Stock material or miscellaneous articles – Coated or structually defined flake – particle – cell – strand,... – Rod – strand – filament or fiber
Reexamination Certificate
1999-12-07
2004-01-20
Kelly, Cynthia H. (Department: 1774)
Stock material or miscellaneous articles
Coated or structually defined flake, particle, cell, strand,...
Rod, strand, filament or fiber
C428S375000, C428S379000, C174S1100SR, C174S11000P, C174S1200SR
Reexamination Certificate
active
06680120
ABSTRACT:
This application is based on and claims the benefit of German Patent Application No. 19903137.1 filed Jan. 27, 1999, which is incorporated by reference herein.
BACKGROUND OF THE INVENTION
The invention relates to a baked enamel, particularly for coating a wire, with a thermoplastic polyamide. The invention is further directed to a wire coated with such an enamel.
Baked enamels can be applied in their liquid state to the surface of substrates and can be bonded through heating after curing. Of particular significance are baked enamel wires comprising an electrical conductor and a topcoat of a baked enamel between which there is typically one or several electrically insulating coating layers. Baked enamel wires are used, in particular, in the production of coils, e.g., as windings for motors, electromagnets or deflector coils for display screens. The formed windings are bonded together by heating with the aid of the baked enamel coat so as to melt them into a mechanically solid composite.
Prior art baked enamel consists of a thermoplastic polymer that is dissolved in a solvent for application to the substrate. After the enamel has been applied, the substrate generally passes through an oven for drying. Usually, the baked enamel is applied in layers in several passes and subsequently dried after each.
U.S. Pat. No. 4,420,535 describes such as baked enamel. Its basis is an aromatic-aliphatic random copolyamide with the structural unit:
AL is the divalent hydrocarbon group of an unsubstituted aliphatic dicarboxylic acid with preferably 6 to 36 carbon atoms. As a rule, AL is (CH
2
)
x
, whereby x is from 4 to 34, preferably 6 to 12. Alternatively, AL can be the hydrocarbon group of an unsaturated dicarboxylic acid. R is tolyl phenyl or
whereby F is 0, CH
2
or SO
2
. It is also feasible that at least a portion of R is cycloaliphatic, e.g., cyclohexene. Ar is p-phenyl, y is between 35% and 80%, preferably approximately 65%, z is between 65% and 20%, preferably approximately 35% of the structural units. The copolyamide is produced in a manner known in the art, e.g., by reacting dicarboxylic acids with diisocyanates and/or diamines in a solvent, e.g., N-methyl-2-pyrrolidone (NMP). The polyamide as a baked enamel is typically also applied in an amide-based solvent such as NMP or a mixture of NMP and aromatic hydrocarbons.
Wires coated with such baked enamels have proven to be reliable for the stator windings of electric motors. They have proven to be inadequate for rotor windings, however, since the coatings tend to soften at elevated temperatures. Corresponding coils are not sufficiently stable at operating temperatures that in part exceed 155° C. and are subject to the centrifugal forces of motors whose speeds frequently range to around 10,000 rpm. In the prior art, the rotors of electric motors are therefore typically impregnated with a liquid thermosetting plastic, which subsequently cures. However, this procedure is complex compared to the bonding of baked enamel coated wires and is furthermore connected with the emission of hazardous substances.
SUMMARY OF THE INVENTION
It is therefore an object of the invention to develop a baked enamel, which is stable under load even at elevated temperatures.
This object is attained by the invention in that the enamel comprises a cross-linking agent that causes chemical cross-linking of the thermoplastic polymer under the action of heat, whereby the cross-linking agent comprises a polyvalent alcohol, a polyisocyanate as well as a polyol.
The chemical cross-linking of the thermoplastic polyamide, which forms the basis of the baked enamel, causes its resoftening temperature to increase significantly. It is possible, in particular, that the resoftening temperature is higher than the baking temperature for the enamel. As a consequence, the baked enamel's mechanical stability under load is maintained even at temperatures in the range of the baking temperature, while prior art baked enamels basically soften at such temperatures.
