Stock material or miscellaneous articles – Composite – Of metal
Reexamination Certificate
2000-03-02
2001-07-10
Jones, Deborah (Department: 1775)
Stock material or miscellaneous articles
Composite
Of metal
C148S270000, C148S275000, C148S285000, C148S577000, C148S695000, C148S698000, C148S699000, C148S700000, C148S701000, C148S702000, C148S415000, C148S416000, C148S417000, C148S437000, C148S438000, C148S439000, C148S440000
Reexamination Certificate
active
06258463
ABSTRACT:
TECHNICAL FIELD
The invention relates to a process for producing anodic coatings with superior corrosion resistance and other properties on aluminum and aluminum alloy surfaces. The invention also relates to the anodic coatings and to the anodically coated articles produced by the process.
BACKGROUND ART
The formation of protective and decorative oxide coatings on aluminum and aluminum alloys by electrolytically anodizing them is a well-known technology. It has been described in many publications including M. F. Stevenson, Jr., “Anodizing”,
Surface Engineering, ASM Handbook
, Volume 5, ASM International, Materials Park, Ohio, 1994, pp. 482-493 and M. Schwartz, “Deposition from Aqueous Solutions: An Overview”, Chapter 10
, Handbook of Deposition Technologies for Films and Coatings
, Second Edition, R. F. Bunshah, ed., pp. 480-590 (543-545). The most commonly used methods of anodizing use electrolytes of chromic acid (Type I per specification MIL-A-8625), sulfuric acid (Type II), or cold sulfuric acid (Type III). The coatings produced by each are based on alumina, but are usually not pure alumina. For example, the coatings produced using a sulfuric acid electrolyte may contain about 18% aluminum sulfate and 1 to 6% water in addition to alumina. (Unless otherwise noted, all compositional percentage used herein will be in percent by weight.) The alumina itself is commonly a hydrated alumina, 2Al
2
O
3
.H
2
O. The oxide coatings are porous and must be sealed to provide adequate corrosion resistance for the aluminum substrate. Hot sealing with pure water may change the alumina coating to Al
2
O
3
.H
2
O which presumably increases the volume of the alumina and decreases the porosity. Other sealants, such as dichromates or silicates, tend to form precipitates in the pores, effectively blocking them.
Semiconductor manufacturers extensively rely on anodized aluminum for tooling devices inside of semiconductor processing chambers. These chambers require tooling having both the dielectric and corrosion protection of anodized aluminum. With the use of more aggressive process gases and the increase in processing voltages and temperatures, tooling anodized by current methods is becoming inadequate for semiconductor processing chambers.
Cryogenic treatment of metals is well known, see, for example, R. M. Pillai, et al, “Deep-Cryogenic Treatment of Metals”, Tool & Alloy Steels, June 1986, pp. 205-208. Cryogenic treatments include those that lower the temperature of the part to a) about −109° F. (−79° C.) using solid carbon dioxide blocks in an insulated chamber containing the part or carbon dioxide to lower the temperature of an organic liquid in which the part is immersed, b) about −112° F. (−80° C.) in a mechanical refrigerator, or c) about −321° F. (−196° C.) by immersion in liquid nitrogen. One of the cryogenic treatments most commonly done is immersion of the part to be treated in liquid nitrogen (sometimes called deep cryogenic treatment), since, generally speaking, the lower the cryogenic temperature, the more effective the treatment. The effect of the treatment varies from alloy to alloy. One of the most common uses of the treatment results in a more complete transformation of retained austenite to martensite and refined precipitation of carbides in some tool steels. In this case, the resulting change in microstucture and other properties increases resistance to wear.
