ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention pertains to devices comprising electron field emitters, in particular, field emitters containing carbon nanotubes.
2. Discussion of the Related Art
Electron field emitters are useful for a variety of applications including microwave-amplifiers and flat-panel, field-emission displays.
Microwave vacuum tube devices, such as power amplifiers, are essential components of many modern microwave systems including telecommunications, radar, electronic warfare, and navigation systems. While semiconductor microwave amplifiers are available, they generally lack the power capabilities required by most microwave systems. Microwave tube amplifiers, in contrast, provide microwave energy at much higher power levels. The higher power levels of tube devices are the result of the fact that electrons travel at a much higher velocity in a vacuum than in a semiconductor. The higher speed permits use of larger structures with the same transit time. Larger structures, in turn, permit greater power levels.
Microwave tube devices typically operate by introducing a beam of electrons into a region where the beam interacts with an input signal, and then deriving an output signal from the modulated electron beam. See, e.g., A. W. Scott,
Understanding Microwaves,
Ch. 12, John Wiley & Sons (1993), the disclosure of which is hereby incorporated by reference. Microwave tube devices include traveling wave tubes, gridded tubes, klystrons, cross-field amplifiers and gyrotrons. The usual source of electrons for microwave tube devices is a thermionic emission cathode, typically formed from tungsten cathodes, optionally coated with barium oxide or mixed with thorium oxide. The cathode is heated to a temperature around 1000° C. to produce thermionic electron emission on the order of amperes per square centimeter.
The requisite heating of thermionic cathodes causes a number of problems. Cathode lifetime is limited because key constituents of the cathode, such as barium oxide, evaporate under the high operating temperatures, and when the barium is depleted, the cathode (and hence the tube) no longer perform. Many traveling wave tubes (TWTs), for example, have operating lives of less than a year. Also, the need to raise the cathode to the operating temperature causes emission delays of up to several minutes, which is not acceptable for most commercial applications. In addition, the high temperature operation generally requires a peripheral cooling system, such as a fan, thereby increasing the size of the overall device or system. It would therefore be desirable to develop microwave tube devices that do not require such high temperature operation, e.g., cold cathode devices.
Another promising application of field emitters is thin, matrix-addressable, flat panel displays. See, for example,
Semiconductor International,
December 1991, p.46; C. A. Spindt et al.,
IEEE Transactions on Electron Devices,
Vol. 38, 2355 (1991); I. Brodie and C. A. Spindt,
Advances in Electronics and Electron Physics,
edited by P. W. Hawkes, Vol. 83, pp. 1 (1992); and J. A. Costellano, Handbook of Display Technology, Academic Press, 254 (1992); and U.S. Pat. Nos. 4,940,916; 5,129,850; 5,138,237 and 5,283,500, the disclosures of which are hereby incorporated by reference.
A variety of characteristics are known to be advantageous for cathode materials of field emission devices. The emission current is advantageously voltage controllable, with driver voltages in a range obtainable from “off the shelf” integrated circuits. For typical device dimensions (e.g. 1 &mgr;m gate-to-cathode spacing), a cathode that emits at fields of 25 &mgr;m or less is generally desirable for typical CMOS circuitry. The emitting current density is advantageously in the range of 1-10 mA/cm
2
for flat panel display applications and >100mA/cm
2
for microwave power amplifier applications. The emission characteristics are advantageously reproducible from one source to another and advantageously stable over a very long period of time (tens of thousands of hours). The emission fluctuations (noise) are advantageously small enough to avoid limiting device performance. The cathode is advantageously resistant to unwanted occurrences in the vacuum environment, such as ion bombardment, chemical reaction with residual gases, temperature extremes, and arcing. Finally, the cathode manufacturing is advantageously inexpensive, e.g. no highly critical processes and adaptable to a wide variety of applications.
Conventional field emission cathode materials are typically made of metal (such as Mo) or semiconductor material (such as Si) with tips of submicron size. While useful emission characteristics have been demonstrated for these materials, the control voltage required for emission is relatively high (around 100 V) because of their high work functions and relatively dull (i.e., insufficiently sharp) tips. This high voltage operation increases the damaging instabilities due to ion bombardment and surface diffusion on the emitter tips and necessitates high power densities to be supplied from an external source to produce the required emission current density. The fabrication of uniform sharp tips is difficult, tedious and expensive, especially over a large area. In addition, the vulnerability of these materials to conditions of a typical operating environment, e.g., ion bombardment, reaction with chemically active species, and temperature extremes, is of concern.
Carbon materials (diamond and carbon nanotubes) have recently emerged as potentially useful electron field emitters. Diamond offers advantages due to the negative or low electron affinity on its hydrogen-terminated surfaces, but the technological advances have been somewhat slow because of emission non-uniformity and the tendency for graphitization in diamond emitters at increased emission currents, e.g., above about 30 mA/cm
2
.
Carbon nanotubes feature a high aspect ratio (>1,000) and a small tip radii of curvature (~5-50 nm). These geometric characteristics, coupled with the high mechanical strength and chemical stability of the tubules, make carbon nanotubes attractive as electron field emitters. See, e.g., German patent No. 4,405,768; Rinzler et al.,
Science,
Vol. 269, 1550 (1995); De Heer et al.,
Science,
Vol. 270, 1179 (1995); Saito et al.,
Jpn. J. Appl. Phys.,
Vol. 37, L346 (1998); Wang et al.,
Appl. Phys. Lett.,
Vol. 70, 3308 (1997); Saito et al.,
Jpn. J. Appl.
Phys., Vol. 36, L1340 (1997); and Wang et al.,
Appl. Phys. Lett.,
Vol. 72, 2912 (1998), the disclosures of which are hereby incorporated by reference. However, carbon nanotubes are typically available in the form of needle-like or spaghetti-like powders which are not easily or conveniently incorporated into a field emitter device structure. And due to this random configuration, the electron emission capabilities are not fully utilized. In addition, adherence of thin film nanotubes to a conductive substrate is problematic because the nanotube material is usually free of dangling bonds and high energy sites, making chemical bonding to the substrate difficult.
Processes which allow relatively easy fabrication of adherent and stable carbon nanotube field emitter structures, advantageously providing a substantial number of nanotube ends oriented toward a single direction, are therefore desired.
SUMMARY OF THE INVENTION
The invention provides an improved process for fabricating carbon nanotube field emitter structures, in which the nanotubes protrude from a supporting base material to provide desired emission properties. The resulting emitter structures are useful in a variety of devices, including microwave vacuum tube devices and flat-panel, field-emission displays. To attain the protruding nanotube emitter structure, according to one embodiment of the invention (reflected in FIGS.
2
A-
2
F), nanotubes and a conductive material, e.g., metal particles, are mixed and consolidated into a compact, and the compact is then sectioned to expose a substantial number of nanotube ends (s
Jin Sung-ho
Kochanski Gregory Peter
Zhu Wei
Agere Systems Guardian Corp.
Gerike Matthew J.
Ramsey Kenneth J.
Rittman Scott J.
LandOfFree
Article comprising enhanced nanotube emitter structure and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Article comprising enhanced nanotube emitter structure and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Article comprising enhanced nanotube emitter structure and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2487641