Catalyst – solid sorbent – or support therefor: product or process – Catalyst or precursor therefor – Metal – metal oxide or metal hydroxide
Reexamination Certificate
1999-01-28
2001-06-19
Yildirim, Bekir L. (Department: 1764)
Catalyst, solid sorbent, or support therefor: product or process
Catalyst or precursor therefor
Metal, metal oxide or metal hydroxide
C502S303000, C502S304000, C502S326000, C502S327000, C502S336000, C502S339000, C502S335000
Reexamination Certificate
active
06248688
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a zirconium, rare earth containing composition comprising zirconium, cerium, neodymium and praseodymium components and the use of this composition in a catalyst composition useful for the treatment of gases to reduce contaminants contained therein and method process to make the catalyst composition. The present invention relates to an improved catalysts of the type generally referred to as “three-way conversion” or “TWC” catalysts. TWC catalysts have the capability of substantially simultaneously catalyzing the oxidation of hydrocarbons and carbon monoxide and the reduction of nitrogen oxides.
2. Discussion of Related Art
Three-way conversion catalysts (TWC) have utility in a number of fields including the treatment of exhaust from internal combustion engines, such as automobile and other gasoline-fueled engines. Emissions standards for unburned hydrocarbons, carbon monoxide and nitrogen oxides contaminants have been set by various governments and must be met, for example, by new automobiles. In order to meet such standards, catalytic converters containing a TWC catalyst are located in the exhaust gas line of internal combustion engines. The catalysts promote the oxidation by oxygen in the exhaust gas of the unburned hydrocarbons and carbon monoxide and the reduction of nitrogen oxides to nitrogen.
Known TWC catalysts which exhibit good activity and long life comprise one or more platinum group metals (e.g., platinum or palladium, rhodium, ruthenium and iridium) located upon a high surface area, refractory oxide support, e.g., a high surface area alumina coating. The support is carried on a suitable carrier or substrate such as a monolithic carrier comprising a refractory ceramic or metal honeycomb structure, or refractory particles such as spheres or short, extruded segments of a suitable refractory material.
U.S. Pat. No. 4,134,860 relates to the manufacture of catalyst structures. The catalyst composition can contain platinum group metals, base metals, rare earth metals and refractory, such as alumina support. The composition can be deposited on a relatively inert carrier such as a honeycomb.
High surface area alumina support materials, also referred to as “gamma alumina” or “activated alumina”, typically exhibit a BET surface area in excess of 60 square meters per gram (“m
2
/g”), often up to about 200 m
2
/g or more. Such activated alumina is usually a mixture of the gamma and delta phases of alumina, but may also contain substantial amounts of eta, kappa and theta alumina phases. It is known to utilize refractory metal oxides other than activated alumina as a support for at least some of the catalytic components in a given catalyst. For example, bulk ceria, zirconia, alpha alumina and other materials are known for such use. Although many of these materials suffer from the disadvantage of having a considerably lower BET surface area than activated alumina, that disadvantage tends to be offset by a greater durability of the resulting catalyst.
In a moving vehicle, exhaust gas temperatures can reach 1000° C. or higher, and such elevated temperatures cause the activated alumina (or other) support material to undergo thermal degradation caused by a phase transition with accompanying volume shrinkage, especially in the presence of steam, whereby the catalytic metal becomes occluded in the shrunken support medium with a loss of exposed catalyst surface area and a corresponding decrease in catalytic activity. It is a known expedient in the art to stabilize alumina supports against such thermal degradation by the use of materials such as zirconia, titania, alkaline earth metal oxides such as baria, calcia or strontia or rare earth metal oxides, such as ceria, lanthana and mixtures of two or more rare earth metal oxides. For example, see C. D. Keith et al U.S. Pat. No. 4,171,288.
