Catalytic partial oxidation process and promoted nickel...

Details Catalytic partial oxidation process and promoted nickel... Catalytic partial oxidation process and promoted nickel...

2000-07-27

2002-06-11

Richter, Johann (Department: 1621)

Compositions

Gaseous compositions

Carbon-oxide and hydrogen containing

C518S702000, C518S703000

Reexamination Certificate

active

06402989

ABSTRACT:

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT
No applicable.
FIELD OF THE INVENTION
The present invention relates to catalysts and processes for the catalytic partial oxidation of hydrocarbons (e.g., natural gas), for the preparation of a mixture of carbon monoxide and hydrogen using a supported metal catalyst. More particularly, the invention relates to catalysts and processes using catalysts comprising promoted nickel-based catalysts supported on magnesium oxide.
BACKGROUND OF THE INVENTION
Large quantities of methane, the main component of natural gas, are available in many areas of the world, and natural gas is predicted to outlast oil reserves by a significant margin. However, most natural gas is situated in areas that are geographically remote from population, and industrial centers. The costs of compression, transportation, and storage make its use economically unattractive.
To improve the economics of natural gas use, much research has focused on methane as a starting material for the production of higher hydrocarbons and hydrocarbon liquids. The conversion of methane to hydrocarbons is typically carried out in two steps. In the first step, methane is reformed with water to produce carbon monoxide and hydrogen (i.e., synthesis gas or “syngas”). In a second step, the syngas is converted to hydrocarbons.
Current industrial use of methane as a chemical feedstock proceeds by the initial conversion of methane to carbon monoxide and hydrogen by either steam reforming, which is the most widespread process, or by dry reforming. Steam reforming currently is the major process used commercially for the conversion of methane to synthesis gas, proceeding according to Equation 1.
CH
4
+H
2
O
CO+3H
2
  (1)
Although steam reforming has been practiced for over five decades, efforts to improve the energy efficiency and reduce the capital investment required for this technology continue.
The catalytic partial oxidation of hydrocarbons, e.g., natural gas or methane to syngas is also a process known in the art. While currently limited as an industrial process, partial oxidation has recently attracted much attention due to significant inherent advantages, such as the fact that significant heat is released during the process, in contrast to steam reforming processes.
In catalytic partial oxidation, natural gas is mixed with air, oxygen-enriched air, or oxygen, and introduced to a catalyst at elevated temperature and pressure. The partial oxidation of methane yields a syngas mixture with a H
2
:CO ratio of 2:1, as shown in Equation 2.
CH
4
+1/2O
2
CO+2H
2
  (2)
This ratio is more useful than the H
2
:CO ratio from steam reforming for the downstream conversion of the syngas to chemicals such as methanol and to fuels. The partial oxidation is also exothermic, while the steam reforming reaction is strongly endothermic. Furthermore, oxidation reactions are typically much faster than reforming reactions. This allows the use of much smaller reactors for catalytic partial oxidation processes. The syngas in turn may be converted to hydrocarbon products, for example, fuels boiling in the middle distillate range, such as kerosene and diesel fuel, and hydrocarbon waxes by processes such as the Fischer-Tropsch Synthesis.
The selectivities of catalytic partial oxidation to the desired products, carbon monoxide and hydrogen, are controlled by several factors, but one of the most important of these factors is the choice of catalyst composition. Difficulties have arisen in the past in making such a choice economical. Typically, catalyst compositions have included precious metals and/or rare earths. The large volumes of expensive catalysts needed by present day catalytic partial oxidation processes have placed these processes generally outside the limits of economic justification.
For successful operation at commercial scale, the catalytic partial oxidation process must be able to achieve a high conversion of the methane feedstock at high gas hourly space velocities, and the selectivity of the process to the desired products of carbon monoxide and hydrogen must be high. Such high conversion and selectivity must be achieved without detrimental effects to the catalyst, such as the formation of carbon deposits (“coke”) on the catalyst, which severely reduces catalyst performance. Accordingly, substantial effort has been devoted in this field to the development of catalysts allowing commercial performance without coke formation.
A number of process regimes have been proposed for the production of syngas via partial oxidation reactions. For example, the process described in U.S. Pat. No. 4,877,550 employs a syngas generation process using a fluidized reaction zone. Such a process however, requires downstream separation equipment to recover entrained supported-nickel catalyst particles.
A fixed bed reactor configuration would alleviate the catalyst degradation, but would require a pressure differential (pressure drop) to allow gas flow over the catalyst. To overcome the relatively high pressure drop associated with gas flow through a fixed bed of catalyst particles, which can prevent operation at the high gas space velocities required, various structures for supporting the active catalyst in the reaction zone have been proposed. U.S. Pat. No. 5,510,056 discloses a monolithic support such as a ceramic foam or fixed catalyst bed having a specified tortuosity and number of interstitial pores that is said to allow operation at high gas space velocity. The preferred catalysts for use in the process comprise ruthenium, rhodium, palladium, osmium, iridium, and platinum. Data are presented for a ceramic foam supported rhodium catalyst at a rhodium loading of from 0.5-5.0 wt %.
U.S. Pat. No. 5,648,582 also discloses a process for the catalytic partial oxidation of a feed gas mixture consisting essentially of methane. The methane-containing feed gas mixture and an oxygen-containing gas are passed over an alumina foam supported metal catalyst at space velocities of 120,000 hr.
−1
to 12,000,000 hr.
−1
The catalytic metals exemplified are rhodium and platinum, at a loading of about 10 wt %.
Catalysts containing Group VIII metals such as nickel on a variety of supports are known in the art. For example, V. R. Choudhary et al. (“Oxidative Conversion of Methane to Syngas over Nickel Supported on Low Surface Area Catalyst Porous Carriers Precoated with Alkaline and Rare Earth Oxides,” J. Catal., Vol. 172, pages 281-293, 1997) disclose the partial oxidation of methane to syngas at contact times of 4.8 ms (at STP) over supported nickel catalysts at 700 and 800° C. The catalysts were prepared by depositing NiO—MgO on different commercial low surface area porous catalyst carriers consisting of refractory compounds such as SiO
2
, Al
2
O
3
, SiC, ZrO
2
and HfO
2
. The catalysts were also prepared by depositing NiO on the catalyst carriers with different alkaline and rare earth oxides such as MgO, CaO, SrO, BaO, Sm
2
O
3
and Yb
2
O
3
.
U.S. Pat. No. 5,149,464 discloses a method for selectively converting methane to syngas at 650° C. to 950° C. by contacting the methane/oxygen mixture with a solid catalyst, which is either:
(a) a catalyst of the formula M
x
M′
y
O
z
where:
M is at least one element selected from Mg, B, Al, Ln, Ga, Si, Ti, Zr and Hf;
Ln is at least one member of lanthanum and the lanthanide series of elements,
M′ is a d-block transition metal, and each of the ratios x/z and y/z and (x+y)/z is independently from 0.1 to 8; or
(b) an oxide of a d-block transition metal; or
(c) a d-block transition metal on a refractory support; or
(d) a catalyst formed by heating a) or b) under the conditions of the reaction or under nonoxidizing conditions.
The d-block transition metals are stated to be selected from those having atomic number 21 to 29, 40 to 47 and 72 to 79, the metals scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, ha

Affiliated with

Also associated with

Rating

Catalytic partial oxidation process and promoted nickel... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Catalytic partial oxidation process and promoted nickel..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Catalytic partial oxidation process and promoted nickel... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2936599