Stock material or miscellaneous articles – All metal or with adjacent metals – Composite; i.e. – plural – adjacent – spatially distinct metal...
Patent
1995-04-26
1996-07-09
Ryan, Patrick J.
Stock material or miscellaneous articles
All metal or with adjacent metals
Composite; i.e., plural, adjacent, spatially distinct metal...
428650, 428209, 205 80, 205105, B32B 900
Patent
active
055343562
ABSTRACT:
There is provided an anodizable aluminum substrate having an increased breakdown voltage. The increase in breakdown voltage is achieved by selecting an appropriate aluminum alloy and appropriate processing parameters. Sealing the anodic film increases the breakdown voltage by decreasing corrosion. A preferred sealant is an epoxy cresol novolac having a low room temperature viscosity that cures to a highly cross-linked polymer.
REFERENCES:
patent: 4188652 (1980-02-01), Smolko
patent: 4301765 (1981-11-01), Behn et al.
patent: 4491622 (1985-01-01), Butt
patent: 4495378 (1985-01-01), Dotzer et al.
patent: 4499118 (1985-02-01), Dietz et al.
patent: 4570337 (1986-02-01), Butt
patent: 4582556 (1986-04-01), Butt et al.
patent: 4594770 (1986-06-01), Butt
patent: 4611745 (1986-09-01), Nakahashi et al.
patent: 4682414 (1987-07-01), Butt
patent: 4696851 (1987-09-01), Pryor
patent: 4827377 (1989-05-01), Butt
patent: 4842959 (1989-06-01), Maeda et al.
patent: 4853491 (1989-08-01), Butt
patent: 4862323 (1989-08-01), Butt
patent: 4866571 (1989-09-01), Butt
patent: 4888449 (1989-12-01), Crane et al.
patent: 4939316 (1990-07-01), Mahulikar et al.
patent: 4953001 (1990-08-01), Kaiser, Jr. et al.
patent: 4967260 (1990-10-01), Butt
patent: 5013871 (1991-05-01), Mahulikar et al.
patent: 5055967 (1991-10-01), Sukonnik et al.
patent: 5066368 (1991-11-01), Pasqualoni et al.
patent: 5077595 (1991-12-01), Fukunaga
patent: 5103292 (1992-04-01), Mahulikar
patent: 5256205 (1993-10-01), Schmitt, III et al.
Brock Andrew J.
Holmes Michael A.
Jalota Satish
Liang Dexin
Mahulikar Deepak
Lee Cathy K.
Olin Corporation
Rosenblatt Gregory S.
Ryan Patrick J.
LandOfFree
Anodized aluminum substrate having increased breakdown voltage does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Anodized aluminum substrate having increased breakdown voltage, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Anodized aluminum substrate having increased breakdown voltage will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1866111