Compositions: coating or plastic – Coating or plastic compositions – Proteinaceous material containing
Patent
1980-09-18
1982-06-08
Poer, James
Compositions: coating or plastic
Coating or plastic compositions
Proteinaceous material containing
432 13, 432 14, 432 18, C04B 702
Patent
active
043337660
ABSTRACT:
A process for manufacturing calcium silicate and/or aluminate based products, such as Portland cement or aluminous cements. The raw material subjected to a first heating step in which it is heated in a preheater-decarbonator and/or a rotating kiln to a temperature less than that at which impurities, such as alkalines, chlorine and sulfur, are volatized. The heated raw material is then subjected to a second heating step in the presence of a reducing gas, preferably in a plasma furnace, the raw material being heated to a temperature higher than the temperature at which the impurities are volatilized, as for example above 1950.degree. C., and more than 80% of the material is in fusion, whereupon the material is cooled to produce the clinkers of improved quality and/or with lower energy consumption. An important feature of the invention is the utilization of the gases generated during the second heating step and during cooling to implement heating of the raw material. It is equally important, however, that the gases generated during the second heating step are not utilized to heat the raw materials unless such gases are first purified.
REFERENCES:
patent: 4126471 (1978-11-01), Herchenbach et al.
patent: 4191586 (1980-03-01), Dambrine
Bonet Claude
Delmas Robert
Moisset Jacques
Petit Alain
Rouanet Alain
Lafarge
Poer James
LandOfFree
Calcium process for manufacturing silicate and/or aluminate base does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Calcium process for manufacturing silicate and/or aluminate base, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Calcium process for manufacturing silicate and/or aluminate base will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-551808