Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
1999-10-07
2002-02-26
Henderson, Christopher (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C525S344000, C525S504000
Reexamination Certificate
active
06350818
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to organic polymers suitable for use in anti-reflective coatings on semiconductor devices, and methods for preparing them. More specifically, the polymers of the present invention can be used to form a layer which prevents the reflection of light from lower layers coated on a semiconductor chip when photolithography processes using short wavelength light sources, such as 248 nM (KrF) and 193 nm (ArF) wavelengths, are employed during the manufacture of 64M, 256M, 1G, 4G and 16G DRAM semiconductor devices. Anti-reflective coatings comprising polymers of the present invention also eliminate the standing wave effect when an ArF beam is used, and reflection/diffraction caused by changes in the thickness of the photoresist layer itself. The present invention also relates to an anti-reflective composition containing these polymers, alone or in combination with other light-absorbing compounds, and the anti-reflective coating formed from these compositions, as well as preparation methods therefor.
2. Description of the Prior Art
In photolithography processes for forming submicro-patterns during the manufacture of semiconductors, it is unavoidable to have reflective notching of the standing wave of the exposing radiation. This effect is due to the spectroscopic properties of the lower layers coated on the semiconductor wafer, changes in the photoresist layer and variations in the critical dimension (CD) due to diffracted and reflected light from the lower layer. Therefore, it has been suggested that a layer, called an anti-reflective coating, be introduced into the semiconductor device to prevent the reflection of light from the lower layers. This anti-reflective coating usually comprises an organic material that absorbs light in the wavelength range of the light beam source used in the lithography process.
Anti-reflective coatings are categorized into inorganic and organic anti-reflective coatings depending on the coating materials used, or into light-absorbing and light-interfering coatings depending on the mechanism.
An inorganic anti-reflective coating is used mainly in the process of submicro-pattern formation using i-line radiation with a wavelength of 365 nm. TiN and amorphous carbon have been widely used in light-absorbing coatings, and SiON has been used in light-interfering coatings.
Inorganic SiON has been used for anti-reflective coatings in submicro-pattern formation processes using a KrF beam,. A recent trend has been to try to use organic compounds in an anti-reflective coating. Based on knowledge to date, the following are prerequisites for an adequate organic anti-reflective coating:
First, during the pattern formation process, the photoresist must not be peeled from the substrate by dissolving in the solvent used in the organic anti-reflective coating. For this reason, the organic anti-reflective coating needs to be designed to form a cross-linked structure, and must not produce chemicals as a by-product.
Second, acid or amine compounds must not migrate in or out of the anti-reflective coating. This is because there is a tendency for “undercutting” at the lower side of the pattern if an acid migrates, and for “footing” if a base such as an amine migrates.
Third, the anti-reflective coating must have a faster etching speed compared to the photoresist layer so that the etching process can be performed efficiently by utilizing the photoresist layer as a mask.
Fourth, the anti-reflective coating must function with a minimal thickness.
Up to now, suitable anti-reflective coatings have not been developed for use in processes for forming a submicro-pattern using an ArF beam. Furthermore, since there is no known inorganic anti-reflective coating which controls the interference from a 193 nm light source, the use of organic chemicals in anti-reflective coatings is currently being studied.
Therefore, it is desirable to use and develop organic anti-reflective coatings that absorb light strongly at specific wavelengths to prevent the standing wave effect and light reflection in lithography processes, and to eliminate the rear diffraction and reflected light from the lower layers.
SUMMARY OF THE INVENTION
The present invention provides novel chemical compounds suitable for use in anti-reflective coatings in photolithography processes for forming submicro-patterns sing 193 nm (Arf) and 248 nm (KrF) light beams in the manufacture of semiconductor devices.
The present invention further provides preparation methods for chemical compounds to be used in anti-reflective coatings.
The present invention also provides anti-reflective coating compositions containing the above-mentioned compounds and preparation methods thereof.
The present invention also provides anti-reflective coatings formed by using the above-mentioned anti-reflective composition, and methods for the formation thereof.
DETAILED DESCRIPTION OF THE INVENTION
Polymers of the present invention are selected from the group consisting of compounds represented by the following general formulas (1), (2) and (3):
wherein, R is hydrogen, a C
1
-C
6
alkyl group, hydroxy or hydroxymethyl; and m:n is the mole ratio of 0.1-0.9:0.1-0.9;
wherein, R is hydrogen, a C
1
-C
6
alkyl group, hyrdoxy or hydroxymethyl; x is an number between 1 and 5; and a:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9: 0.1-0.9:0.1-0.9; and
wherein,
R
1
is hydrogen, methyl or hydroxy; and e is the average degree of polymerization. Preferably e has a value of 3.0~17.0.
The polymers of the present invention are designed to facilitate light absorption at wavelengths of 193 nm and 248 nm by having groups that absorbs light strongly at both wavelengths,
The polymers represented by general formula 1 above can be prepared in accordance with the reaction equation 1 set forth below, wherein polyhydroxystyrene resin (Compound I) and diazonaphthoquinone halide (Compound II) are reacted in a solvent in the presence of an amine:
wherein, R is hydrogen, a C
1
-C
6
alkyl group, hydroxy or hydroxymethyl; Y is a halogen group; and m: n is the mole ratio of 0.1-0.9: 0.1-0.9.
The polymer represented by the general formula 2 above can be prepared in accordance with reaction equation 2 set forth below, wherein poly(styrene-acrylate) resin (Compound III) and diazonaphthoquinone halide (Compound II) are reacted in a solvent in the presence of an amine:
wherein, R is hydrogen, a C
1
-C
6
alkyl group, hydroxy or hydroxymethyl; Y is a halogen group; x is an number from 1 to 5; and a:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9.
The polymer represented by general formula 3 above can be prepared in accordance with reaction equation 3 set forth below, wherein novolac resin (Compound IV) and diazonaphthoquinone halide (Compound II) are reacted in a solvent in the presence of an amine:
wherein, R
1
is hydrogen, methyl or hydroxy; Y is a halogen group; and e is the average degree of polymerization. The raw materials used in the above reactions, polyhydroxystyrene (I), diazonaphthoquinone halide (II), poly(styrene-acrylate) resin (III) and novolac resin (IV), are commercially available or can be synthesized by known methods.
The amine used in preparing the polymers of the present invention is preferably trialkylamine, and more preferably triethylamine.
The solvent used in preparing the polymers of the present invention may be selected from the group consisting of tetrahydrofuran, toluene, benzene, methylethylketone and dioxane.
The reaction temperature of the polymerization process used for preparing the polymers of the present invention is preferably between 50 and 80° C.
The present invention also provides an anti-reflective coating composition containing a polymer of the general formula 1, 2 or 3 alone in an organic solvent.
Anti-reflective coating composition of the present invention may also comprise one of the polymers of general formula 1, 2 or 3 and a light absorbing compound selected from the group consisting of anthracene and its derivatives, fluorenone derivatives, fluorene and it
Baik Ki-Ho
Hong Sung-Eun
Jung Min-Ho
Kim Hyeong-Soo
Henderson Christopher
Hyundai Electronics Industries Co,. Ltd.
LandOfFree
Anti reflective coating polymers and the preparation method... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Anti reflective coating polymers and the preparation method..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Anti reflective coating polymers and the preparation method... will most certainly appreciate the feedback.