Bulk cerium oxide (ceria) is disclosed to provide an excellent refractory oxide support for platinum group metals other than rhodium, and enables the attainment of highly dispersed, small crystallites of platinum on the ceria particles, and that the bulk ceria may be stabilized by impregnation with a solution of an aluminum compound, followed by calcination. U.S. Pat. No. 4,714,694 of C. Z. Wan et al, discloses aluminum-stabilized bulk ceria, optionally combined with an activated alumina, to serve as a refractory oxide support for platinum group metal components impregnated thereon. The use of bulk ceria as a catalyst support for platinum group metal catalysts other than rhodium, is also disclosed in U.S. Pat. No. 4,727,052 of C. Z. Wan et al and in U.S. Pat. No. 4,708,946 of Ohata et al.
U.S. Pat. No. 4,808,564 discloses a catalyst for the purification of exhaust gases having improved durability which comprises a support substrate, a catalyst carrier layer formed on the support substrate and catalyst ingredients carried on the catalyst carrier layer. The catalyst carrier layer comprises oxides of lanthanum and cerium in which the molar fraction of lanthanum atoms to total rare earth atoms is 0.05 to 0.20 and the ratio of the number of the total rare earth atoms to the number of aluminum atoms is 0.05 to 0.25.
U.S. Pat. No. 4,438,219 discloses an alumina supported catalyst for use on a substrate. The catalyst is stable at high temperatures. The stabilizing material is disclosed to be one of several compounds including those derived from barium, silicon, rare earth metals, alkali and alkaline earth metals, boron, thorium, hafnium and zirconium. of the stabilizing materials barium oxide, silicon dioxide and rare earth oxides which include lanthanum, cerium, praseodymium, neodymium, and others are indicated to be preferred. It is disclosed that contacting them with a calcined alumina film permits the calcined alumina film to retain a high surface area at higher temperatures.
European Patent Application 95/01849 (Publication No. 95/35152) discloses a layered catalyst composite including an oxygen storage composition which comprises a diluent such as zirconia, ceria, and one or more rare earth oxides selected from lanthana, neodymia and yttria. Also disclosed as oxygen storage components are praseodymia, ceria and neodymia which can be applied as soluble salts to a catalyst composition.
U.S. Pat. Nos. 4,476,246, 4,591,578 and 4,591,580 disclose three-way catalyst compositions comprising alumina, ceria, an alkali metal oxide promoter and noble metals. U.S. Pat. Nos. 3,993,572 and 4,157,316 represent attempts to improve the catalyst efficiency of Pt/Rh based TWC systems by incorporating a variety of metal oxides, e.g., rare earth metal oxides such as ceria and base metal oxides such as nickel oxides. U.S. Pat. No. 4,591,518 discloses a catalyst comprising an alumina support with components deposited thereon consisting essentially of a lanthana component, ceria, an alkali metal oxide and a platinum group metal. U.S. Pat. No. 4,591,580 discloses an alumina supported platinum group metal catalyst. The support is sequentially modified to include support stabilization by lanthana or lanthana rich rare earth oxides, double promotion by ceria and alkali metal oxides and optionally nickel oxide. Palladium containing catalyst compositions, e.g., U.S. Pat. No. 4,624,940, have been found useful for high temperature applications. The combination of lanthanum and barium is found to provide a superior hydrothermal stabilization of alumina which supports the catalytic component, palladium.
U.S. Pat. No. 4,294,726 discloses a TWC catalyst composition containing platinum and rhodium obtained by impregnating a gamma alumina carrier material with an aqueous solution of cerium, zirconium and iron salts or mixing the alumina with oxides of, respectively, cerium, zirconium and iron, and then calcining the material at 500 to 700° C. in air after which the material is impregnated with an aqueous solution of a salt of platinum and a salt of rhodium dried and subsequently treated in a hydrogen-containing gas at a temperature of 250-650° C. The alumina
Syed Mukaram K.
Wu Joseph H. Z.
Engelhard Corporation
Negin Richard A.
Yildirim Bekir L.
LandOfFree
Catalyst composition containing oxygen storage components does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Catalyst composition containing oxygen storage components, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Catalyst composition containing oxygen storage components will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2466937