ABSTRACT:
A Selective Catalytic Reduction (SCR) catalyst was prepared by slurry coating ZSM-5 zeolite onto a cordierite monolith, then subliming an iron salt onto the zeolite, calcining the monolith, and then dipping the monolith either into an aqueous solution of manganese nitrate and cerium nitrate and then calcining, or by similar treatment with separate solutions of manganese nitrate and cerium nitrate. The supported catalyst containing iron, manganese, and cerium showed 80 percent conversion at 113 degrees Celsius of a feed gas containing nitrogen oxides having 4 parts NO to one part NO2, about one equivalent ammonia, and excess oxygen; conversion improved to 94 percent at 147 degrees Celsius. N2O was not detected (detection limit: 0.6 percent N2O).
REFERENCES:
patent: 4220632 (1980-09-01), Pence et al.
patent: 4778665 (1988-10-01), Krishnamurthy et al.
patent: 4961917 (1990-10-01), Byrne
patent: 5024981 (1991-06-01), Speronello et al.
patent: 5077026 (1991-12-01), Nair et al.
patent: 5312608 (1994-05-01), Hayasaka et al.
patent: 5451387 (1995-09-01), Farnos et al.
patent: 5482692 (1996-01-01), Audeh et al.
patent: 5516497 (1996-05-01), Speronello et al.
patent: 5520895 (1996-05-01), Sharma et al.
patent: 5552129 (1996-09-01), Farnos et al.
patent: 5589147 (1996-12-01), Farnos et al.
patent: 5776423 (1998-07-01), Feeley et al.
patent: 6276132 (2001-08-01), Kanesaka et al.
patent: 6514470 (2003-02-01), Ott et al.
patent: 2006/0159607 (2006-07-01), Ott
Byrne et al.., “Selective Catalytic Reduction of NOxUsing Zeolitic Catalysis For High Temperature Application,” , Catalysis Today, 13 (1992) 33-42.
Long et al., “Low Temperature Selective Catalytic Reduction (SCR) of NO with NH3Over Fe-Mn Based Catalysts,” Chem. Commun., 2002, 452-453.
Qi et al., “Low-Temperature SCR of NO with NH3Over USY-Supported Manganese Oxide-Based Catalysts.” Catalysis Letters vol. 87, No. 1-2, Apr. 2003.
Qi et al., “A Superior Catalyst For Low-Temperature NO Reduction with NH3.” Chem. Commun., 2003, 848-849.
Borkowsky Samuel L.
Los Alamos National Security LLC
Vanoy Timothy C.
LandOfFree
Catalyst and method for reduction of nitrogen oxides does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Catalyst and method for reduction of nitrogen oxides, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Catalyst and method for reduction of nitrogen oxides will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2790158