Bis-Schiff base ligand-containing mono-metallocene olefin...

Details Bis-Schiff base ligand-containing mono-metallocene olefin... Bis-Schiff base ligand-containing mono-metallocene olefin...

2002-09-27

2004-06-08

Rabago, Roberto (Department: 1713)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

Polymers from only ethylenic monomers or processes of...

C526S161000, C526S172000, C526S943000, C502S103000, C502S104000, C502S117000, C502S155000, C502S167000, C556S034000, C556S052000, C556S054000, C556S056000

Reexamination Certificate

active

06747105

ABSTRACT:

BACKGROUND OF THE INVENTION
The present invention relates to an olefin polymerization catalyst, its preparation process and application thereof In particular this invention relates to a bis-Schiff base ligand-containing transition metal compound, its preparation process and a process for homopolymerization or copolymerization of olefins with said compound as a major catalyst.
In the field of olefin polymerization, non-metallocene olefin polymerization catalysts exhibit certain advantages in some aspects over metallocene olefin polymerization catalysts, e.g., a much wider range of the ligand for synthesizing the catalyst, capability of some complexes to catalyze the copolymerization of polar monomers with &agr;-olefins, capability to catalyze the oligomerization of ethylene by changing the substitution group of the ligand, and so on. V. C. Gibson (Angew. Chem, Int. Ed. 1999, 38 p428) comprehensively summarizes various catalytic systems for non-metallocene olefin polymerization, wherein the active center metal involves groups IIIB-XIB transition metals. CN1225645A discloses a post-transition metal catalyst for olefin polymerization formed by a bidentate ligand such as an imide and a central metal being selected from Groups IIIB-XIIB metals.
EP0874005A discloses a bis-schiff base [N,O]-coordinated olefin polymerization catalytic system for the first time, wherein the metal element M is selected from IIIB-XIB metals. The disclosed non-bridge complex has the following structural formula;
wherein R
1
is selected from hydrogen, halogen, and alkyl. This patent application especially points out that the substitution group adjacent to the hydroxyl is preferably halogen or C
3
-C
20
branched alkyl if there is no substituent or the substituent which is a smaller alkyl such as methyl, ethyl and the like at this position, the polymerization activity of the system is low. This type of catalyst has major advantages of providing a same catalytic activity compared to that of an ordinary metallocene for the catalytic polymerization of olefins, and resulting in much higher molecular weight of the obtained polyethylene with broader range of distribution of the molecular weight as compared to the polyethylene derived with a metallocene catalyst. The shortcomings of such catalyst exists in that the copolymerization property is poor, and when it is used for the copolymerization of ethylene with &agr;-olefins, the molecular weight decreases to a large extent and the insertion rate of the comonomer reached only less than 4 mol %.
An outstanding merit of the metallocene catalyst system lies in the possession of a very high copolymerization power, which is favorable to obtaining low-density polyethylene plastomer, even elastomer. However, the fatal weakness of the metallocene catalyst is that the molecular weight of the polymer drops so sharply along with the increasing insertion rate of the comonomer when the catalyst catalyzes the copolymerization of ethylene with &agr;-olefins with a result that it is hard to simultaneously obtain polyethylene with both a high molecular weight and a high content of comonomer (high branching degree).
SUMMARY OF THE INVENTION
The object of the present invention is to provide a bis-Schiff base ligand-containing olefin polymerization catalyst and its preparation process.
Another object of the present invention is to provide a process for conducting olefin polymerization by using the aforesaid catalyst
It has been found out through research work that the introduction of a cyclopentadienyl ligand into a bis-Schiff base ligand transition metal catalyst can yield a polyolefin product with a high molecular weight and a high content of the comonomer in the copolmerization of &agr;-olefins. If such a catalyst is used for the copolymerization of ethylene with hexene, the molecular weight Mw of the polymerization product can attain to 570,000 when the insertion rate of hexene is 4.34 mol %.