Of decisive significance is the fact that the cross-linking agent does not react, or at most reacts only partly, when the baked enamel is applied and cured and, particularly, when the solvent is expelled in an oven. Otherwise the resoftening of the baked enamel, which is required for bonding to the substrates, is impeded. The proportion of the cross-linking agent in the baked enamel is advantageously low. Preferred is a proportion of up to approximately 30 percent by weight, particularly 20 percent by weight, in relation to the thermoplastic polyamide.
A particular advantage of the baked enamel according to the invention is that its application and drying properties do not significantly differ from those of conventional baked enamels. In particular, conventional coating machines and ovens can be used for the production of baked enamel wires. Furthermore, the coatings exhibit good coating properties at comparable costs. The improved stability at temperatures above 150° C. makes it possible for the first time to use baked enamels to stabilize rotor windings.
The cross-linking agent comprises mutually reactive monomers of which at least one monomer is capable of reacting with the thermoplastic polyamide. The monomers react with each other and with the thermoplastic polyamide under the action of heat at the baking temperature of the enamel. Preferably, at least one of the monomers is an educt of the thermoplastic polyamide or reacts to one of its structural units during cross-linking. To facilitate processing, it is proposed that the cross-linking agent contain a solvent for the monomers and the thermoplastic polyamide.
After the baked enamel has been applied to the substrate it is typically dried in an oven for a few seconds at a temperature of between approximately 300° and 400° C. To make it possible to continue to use conventional ovens, it is advantageous if the cross-linking time of the cross-linking agent at the drying temperature is long compared to the drying time of the baked enamel.
Polyamides have proven to be suitable for the thermoplastic polymers, particularly copolyamides as described in the introduction. For their production, a mixture of diisocyanates is preferably used in which the molar ratio of toluene diisocyanate (TDI) to 4,4′ methylene di(phenyl isocyanate) (MDI) is between 50:50 and 100:0, preferably around 60:40. A particular advantage of polyamide-based baked enamels is their good chemical stability, particularly their low solubility in solvents such as gasoline and oil.
Particularly high stability of the baked enamel at elevated temperatures is obtained if the polyamide is constituted of aromatic and aliphatic structural units as described above. Particularly molar ratios of aliphatic to aromatic structural units of from 60:40 to 50:50 mol percent, preferably about 56:44 mol percent have proven successful. While prior art copolyamides exhibit a significant decrease in heat resistance at these mixing ratios compared to the maximum obtainable value, cross-linked polymers according to the invention show increased heat resistance at this ratio. But even the heat resistance of prior art copolyamides with different ratios can be increased by cross-linkage according to the invention.
A preferred cross-linking agent, particularly for polyamides, comprises a polyvalent alcohol. Divalent alcohols have proven successful, particularly propylene glycol or dipropylene glycol
HO—CH(CH
3
)—CH
2
—O—CH
2
—CH(CH
3
)—OH.
Furthermore, the cross-linking agent comprises a polyisocyanate, usable also, for example, as an educt of a polyamide.
Advantageously, the baked enamel is a mixture of at least one thermoplastic polymer, at least one cross-linking agent and one or several solvents. As solvents for copolyamide-based baked enamels, NMP or mixtures of NMP and aromatic hydrocarbons, e.g., cresol or xylene, have proven successful. Such a mixture can be produced as a homogenous storable liquid.
The described baked enamel is suitable for coating any type of substrate to be bonded under the action of heat. However, i
Boockmann Gerhard
Nagel Rolf
Preux Laurent
Gray J. M.
Kelly Cynthia H.
Nexans
Sughrue & Mion, PLLC
LandOfFree
Baked enamel does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Baked enamel, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Baked enamel will most certainly appreciate the feedback.