ABSTRACT:
BACKGROUND
Long wavelength vertical cavity surface emitting lasers (VCSELs) are attractive for long reach optical communication applications. Fabrication of long wavelength VCSELs incorporating well-developed AlAs/GaAs distributed Bragg reflectors (DBRs) is achieved by growing highly strained InGaAsN active regions on GaAs. Long wavelength VCSEL structures include structures where InGaAsN active regions are sandwiched between a first and second cladding region of AlGaAs/GaAs or InGaP/GaAs and top and bottom AlGaAs/GaAs DBR mirror layers.
Research by Kawaguchi et al. in Electronics Letters, 36, 2000, 1776 indicates that the material quality of metal-organic chemical vapor deposition (MOCVD) InGaAsN is severely degraded if the InGaAsN quantum well active layer is grown directly on the AlGaAs/GaAs DBR and lower cladding layers. To achieve acceptable material quality for the quantum well active layer, two separate reactors are used to grow the wafers for 1.3 &mgr;m wavelength VCSELs with InGaAsN quantum well active layers. A first reactor is used to grow the AlGaAs/GaAs DBR and lower cladding layers. Subsequently, the wafer is transferred to a second reactor for the growth of InGaAsN quantum well active layers, the top cladding layer and the top DBR mirror layers. These long wavelength InGaAsN VCSELs have “symmetric” structures where both the top and bottom cladding layers have the same composition. Sato et al. in Electronics Letters, 36, 2000, 2018 disclose an “asymmetric” VCSEL structure grown in a two reactor MOCVD process where a GaInP layer functions as an etch stop.
SUMMARY OF INVENTION
The use of an InGaAsN quantum well active layer allows VCSEL operation in the important 1300 nm or longer wavelength regime which is of interest for telecommunications and Internet infrastructure applications. In accordance with the invention, an asymmetric InGaAsN VCSEL structure may be made which allows all growth steps to be performed in the same metal-organic chemical vapor deposition (MOCVD) reactor.
In the asymmetric VCSEL structure, the first AlGaAs/GaAs DBR mirror layer is followed by growth of a sufficiently thick nitrogen or nitrogen and phosphorus containing layer such as GaAsN, InGaAsPN, GaAsPN, GaAsN, AlGaAsN, InGaPN, or similar compositions to improve growth of the InGaAsN quantum well active layer by serving to getter Al while not interrupting the MOCVD growth process. The top cladding layer may be AlGaAs to provide for higher band offset resulting in better electron confinement than is provided by a nitrogen or phosphorus containing cladding layer. However, AlGaAs requires a more complicated growth structure and typically GaAs is used for the top cladding layer. Instead of using a C-doped GaAs contact layer, a reverse-biased tunnel junction can be used to form the p-contact to reduce resistance and optical losses.
Using an asymmetric InGaAsN VCSEL structure results in the InGaAsN quantum well active layer having a quality that is comparable to that achieved by the conventional two reactor MOCVD process while providing good laser performance along with lower production costs by using a single reactor MOCVD process.
REFERENCES:
patent: 50934 (1865-11-01), Choquetta et al.
patent: 5583351 (1996-12-01), Brown et al.
patent: 5710439 (1998-01-01), Ohkubo
patent: 5903586 (1999-05-01), Ramdani et al.
patent: 5912913 (1999-06-01), Kondow et al.
patent: 5978398 (1999-11-01), Ramdani et al.
patent: 6015979 (2000-01-01), Sugiura et al.
patent: 6049556 (2000-04-01), Sato
patent: 6207973 (2001-03-01), Sato et al.
patent: 6238944 (2001-05-01), Floyd
patent: 6304588 (2001-10-01), Chua et al.
patent: 6306672 (2001-10-01), Kim
patent: 6455340 (2002-09-01), Chua et al.
patent: 2001/0050934 (2001-12-01), Choquette et al.
patent: 2002/0034203 (2002-03-01), Shimizu et al.
patent: 2002/0105988 (2002-08-01), Park et al.
patent: 2003/0013224 (2003-01-01), Shimizu et al.
patent: 2003/0108075 (2003-06-01), Kim et al.
Kawaguchi et al., “Lasing Characteristics of Low-Threshold GaInNAs Laser Grown by Metalorganic Chemical Vapor Deposition”, Japan Journal of Applied Physics, vol. 40(2001) pp. 744-746, no month.
Kageyama et al., “High-Temperature Operation up to 170 Degrees C of GaInNAs-GaAs Quantum-Well Lasers Grown by Chemical Beam Epitaxy”, IEEE Photonics Technology Letters, vol. 12, No. 1, Jan. 2000, pp. 10-12.
Sato et al. “Continuous Wave Operation of 1.26um GaInNAs/GaAs Vertical-Cavity Surface-Emitting Lasers Grown by Metalorganic Chemical Vapour Deposition”, Electronic Letters, Nov. 23, 2000, vol. 36, No. 24, pp. 2018-2019.
Harris, J.S. Jr., “GaInNAs, a New Material for Long Wavelength VCSELs”, 10th Seoul Interlational Symposium on Physics of Semicondcutors and Application, Nov. 1-3, 2000, p. 1, no month.
Bour David P.
Chang Ying-Lan
Leary Michael H.
Takeuchi Tetsuya
Tan Michael R. T.
Vy Hung Tran
Wong Don
LandOfFree
Asymmetric InGaAsN vertical cavity surface emitting lasers does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Asymmetric InGaAsN vertical cavity surface emitting lasers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Asymmetric InGaAsN vertical cavity surface emitting lasers will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3340043