DETAILED DESCRIPTION OF THE INVENTION
The olefin polymerization catalyst provided by the present invention has the following structural formula (I),
wherein R
1
is selected from the group consisting of hydrogen, C
1
-C
12
alkly, C
1
-C
12
alkoxy, and C
6
-C
12
aryls, R
2
and R
2
′ are respectively selected from hydrogen and C
1
-C
4
alkyl, R
3
is selected from the group consisting of hydrogen, C
1
-C
12
alkyl, C
1
-C
12
alkoxy, and C
6
-C
12
aryl, and M is selected from Ti, Zr and Hf.
R
1
in formula (I) is a substitution group on the benzene ring of salicylidene; preferably hydrogen or C
1
-C
6
alkyl such as methyl, ethyl, propyl, n-butyl, iso-butyl or tert-butyl. The substitution can be at 3-6 position, preferably 3 or 5 position, i.e. the substitution is at the para- or ortho-position of the hydroxyl.
R
2
and R
2
′ in formula (I) are substitution groups on the aniline ring, preferably hydrogen, methyl ethyl, propyl, iso-propyl, n-butyl, tert-butyl or iso-butyl. R
2
and R
2
′ can be identical or different. If they are identical, it is preferred that both are hydrogen, methyl, ethyl, tert-butyl or iso-propyl. If they are different, it is preferred that one substitution group is hydrogen or a C
1
-C
4
alkyl, and the other is a C
1
-C
4
alkyl, e.g., one is hydrogen and the other is methyl, ethyl, or propyl.
R
3
is a substitution group on the frame of cyclopentadiene, preferably hydrogen or a C
1
-C
4
alkyl such as methyl, ethyl, and more preferably hydrogen.
M is a transition metal, preferably Ti, or Zr.
The process for preparing the catalyst of the present invention comprises the following steps:
(1) Reacting a Schiff base ligand compound shown by formula (II) with an alkyl alkali metal compound in an organic medium to form an alkali metal salt of a Schiff base ligand. R
1
in formula (II) is selected from the group consisting of hydrogen, C
1
-C
12
alkyl, C
1
-C
12
alkoxy, and C
6
-C
12
aryl, and R
2
and R
2
′ are selected from hydrogen and C
1
-C
4
alkyl respectively
(2) Reacting the alkali metal salt of the Schiff base ligand with a cyclopentadienyl metal chloride having a formula of CpMCl
3
in an organic medium, removing the solvent, washing the residue with an organic solvent, filtering the resultant, and recrystallizing the filtrate. In said CpMCl
3
, M is Ti, Zr, or Hf, Cp is a mono-substituted cyclopentadienyl, and substitution group R
3
is selected from the group consisting of hydrogen, C
1
-C
12
alkyl, C
1
-C
12
alkoxy, and C
6
-C
12
aryl.
Step (1) relates to the reaction for preparing the alkali metal salt of the ligand, wherein the suitable reaction temperature is −78-25° C. and in particular, a low temperature should be maintained at the beginning of the reaction to prevent the rapid elevation of the reaction temperature and the formation of byproducts. Among said alkyl alkali metal compounds, alkyl lithium is preferred with butyl lithium being more preferred. In the synthesis of the ligand salt, the molar ratio of the ligand to the alkyl metal compound is 0.1-2.0:1 and the reaction time is preferably 0.1-24 hours.
The suitable temperature in reaction step (2) is −78-25° C., and the reaction time is preferably 0.5-24 hours. The molar ratio of the alkali metal salt of the Schiff base ligand to CpMCl
3
in the reaction is 1.0-2.0:1. Among the CpMCl
3
compounds, Ti is preferred for M and cyclopentadienyl is preferred for Cp.
The organic medium used in aforesaid steps (1) and (2) is selected from tetrahydrofuran and ethyl ether, preferably tetrahydrofuran. The organic solvent used for washing in step (2) is selected from the group consisting of ethyl ether, benzene, toluene, n-hexane, petroleum ether, and the mixture thereof.
The process for preparing the complex of formula (II) in step (1) comprises dehydrating condensation of the corresponding aniline compound of formula (II), such as aniline, 2,6-di-isopropyl aniline with the corresponding salicylal compound in equal mole ratio in ethanol at the reflux temperature for 0.1-10 hours; after the reaction, cooling the resultant to the room temperature, filtra

Affiliated with

Also associated with

Rating

Bis-Schiff base ligand-containing mono-metallocene olefin... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Bis-Schiff base ligand-containing mono-metallocene olefin..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Bis-Schiff base ligand-containing mono-metallocene olefin... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3339842