Catalyst – solid sorbent – or support therefor: product or process – Catalyst or precursor therefor – Halogen or compound containing same
Reexamination Certificate
2002-03-28
2003-11-18
Wood, Elizabeth D. (Department: 1755)
Catalyst, solid sorbent, or support therefor: product or process
Catalyst or precursor therefor
Halogen or compound containing same
C502S305000, C502S313000, C502S315000, C502S224000, C502S229000
Reexamination Certificate
active
06649560
ABSTRACT:
The present invention relates to the field of the fluorination of halogenated hydrocarbons and more particularly to the preparation of bulk catalysts based on chromium and on nickel which can be used for this purpose.
One of the various access routes to hydroalkanes, which are substitutes for CFCs (ChloroFluoroCarbons), is gas-phase fluorination with HF. For this, many catalysts are described in the literature and a good number of them are based on chromium. The change from CFCs to the substitutes has led to research into the catalysts in order to improve their performances, both from the viewpoint of activity and of selectivity.
First of all, studies have been carried out in order to improve the performances of chromium-based catalysts. Thus, Patent Application EP 514,932 claims, as fluorination catalyst, a chromium oxide with a high specific surface which, according to the authors, has a high activity and a long lifetime.
In the same way, work has been carried out in order to modify the performances of chromium-based catalysts by addition of doping agents or of cocatalysts. Thus, as regards mixed Ni—Cr catalysts, Patent FR 2,669,022 claims the synthesis of F134a (1,1,1,2-tetrafluoroethane) by gas-phase fluorination of F133a (1-chloro-2,2,2-trifluoroethane) over a catalyst based on derivatives of nickel and of chromium which are supported on more or less fluorinated aluminas, or even on aluminium fluoride. The presence of the support contributes certain characteristics to the catalyst, in particular a degree of strength. On the other hand, there is a risk, with the small amounts of active materials, of limiting the catalytic activity, or even the lifetime of the catalyst; in addition, the low contents of non-precious metals do not facilitate a profitable recovery of the spent catalysts.
Patent EP 546,883 describes the preparation of bulk catalysts based on chromium and on nickel by the sol-gel method in several stages, the first consisting in forming a mixed sol of chromium III and nickel II hydroxides. This technique, which starts with a mixture of the precursors of the chromium and of the nickel, is relatively lengthy and expensive to implement.
In Patent Application WO 93/25507, the preparation of catalysts based on chromium and on at least one derivative of a transition metal chosen from nickel, platinum and palladium is carried in various ways: impregnation of a support, coprecipitation, impregnation of a chromium derivative, and the like. No characteristic of the catalyst or of the support is provided in this document.
It has now been found that a mixed Ni—Cr catalyst which is particularly effective in the gas-phase fluorination by HF of saturated or olefinic halogenated hydrocarbons can be obtained by simple impregnation of a bulk chromium oxide, with a large specific surface and with a high pore volume, with a solution of a nickel derivative.
The subject of the invention is thus bulk catalysts based on chromium and on nickel which are obtained by impregnation of an amorphous chromium III oxide with a solution of a nickel derivative, characterized in that the bulk chromium oxide used exhibits a BET specific surface of greater than 150 m
2
/g, preferably of greater than 180 m
2
/g, and a pore volume (defined as the volume of the pores with a radius of less than 7.5 &mgr;m) of greater than 0.15 ml/g, preferably of greater than 0.18 ml/g.
A chromium III oxide with a BET specific surface greater than 150 m
2
/g can be synthesized by the various techniques known to the person skilled in the art. Mention may be made, as non-limiting example, of the calcination of a chromium III hydroxide precipitate, the formation of a chromium III hydroxide gel, followed by the calcination thereof, the reduction of chromium VI by an alcohol or another reducing agent, or the thermal decomposition of an oxidized derivative of chromium, such as CrO
3
and (NH
4
)
2
Cr
2
O
7
. It is preferable to use a chromium oxide obtained by calcination of a chromium III hydroxide or by reduction of chromium VI oxide. Commercial chromium III oxides may be suitable, provided that they have a suitable specific surface and a suitable porosity.
