ABSTRACT:
FIELD OF THE INVENTION
The invention relates to a burner membrane comprising heat-resistant stainless steel fibres.
BACKGROUND OF THE INVENTION
A number of types of burner membranes composed of heat-resistant stainless steel fibres are already known, comprising, for example, a sintered metal fibre web or a knitted metal fibre structure.
However, the use of a sintered web as a burner membrane, as described in European patent EP 0157432 (priority date:1984), displays a few drawbacks.
For example, the porosity of a sintered metal fibre web as such is often insufficiently homogeneous, so that the flow of gas through the membrane is not sufficiently uniform. The axial temperature gradient that is established through the burner membrane during burning results in a non-homogeneous thermal expansion and mechanical [stresses]. After a number of heating and cooling cycles, these stresses can lead to cracks or fissures in the membrane. These drawbacks can in part be dealt with by providing the surface of the burner membrane with a regular pattern of perforations or a grid-like pattern of grooves, such as described respectively in PCT patent application WO 93/18342 (priority date: 1992) and European patent EP 0390255 (priority date:1989), both submitted by the applicant.
Furthermore, a burner membrane composed of a sintered metal fibre web is deformable only to a limited extent, which also constitutes a significant drawback.
Knitted membranes composed of metal fibres, as described in PCT patent application WO 97/04152 (priority date:1995) of the applicant, deal to a significant extent with the aforementioned drawbacks, but their construction is relatively complicated.
SUMMARY OF THE INVENTION
It is the object of the invention to deal with the drawbacks of the aforementioned types of burner membranes and to provide a metal fibre burner membrane that possesses a high and nearly homogeneous porosity, and that is to a large extent deformable. Moreover, the membrane possesses a considerable mechanical cohesion and strength, and can be fabricated in an inexpensive and simple manner.
To this end, the invention provides a burner membrane comprising at least one layer consisting of a compressed, needled fibre web composed of heat-resistant stainless steel fibres. The porosity of the burner membrane is between 60% and 95%.
The heat-resistant stainless steel fibre bundles that are incorporated in the fibre web and that are composed, for example, of Fecralloy®, can be obtained by means of the technique of bundled drawing, as described in U.S. Pat. No. 3,379,000, or by shaving the rolled edge of a roll of metal foil, as described in U.S. Pat. No. 4,930,199, or directly from the melt, for example by extrusion, as described in U.S. Pat. No. 5,524,704.
With respect to the present invention, the better fibres are those obtained by shaving the rolled edge of a roll of metal foil, as described in U.S. Pat. No. 4,930,199. The reason is that they have not a round transversal cross-section, which allows them to be intertwined to a more coherent structure during the needling operation.
The steel fibres have an equivalent diameter of between 5 &mgr;m and 150 &mgr;m, by preference between 10 &mgr;m and 50 &mgr;m. The equivalent diameter is here defined as the diameter of an imaginary round fibre having the same cross-section as that of the real fibre in question.
Apart from this, steel wool can also be used to fabricate the fibre web.
The burner membrane according to the invention can be obtained by and the sintering step of the web can be avoided by:
a) providing a fibre web composed of heat-resistant stainless steel fibres, whether multi-layered or not;
b) needling the fibre web;
c) compressing the needled fibre web to the desired porosity, for example by means of a roller or press operation.
Compressing is done to give the desired stability to the membrane. The needled fibre web may be compressed to such a degree that cold weldings are just avoided.
A correspondingly formed burner membrane can be obtained by needling a flat, tubular, cylindrical or conical metal fibre web.
The burner membrane according to the invention has a nearly homogeneous porosity, which is between 60% and 95%, and by preference between 80% and 95%. This makes it possible to utilize large and uniform gas flows.
The weight of the burner membrane is between 400 g/m
2
and 4000 g/m
2
, and is by preference between 1000 g/m
2
and 2500 g/m
2
.
Needling or needle punching can be done by punching the web of metal fibres by means of a bed of needles. Due to this operation, the metal fibres are intertwined with one another, a fact which lends considerable mechanical cohesion and strength, yet does not impair the good deformability of the needled felt and yet does not lead to an unacceptable decrease in porosity. During the needling operation care must be taken not to punch twice or more times at the same spot, since this may decrease the homogeneity of the web. Moreover, the thermal expansion of the burner membrane can take place unhindered, and there is nearly no danger of cracks or fissures appearing.
A needled web of ceramic fibres for burners is known in the art, e.g. in U.S. Pat. No. 5,024,596 (priority date:1985). Needling of a web of ceramic fibres is done in order to avoid the use of a binder and to render the ceramic fibre web more pliable as a result of the avoiding of the binder. Having regard, however, to the brittleness of the ceramic fibres, the degree of compressing of a needled fibre web is very limited
In order to improve the homogeneity of the gas flow even further, the burner membrane according to the invention can be perforated in a regular pattern over at least a portion of its surface, for example by mechanical means or with the aid of laser techniques.
The web formation, needling, compressing and in some cases perforating can be carried out consecutively on a single production line, which makes the manufacture of the burner membrane relatively simple and inexpensive.
The burner membrane according to the invention can also be coated with substances that activate the oxidation of the fuel mixture.
In an alternative embodiment, the needled metal fibre web, whether multilayered or not, can be pressed in a cold isostatic manner such that a smooth surface is obtained on either one or both sides of the web. The principle of cold isostatic pressing is described in European patent EP 0329863 of the applicant.
Furthermore, in addition to a needled fibre web, another metal fibre network, such as a woven or knitted fabric, can also be incorporated into the burner membrane according to the invention.
REFERENCES:
patent: 3379000 (1968-04-01), Webber et al.
patent: 4290746 (1981-09-01), Smith
patent: 4930199 (1990-06-01), Yanagisawa
patent: 5024596 (1991-06-01), Smith
patent: 5088919 (1992-02-01), De Bruyne et al.
patent: 5165887 (1992-11-01), Ahmady
patent: 5380580 (1995-01-01), Rogers et al.
patent: 5524704 (1996-06-01), Stouvenot et al.
patent: 6249941 (2001-06-01), Krupnik et al.
patent: 0 157 432 (1985-02-01), None
patent: 0 157 432 (1985-02-01), None
patent: 0 329 863 (1988-11-01), None
patent: 0 329 863 (1988-11-01), None
patent: 0329863 (1988-11-01), None
patent: 0 348 993 (1989-06-01), None
patent: 0 390 255 (1990-03-01), None
patent: 0 390 255 (1990-03-01), None
patent: WO 93/18342 (1993-09-01), None
patent: WO 97/04152 (1997-06-01), None
Dewaegheneire Gabriel
Lambert Eddy
Caldarola Glenn
Foley & Lardner
N. V. Bekaert S.A.
Wachtel Alexis
LandOfFree
Burner membrane comprising a needled metal fibre web does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Burner membrane comprising a needled metal fibre web, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Burner membrane comprising a needled metal fibre web will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3121189