Catalyst – solid sorbent – or support therefor: product or process – Catalyst or precursor therefor – Plural component system comprising a - group i to iv metal...
Reexamination Certificate
2002-08-30
2004-10-05
Bell, Mark L. (Department: 1755)
Catalyst, solid sorbent, or support therefor: product or process
Catalyst or precursor therefor
Plural component system comprising a - group i to iv metal...
C525S050000, C428S407000
Reexamination Certificate
active
06800581
ABSTRACT:
The present invention relates to a catalyst composition for homopolymerization or copolymerization of olefins.
Ziegler-Natta catalysis for the polymerization of olefins is a widely known catalytic process. A typical Ziegler-Natta catalyst comprises a transition metal compound and a cocatalyst. The transition metal compound may be supported on a support. Supports suitable in A Ziegler-Natta catalysis are known from the prior art to be common refractory oxide supports, such as silica. However, polymeric supports have been developed in recent years. A number of patents claim the use of polymers as supports for polymerization catalysts. U.S. Pat. No. 4,900,706 discloses that polymer supports may be impregnated with titanium, magnesium and chlorine as a component for a catalyst for olefin polymerization wherein copolymers of olefins and styrene are the preferred polymer supports. U.S. Pat. No. 5,118,648 discloses the use of porous polymer supports, with the preferred embodiment comprising divinyl benzene cross-linked polystyrene.
Further, U.S. Pat. No. 5,412,070 discloses that terpolymers of ethylene, propylene and carbon monoxide (aliphatic polyketone) may be effectively employed as a support for a palladium-based catalyst system. In U.S. Pat. No. 5,952,456 it is similarly suggested to use polyketone as a support for the preparation of aliphatic polyketones, but specifically it is disclosed that when an aluminoxane is used it may be attractive to employ commercially available supported aluminoxane, for example methyl aluminoxane on silica.
Anyone skilled in the art is aware of the broad range of electron donors, including ethers, used in association with Ziegler-Natta-catalysts. Consequently, the widest possible chemical resistance available is advantageous in selecting a polymer support material. Polymeric supports also have the advantage of short, low temperature drying steps and reportedly higher tolerance to water and oxygen impurities compared to traditionally used refractory oxide supported catalysts.
However, the polymer supports disclosed in the prior art typically suffer some weaknesses that decrease their utility in this particular application. Compared to oxide supported catalysts the polymer supports known are much more expensive.
It is therefore an object of the present invention to provide a catalyst composition for polymerization of olefins comprising a polymer support which overcomes the drawbacks of the prior art.
Further, it is an object of the present invention to provide a process for homopolymerization or copolymerization of olefins wherein such a catalyst composition may be utilized.
The object regarding the catalyst composition is solved by a catalyst composition for homopolymerization or copolymerization of olefins comprising:
(a) a solid catalyst precursor comprising a transition metal compound of group IVB, VB, or VIB of the periodic table, a magnesium compound and aliphatic polyketone particles; and
(b) a cocatalyst comprising an aluminum alkyl, an aluminoxane or mixtures thereof.
Surprisingly, it was found that aliphatic polyketone may be excellently used as a polymeric support in the field of Ziegler-Natta-catalysis. Aliphatic polyketone has a high melting point, good chemical resistance and mechanical strength.
Further, it is non-friable, insensitive to common solvents and tolerant to typical catalyst components. In preparation of such an aliphatic polyketone support the dehydration step is relatively short and may be carried out at comparatively lower temperatures.
The high melting point, chemical resistance and strength of aliphatic polyketones offer the opportunity to realistically compete with silica as a support. Typical aliphatic polyketones melt at over 210° C. with a high level of ductility and resistance to common organic solvents.
Aliphatic polyketones allow for reaction of the polymer with reducing agents and presumably with Grignard reagents to afford a low-chlorine, magnesiumalkoxide supported catalyst. Therefore, one further advantage is the lack of chlorine in the aliphatie polyketone.