Chromium III oxide can be provided in various forms (pellets, extrudates, balls, and the like). The form used very clearly establishes the form of the final catalyst; it must therefore not be detrimentally affected by the impregnation stage. To achieve this, various additives (graphite, crystalline Cr
2
O
3
, and the like) can be added during the shaping operation, in order to improve the strength of the chromium particles.
Chromium III oxide is impregnated by means of an aqueous or alcoholic solution of a nickel precursor which can be a nickel II oxide, hydroxide, halide, oxyhalide, nitrate, sulphate or other compound which is soluble in aqueous or alcoholic medium. The preferred compound is nickel chloride.
The Ni/Cr atomic ratio in the final catalyst can vary between 0.01 and 1, preferably between 0.02 and 0.6. An atomic ratio of between 0.02 and 0.4 is particularly advantageous.
The impregnation of the chromium oxide can be carried out before the catalyst is shaped (impregnation of Cr
2
O
3
powder) or on chromium III oxide which has already been shaped (balls, pellets, extrudates, and the like). The latter technique is preferred when the form of the catalyst is not detrimentally affected by the impregnation stage. The impregnation can be carried out according to the various techniques known to the person skilled in the art (immersion, impregnation with a volume adjusted to the porosity of the catalyst, and the like). Impregnation adjusted to the pore volume of the catalyst is the preferred technique. The impregnation solution can be an aqueous solution or an alcoholic solution. When there is no solubility problem, the aqueous solution is preferred; the exothermicity due to the reduction by the alcohol of the surface chromium VI (always present at a low content in Cr
2
O3) is thus avoided.
In order to optimize the activity of the catalyst, it is advisable to subject it to a pretreatment with HF in the absence of organic compounds. As chromium III oxide and the nickel derivatives become fluorinated in the presence of HF, it is necessary to carry out this fluorination while controlling the exothermicity of the reaction, in order to prevent the catalyst from deteriorating (crystallization, deterioration of the balls, pellets or extrudates, and the like). A typical pretreatment (or activation) of the catalyst first comprises a drying stage under an inert gas (nitrogen, helium, or the like) or air at a temperature of between 100 and 350° C., followed by a stage of activation by HF. To control the exothermicity, the HF is, on the one hand, introduced at low temperature (150-200° C.) and, on the other hand, it is diluted in air or, preferably, in an inert gas. After the “exothermicity waves” due to the adsorption of HF on the catalyst have passed, the temperature is gradually increased, in order to reach 350-380° C. and to observe a stationary phase at this temperature. When the strength of the catalyst allows it, the latter can be activated as a stirred or fluidized bed; control of exothermicity is thus easier. In order to avoid any deterioration in the catalyst, it is recommended that a temperature of 400° C. should not be exceeded.
Another subject of the invention is the use of these bulk catalysts for the catalytic fluorination of saturated or olefinic halogenated hydrocarbons by HF in the gas phase.
The halogenated hydrocarbons capable of resulting in HCFCs (HydroChloroFluoroCarbons) or in HFCs (HydroFluoroCarbons) by gas-phase fluorination are compounds containing one or more carbon atoms which result in final products, or even in synthetic intermediates, containing one or more hydrogen atoms. Mention may be made, as non-limiting examples, in this category, of the following compounds: CH
2
Cl
2
, CH
2
ClF, CHCl
3
, CCl
2
═CHCl, CCl
2
═CCl
2
, CH
2
Cl—CF
3
, CHCl
2
—CF
3
, CHClF—CF
3
, CH
3
—CCl
3
, CH
3
—CCl
2
F, CH
3
—CClF
2
, C
3
F
6
, CCl
3
—CH
2
—CHCl
2
Lacroix Eric
Schirmann Jean-Pierre
Elf Atochem
Smith , Gambrell & Russell, LLP
Wood Elizabeth D.
LandOfFree
Bulk catalysts based on chromium and on nickel for the... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Bulk catalysts based on chromium and on nickel for the..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Bulk catalysts based on chromium and on nickel for the... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3128651