Aluminum alloys have also been cryogenically treated. Most commercially available alloys fall into the following classification:
2xxx alloys of Al—Cu and Al—Cu—Mg
3xxx alloys of Al—Mn—Cu
5xxx alloys of Al—Mg
6xxx alloys of Al—Mg—Si
7xxx alloys of Al—Zn—Mg—Cu
In the case of typical cast alloys the improvement in properties due to cryogenic treatment is attributed to plastic flow during the cooling and reheating of the alloy which alleviates microstrain within the alloy. In work hardened alloys improvements may be due to more complete transformation of phases, and in alloys that can be precipitation hardened improvements may be due to more complete or widely distributed precipitation. Virtually all of the cryogenic treatment of aluminum alloys to date has been directed at increasing resistance to wear and improved mechanical properties.
It is an object of the present invention to provide superior anodic coatings on aluminum or aluminum alloys.
It is a particular object of the present invention to provide anodized coatings having superior corrosion resistance.
It is also an object of the present invention to provide a process for the production of superior anodized coatings on aluminum or aluminum alloys.
It is a particular object of the present invention to provide a process for producing anodized coatings with superior corrosion resistance.
It is yet a further object of the present invention to provide articles of aluminum or aluminum alloys, such as tooling for semiconductor processing chambers, with superior anodized coatings.
It is yet a further object of the present invention to provide articles of aluminum or aluminum alloys, such as tooling for semiconductor processing chambers, with anodized coatings having superior corrosion resistance.
SUMMARY OF THE INVENTION
The invention provides a process for producing superior anodized coatings. It includes the steps of cryogenically treating an aluminum or aluminum alloy substrate. The aluminum or aluminum alloy substrate has an outer surface. Then anodizing the cryogenically treated aluminum or aluminum alloy substrate converts the outer surface of the aluminum or aluminum alloy substrate into an anodized layer. The anodized substrate's coating has a thickness of 0.001 to 0.5 mm and a time to penetration of at least 5 hours for aqueous solutions containing 5 to 7 percent HCl.
DETAILED DESCRIPTION
Surprisingly, it has been found that cryogenically treating aluminum alloys changes the properties of the alloy in such a manner that subsequent anodizing yields a coating that is substantially superior, particularly in corrosion resistance, to the same alloy that has not been given the cryogenic treatment prior to anodizing. The amount of improvement due to the cryogenic treatment may be a function of a number of variables including a) the specific alloy composition and its prior mechanical working and heat treatment, b) the specific cryogenic treatment, and c) the specific anodizing process that is used.
The structure and properties of the aluminum alloy prior to cryogenic treatment may be, as noted above, a function of its thermomechanical history. Further, this initial condition of the alloy may have a bearing on the extent to which the cryogenic treatment changes the structure and properties of the alloy. For example, the extent of change may be different for an alloy such as 6061 in a fully annealed condition or in a T-6 condition. (Aluminum alloy 6061, has a nominal composition by weight of Al-1Mg-0.6Si-0.25Cu-0.20Cr. The fully annealed condition indicated the alloy has been held at 775° F. (412° C.) for 2 to 3 hours and cooled at a rate of not greater than 50° F./h (28° C./h) to less than 500° F. (260° C.), with subsequent cooling at any rate. The T6 condition indicates the alloy has been solution treated and aged at 320 to 350° F. (160 to 176° C.) for 8 to 18 hours.) In spite of a difference in the extent of change due to cryogenic treatment, some improvement in the properties of a subsequently grown anodic coating may be expected. The amount of improvement may also be a function of the specific cryogenic treatment. It is anticipated that lowering the temperature decreases treatment time required and improves the ultimate anodized coating.
A cryogenic temperature as high as about −70° C. or below may provide some improvement, depending upon the work history of the substrate. Advantageously, the cryogenic treatment is at a temperature of about −150° C. for significant improvement after anodizing. While any of the treatments noted above or others may be used, treatment at or near liquid nitrogen temperatures of about &mi
Biederman Blake T.
Jones Deborah
Koehler Robert R.
Praxair S.T. Technology, Inc.
LandOfFree
Anodized cryogenically treated aluminum does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Anodized cryogenically treated aluminum, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Anodized cryogenically treated aluminum will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2500138