ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a brake unit including a brake disc of a material having a high thermal loading capacity and a brake pad that cooperates with it in tribological fashion.
RELATED TECHNOLOGY
Brake discs are described, for example, in German Patent Application Nos. 44 38 455 and 43 22 113. German Patent Application No. 43 22 113 describes a brake disc having a metal bearing member with layers of a material capable of withstanding high thermal stresses applied thereon. To prevent the brake pad from being damaged by excessive heating of this area, provision is made, on the one hand, for a metal filling in the ceramic to dissipate the heat acting on the metallic bearing member and, and the other hand, for a ventilated brake pad design.
It is, nevertheless, necessary that the friction member, i.e., the friction pad that cooperates in tribological fashion with the brake disc, be thermally stable. The lower specific thermal capacity and poorer thermal conductivity of ceramic in comparison to the higher thermal capacity of grey cast iron brake discs can cause considerable heat to be generated due to the frictional heat being released. The brake disc easily withstands these temperatures due to its temperature stability. However, a conventional brake pad would disintegrate.
Due to the high temperatures that arise in the area of contact with the brake pad, conventional, industrial brake pads having organic binding systems are, on the whole, not suited for use with brake discs of this kind. The organic binder decomposes in response to the observed temperatures, so that the pad wears away very quickly. Therefore, efforts are underway to develop new kinds of brake pads. Such a new kind of brake pad having a sintered-powder metal base is known from German Patent Application No. 197 11 830.5. It is costly, however.
SUMMARY OF THE INVENTION
Therefore, an object of the present invention is to provide a brake unit of the type including a brake disc of a material having a high thermal loading capacity and a brake pad that cooperates with it in tribological fashion, which combines a brake disc having a thermal load capacity with a suitable brake pad capable of withstanding thermal stresses in a way that enables conventional brake pads to be used as well.
The present invention provides a brake disc essentially made of a short-fiber reinforced ceramic material, whose thermal conductivity, in particular transversely to the disc surface, is at least 20 W/mK, preferably 30 to 45 W/mK, and by combining the brake disc with a brake pad having an organically bonded matrix.
The increased or more uniform thermal conductivity may be attributed to the use of short fibers, which may be oriented in any desired spatial direction.
The present invention represents an optimal pairing of brake disc and brake pad under conditions of an enhanced thermal load-bearing capacity on the part of the brake disc in light of a reasonably expected brake-pad service life, and in light of other tribological requirements, such as friction coefficient level and/or the temperature dependence of the friction coefficient.
The thermal conductivity may be adjusted in every brake disc direction. Initially preferred is an adjustment orthogonally to the disc surface. This ensures, particularly when working with ventilated brake discs, that the frictional heat being released is dissipated over the shortest path.
The thermal conductivity may also be set, however, in parallel with the disc surface. This distributes the frictional heat over the disc and prevents a concentrically disposed region of especially high temperatures from forming in the area of contact with the brake pad and from damaging the brake pad.
The thermal conductivity is calculated to ensure that observed temperatures, even when working with unventilated brake discs, do not rise substantially above about 500° celsius, or to ensure that the brake fluid is heated to levels below about 200° celsius. Preferred however, are ventilated brake discs, whose thermal conductivity is comparable to that of gray cast iron.
Due to the relatively high thermal conductivity of a brake disc according to the present invention, in particular transversely to the brake surface, the temperatures that arise in the area of contact with the brake pad are not substantially more than 500° celsius, in spite of the high stress the brake is subject to. Surprisingly, even commercial brake pads having organic binders can withstand these temperatures, at easily justifiable rates of wear. These generally known pads are usually used for gray cast iron brake discs, which, on the one hand, have a higher thermal conductivity than traditional ceramic and which, on the other hand, have a substantially lower thermal load-bearing capacity than ceramic. The fact that a conventional brake pad is able to be used in a manner that promises success even under the completely changed marginal conditions was not to be expected by one skilled in the art.
It is, however, beneficial for the thermal conductivity of the brake disc to be adjusted for the most part isotropically. The directionally dependent differences in the thermal conductivity should preferably be less than 40% in terms of the highest value. This prevents local temperature peaks from being able to form, which could damage the organically bonded friction pad and, thus, shorten its service life.
A brake disc according to the present invention is preferably a short-fiber reinforced C/SiC ceramic brake disc. This material is certainly known to one skilled in the art and is described, for example, in the German Patent Application No. 197 11 829.1. This material is extremely temperature-stable and can, nevertheless, be combined according to the present invention with a brake pad having an organically bonded matrix.
It is advantageous for a brake disc of the present invention to be made of short-fiber reinforced C/SiC ceramic having isotropically oriented short fibers. In one embodiment of the present invention, the brake disc is made of a short-fiber reinforced composite ceramic having highly heat-resistant fibers, which are bonded by reaction to a silicon-based matrix, short fiber bundles being embedded as randomly distributed bundles in the matrix. The short-fiber bundles are made of bunched individual fiber filaments, with the individual filaments being mostly maintained. They are surrounded at least in their edge area by a coating of carbon, which has reacted completely or partially with the matrix material.
The thermal conductivity or the isotropic quality may be adjusted by varying the homogeneity of the material. A multidirectional, random arrangement of the short-fiber bundles to bridge over the regions of less thermal conductivity, above all at phase boundaries, is desirable. In this manner, thermal conductivity values comparable to those of gray cast iron are obtained. The more pores and/or pure silicon is contained in the material, the lower the thermal conductivity is. The existence of air-filled pores likewise generally degrades thermal conductivity. If many silicon-filled pores are present, the result can be structural anomalies and cracking.
Isotropy is achieved by using short carbon fiber bundles, as described in German Patent Application No. 197 11 829, and by homogeneously mixing the parent substances. The fiber bundles are present in any desired orientation, thus in an isotropic arrangement.
A brake disc according to the present invention preferably contains about 35-45% by volume of fibers, about 40-50% by volume of silicon carbide (from converted graphite material of the C/C member subjected to the siliconization), and maximally about 15% by volume of free silicon. There are preferably no air-filled pores.
A brake pad according to the present invention is advantageously provided with a rear metallic plate. The combination of an organic brake pad, having a high thermal conductivity, with a rear ceramic plate is likewise possible and enhances the stability and load-bearing capacity of a brake unit according to the
Naumann Emil
Rebstock Kolja
Daimler-Benz Aktiengesellschaft
Graham Matthew C.
Kenyon & Kenyon
LandOfFree
Brake unit including brake disc and brake lining does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Brake unit including brake disc and brake lining, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Brake unit including brake disc and brake lining will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2518031