Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – At least one aryl ring which is part of a fused or bridged...
Reexamination Certificate
2001-03-24
2002-10-15
Yoon, Tae H. (Department: 1714)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
At least one aryl ring which is part of a fused or bridged...
C524S285000, C560S120000, C528S486000
Reexamination Certificate
active
06465551
ABSTRACT:
Field of the Invention
This invention relates to compounds and compositions comprising specific metal salts of bicyclo[2.2.1 ]heptane dicarboxylate salts in order to provide highly desirable properties within thermoplastic articles. The inventive salts and derivatives thereof are useful as nucleating and/or clarifying agents for such thermoplastics. Such compounds provide excellent crystallization temperatures, stiffness, and calcium stearate compatibility within target thermoplastics. Also, such compounds exhibit desirable migratory properties within thermoplastic articles and low hygroscopicity and therefore excellent shelf stability as powdered or granular formulations. Thermoplastic additive compositions and methods of producing thermoplastics with such compounds are also contemplated within this invention.
BACKGROUND OF THE PRIOR ART
All U.S. patents cited below are herein entirely incorporated by reference.
As used herein, the term “thermoplastic” is intended to mean a polymeric material that will melt upon exposure to sufficient heat but will retain its solidified state, but not prior shape without use of a mold or like article, upon sufficient cooling. Specifically, as well, such a term is intended solely to encompass polymers meeting such a broad definition that also exhibit either crystalline or semi-crystalline morphology upon cooling after melt-formation through the use of the aforementioned mold or like article. Particular types of polymers contemplated within such a definition include, without limitation, polyolefins (such as polyethylene, polypropylene, polybutylene, and any combination thereof), polyamides (such as nylon), polyurethanes, polyester (such as polyethylene terephthalate), and the like (as well as any combinations thereof).
Thermoplastics have been utilized in a variety of end-use applications, including storage containers, medical devices, food packages, plastic tubes and pipes, shelving units, and the like. Such base compositions, however, must exhibit certain physical characteristics in order to permit widespread use. Specifically within polyolefins, for example, uniformity in arrangement of crystals upon crystallization is a necessity to provide an effective, durable, and versatile polyolefin article. In order to achieve such desirable physical properties, it has been known that certain compounds and compositions provide nucleation sites for polyolefin crystal growth during molding or fabrication. Generally, compositions containing such nucleating compounds crystallize at a much faster rate than un-nucleated polyolefin. Such crystallization at higher temperatures results in reduced fabrication cycle times and a variety of improvements in physical properties, such as, as one example, stiffness.
Such compounds and compositions that provide faster and or higher polymer crystallization temperatures are thus popularly known as nucleators. Such compounds are, as their name suggests, utilized to provide nucleation sites for crystal growth during cooling of a thermoplastic molten formulation. Generally, the presence of such nucleation sites results in a larger number of smaller crystals. As a result of the smaller crystals formed therein, clarification of the target thermoplastic may also be achieved, although excellent clarity is not always a result. The more uniform, and preferably smaller, the crystal size, the less light is scattered. In such a manner, the clarity of the thermoplastic article itself can be improved. Thus, thermoplastic nucleator compounds are very important to the thermoplastic industry in order to provide enhanced clarity, physical properties and/or faster processing.
As an example of one type of nucleator, dibenzylidene sorbitol compounds are common nucleator compounds, particularly for polypropylene end products. Compounds such as 1,3-O-2,4-bis(3,4-dimethylbenzylidene) sorbitol (hereinafter DMDBS), available from Milliken Chemical under the trade name Millad® 3988, provide excellent nucleation characteristics for target polypropylenes and other polyolefins. Other well known compounds include sodium benzoate, sodium 2,2′-methylene-bis-(4,6-di-tert-butylphenyl) phosphate (from Asahi Denka Kogyo K.K., known as NA-11), talc, and the like. Such compounds all impart high polyolefin crystallization temperatures; however, each also exhibits its own drawback for large-scale industrial applications.
