suppressing the formation or accumulation of sodium cyanide during operation of the cell, of reacting with sodium to reduce problems associated with sodium intercalation, and of reacting with one of titanium or zirconium to form titanium or zirconium diboride during operation of the cell to produce aluminum.
U.S. Pat. No. 5,217,583 discloses electrodes suitable for electrochemical processing which are a preferred product form, particularly electrodes for use in the electrowinning of aluminum from its oxide. According to the patent, such products are comprised of a dimensionally stable combustion synthesis product of a composition containing at least 20% by weight of a particulate combustible material; at least 15% by weight of a particulate filler material capable of providing desired mechanical and electrical properties; and up to 35% by weight of a particulate inorganic binder having a melting point lower than the combustion synthesis temperature.
U.S. Pat. No. 4,243,502 discloses a wettable cathode for an electrolytic cell for the electrolysis of a molten charge, in particular for the production of aluminum, where the said cathode comprises individual, exchangeable elements each with a component part for the supply of electrical power. The elements are connected electrically, via a supporting element, by molten metal which has separated out in the process. The interpolar distance between the anodes and the vertically movable cathode elements is at most 2 cm.
U.S. Pat. No. 4,376,029 discloses a cathode component for a Hall aluminum cell which is economically produced from a mixture of a carbon source, preferably calcined petroleum coke, and optionally calcined acicular needle petroleum coke, calcined anthracite coal; a binder such as pitch including the various petroleum and coal tar pitches; titanium dioxide, TiO
2
; and boric acid, B
2
O
3
or boron carbide, B
4
C; forming said mixture into shapes and heating to a TiB
2
-forming temperature.
U.S. Pat. No. 4,439,382 discloses that titanium diboride graphite composite articles are produced by mixing TiO
2
, petroleum coke and a binder to form a plastic dispersion. Articles are shaped by molding or extrusion and baked to carbonize the binder to form a baked carbon-TiO
2
composite. The article is impregnated with a molten or dispersed boron compound, then heated to drive TiB
2
forming reaction. The article is then further heated to a graphitizing temperature to form a graphite-TiB
2
composite useful as a cathode component in a Hall aluminum reduction cell.
U.S. Pat. No. 4,456,519 discloses an electrode made of a number of elongated elements which are plates, rods or tubes. The elements are composed of inorganic conductive fibers embedded in a solid, electrochemically active material. The fibers are oriented in the direction of current flow.
U.S. Pat. No. 4,465,581 discloses that TiB
2
-graphite composite articles suitable for use as cathode components in a Hall aluminum reduction cell are made by impregnating a TiO
2
-carbon composite with a boron compound and carbon black dispersed in water, or alternately by impregnating a boron or boron compound-carbon composite with a carbon black-TiO
2
dispersion, and heating the article to a reaction temperature whereby TiB
2
is formed and the amorphous carbon converted to graphite. The article may be impregnated with a carbonizable liquid, re-baked, and re-heated to a graphitizing temperature to increase its strength and density.
U.S. Pat. No. 4,478,693 discloses an inert type electrode composition suitable for use in the electrolytic production of metals such as aluminum. The aluminum is produced from an aluminum-containing material dissolved in a molten salt. The electrode composition is fabricated from at least two metals or metal compounds combined to provide a combination metal compound containing at least one of the group consisting of oxide, fluoride, nitride, sulfide, carbide or boride.
U.S. Pat. No. 5,129,998 discloses that the density of various refractory hard metal articles are controlled so that articles made from the refractory hard metals are able to float on the surface of molten aluminum. Floating such articles on aluminum has been found to both stabilize and protect the surface of molten aluminum. Floating cathodes for use in aluminum reduction cells is a particular application for the floating refractory hard metals.
U.S. Pat. No. 5,527,442 discloses a carbonaceous, refractory or metal alloy substrate material coated with a refractory material, the refractory material including at least one of borides, silicides, nitrides, aluminides, carbides, phosphides, oxides, metal alloys, inter-metallic compounds and mixtures of one of titanium, chromium, zirconium, hafnium, vanadium, silicon, niobium, tantalum, nickel, molybdenum and iron and at least one refractory oxide of rare earth metals. An aluminum production cell including a component made up of a material coated with the coating described above is also disclosed.
U.S. Pat. No. 5,538,604 discloses an improved carbonaceous material suitable for use as a liner in an aluminum producing electrolytic cell, the cell using an electrolyte comprised of sodium containing compounds and the carbonaceous material penetrable by sodium or nitrogen and resistant to formation or accumulation of sodium cyanide during operation of the cell. The carbonaceous material is comprised of carbon and a reactive compound capable of reacting with one of sodium, nitrogen and sodium cyanide during operation of the cell to produce aluminum, the reactive compound present in an amount sufficient to suppress formation or accumulation of cyanide compounds in the liner.
U.S. Pat. No. 5,006,209 discloses that cathodes for use in low temperature cells 660° to 800° C. are typically composed of an electrically conductive, refractory hard metal which is wet by molten aluminum and stands up well in the bath under operating conditions and that the preferred cathode material is titanium diboride. U.S. Pat. No. 4,865,701 discloses that other useful cathode materials include titanium carbide, zirconium carbide, zirconium diboride, niobium diboride, tantalum diboride and combinations of said diboride in solid solution form, e.g., (Nb, Ta)B
2
.
In spite of these disclosures, there is still need for an improved cathode suitable for use in an electrolytic cell for producing aluminum.
SUMMARY OF THE INVENTION
It is an object of the invention to provide an improved cathode for use in an electrolytic cell for reducing alumina to aluminum in a molten salt.
It is another object of the invention to provide a cathode comprised of a base material having high electrical resistivity for use in an electrolytic cell for reducing alumina to aluminum in a molten salt.
It is yet another object of the invention to provide a composite cathode comprised of a base

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Cathode for aluminum producing electrolytic cell does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Cathode for aluminum producing electrolytic cell, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Cathode for aluminum producing electrolytic cell will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3188706

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.