With regard to the reaction of aliphatic polyketones with reducing agents these aliphatic polyketones have to be differentiated from the widely know aromatic polyketones. Typicial aromatic polyketones have virtually inaccessible ketone sites, which make them very poor candidates for a reaction with Grignard reagents. The bulk of the polymer backbone of the aromatic polyketones makes them unlikely candidates for surface modification. Further, aromatic polyketones generally have very high melting temperatures.
The use of aliphatic polyketone as a support in the catalyst composition according to the present invention has the following advantages:
reduced chlorine content relative to traditional chlorinated supported catalysts, such as polyvinylchloride;
low potential toxicity;
an electron donor is “built in” in an unreacted, accessible ketone site;
high solvent resistance;
reactivity of aliphatic ketone sites to reducing and alkylating agents (such as hydrates, aluminum alkyls and Grignard reagents);
secondary and tertiary alkoxides which have been claimed to enhance activity, bulk density, etc. may be “built in” from the support;
high temperature resistance of aliphatic polyketones that can allow for higher preparation temperatures;
good aluminum alkyl compatibility;
higher chemical and thermal stability during processing relative to “standard polymers”.
In summary, using aliphatic polyketone as a support for the catalyst composition of the present invention offers a unique blend of the properties of silica and polymer supports known in the prior art.
Preferably, the polymer particles of the aliphatic polyketone have a mean particle diameter of about 5 to about 10,000 &mgr;m, preferably about 15 to 500 &mgr;m, a pore volume of at least about 0.1 cm
3
/g, a pore diameter of at least about 500 to 10,000 Angstrom and a surface area of from about 0.2 m
2
/g to about 50 m
2
/g, and are, most preferably, regularly shaped.
Aliphatic polyketone suitable as a support for the catalyst composition of the present invention may have a molecular weight in the range of about 3,000 to about 300,000 g/mole.
The polymer particles used in the present invention have labile aliphatic ketone groups as surface active sites. Preferably, these active sites are reacted stoichiometrically with the organo-metallic compound.
Aliphatic polyketone particles offer significant advantages over traditional olefin polymerization catalysts using supports such as silica or magnesium chloride. In contrast to the silica supported catalyst, the polymer particles described in the present invention require substantially milder conditions for dehydration. Their chemical resistance to solvents is unique among most other polymer supports. The stability of the aliphatic polyketone polymer adds significant flexibility to catalyst preparation conditions in terms of solvents and temperature. The polyketone polymer used in the present invention is also commercially available at a significant cost savings compared to silica or magnesium chloride supports. Besides the lower cost of the polymer, the catalyst benefits from very low metal loadings, both of which decrease the final catalyst cost and diminish the ash in the final product. Also, the catalyst in the present invention is more active than conventional silica or magnesium chloride supported Ziegler-Natta catalysts and some supported metallocene catalysts.
Further, the catalyst composition of the present invention may comprise an electron donor which may be oxygenated organic material, such as diethers, diesters, alkyl carbonates and the like, or aryl or alkyl chlorides, such as monochlorbenzene, or mixtures thereof. The most preferred electron donor is ethylbenzoate
The transition metal compound may be represented by the general formula M(OR
1
)
n
X
4-n
wherein M represents a transition metal of group IVB, VB or VIB of the periodic table, R
1
represents an alkyl group, aryl group or cycloalkyl group having 1 to 20 carbon atoms, X represents a haloge
Hamed Orass M.
Ledford John
Moman Akhlaq A.
Nallaveerapan Navin
Palackal Syriac
Bell Mark L.
Brown Jennine
Kramer Levin Naftalis & Frankel LLP
Sabic Basic Industries Corporation
LandOfFree
Catalyst composition for polymerization of olefins and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Catalyst composition for polymerization of olefins and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Catalyst composition for polymerization of olefins and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3301450