Other acetals of sorbitol and xylitol are typical nucleators for polyolefins and other thermoplastics as well. Dibenzylidene sorbitol (DBS) was first disclosed in U.S. Pat. No. 4,016,118 by Hamada, et al. as an effective nucleating and clarifying agents for polyolefin. Since then, large number of acetals of sorbitol and xylitol have been disclosed. Representative US patents include: Kawai, et al., U.S. Pat. No. 4,314,039 on di(alkylbenzylidene) sorbitols; Mahaffey, Jr., U.S. Pat. No. 4,371,645 on di-acetals of sorbitol having at least one chlorine or bromine substituent; Kobayashi, et al., U.S. Pat. No. 4,532,280 on di(methyl or ethyl substituted benzylidene) sorbitol; Rekers, U.S. Pat. No. 5,049,605 on bis(3,4-dialkylbenzylidene) sorbitols including substituents forming a carbocyclic ring.
Another example of the effective nucleating agents are the metal salts of organic acids. Wijga in U.S. Pat. Nos. 3,207,735, 3,207,736, and 3,207,738, and Wales in U.S. Pat. Nos. 3,207,737 and 3,207,739, all patented Sept. 21, 1966, suggest that aliphatic, cycloaliphatic, and aromatic carboxylic, dicarboxylic or higher polycarboxylic acids, corresponding anhydrides and metal salts are effective nucleating agents for polyolefin. They further state that benzoic acid type compounds, in particular sodium benzoate, are the best embodiment of the nucleating agents.
Another class of nucleating agents, alluded to above, was suggested by Nakahara, et al. in U.S. Pat. No. 4,463,113, in which cyclic bis-phenol phosphates was disclosed as nucleating and clarifying agents for polyolefin resins. Kimura, et al. then suggests in U.S. Pat. No. 5,342,868 that the addition of an alkali metal carboxylate to basic polyvalent metal salt of cyclic organophosphoric ester can further improve the clarification effects of such additives. Compounds that are based upon this technologies are marketed under the trade name NA-11 and NA-21.
Furthermore, a certain class of bicyclic compounds, such as bicyclic dicarboxylic acid and salts, have been taught as polyolefin nucleating agents as well within Patent Cooperation Treaty Application WO 98/29494, to Minnesota Mining and Manufacturing. The best working example of this technology is embodied in disodium bicyclo[2.2.1]heptene dicarboxylate and formulations with such compounds.
Such compounds all impart relatively high polyolefin crystallization temperatures; however, each also exhibits its own drawback for large-scale industrial applications.
For example, of great interest is the compatibility of such compounds with different additives widely used within typical polyolefin (e.g., polypropylene, polyethylene, and the like) plastic articles. For instance, calcium stearate is a very popular acid neutralizer present within typical polypropylene formulations to protect the end product from catalyst residue attack. Unfortunately, most of the nucleator compounds noted above exhibit deleterious reactions with such compounds within polyolefin articles. For sodium, and other like metal ions, it appears that the calcium ion from the stearate transfers positions with the sodium ions of the nucleating agents, rendering the nucleating agents ineffective for their intended function. As a result, such compounds sometimes exhibit unwanted plate-out characteristics and overall reduced nucleation performance (as measured, for example) by a decrease in crystallization temperature during and after polyolefin processing. Other processing problems are evident with such compounds as well.
Other problems encountered with the standard nucleators noted above include inconsistent nucleation due to dispersion problems, resulting in stiffness a
Dotson Darin L.
Zhao Xiaodong Edward
Milliken & Company
Moyer Terry T.
Parks William S.
Yoon Tae H.
LandOfFree
Bicyclo[2.2.1]heptane dicarboxylate salts as... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Bicyclo[2.2.1]heptane dicarboxylate salts as..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Bicyclo[2.2.1]heptane dicarboxylate salts as... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2957227