Stock material or miscellaneous articles – Composite – Of inorganic material
Reexamination Certificate
2000-08-07
2003-04-22
Jones, Deborah (Department: 1775)
Stock material or miscellaneous articles
Composite
Of inorganic material
C428S702000, C428S699000, C428S469000
Reexamination Certificate
active
06551730
ABSTRACT:
FIELD OF THE INVENTION
This invention refers to Al
2
O
3
based layers having a total thickness of more than 0.3 mm produced on a substrate by plasma jet spraying.
BACKGROUND OF THE INVENTION
Al
2
O
3
layers produced by plasma jet spraying are used in the technology of electric insulation since years.
Thus, the publication DE 195 38 034 C1 describes a high temperature fuel cell comprising at least to ceramic layers of different composition arranged one upon the other, which layers can be produced by plasma jet spraying.
This sequence of different ceramic layers has the advantage that different requirements, such as electrical insulation and the coefficient of thermal linear expansion, are performed separately by different layers. As an example, ZrO
2
and Al
2
O
3
are mentioned as material for said ceramic layers.
Further, the publication U.S. Pat. No. 5,338,577 describes ceramic coated metallic substrates in which ZrO
2
and Al
2
O
3
are applied successively by plasma jet spraying.
Finally, the publication U.S. Pat. No. 4,588,655 describes a powder for plasma jet spraying consisting of Al
2
O
3
and ZrO
2
.
Normally, a breakdown voltage of 15 kV per mm of layer is reached if no humidity is present. However, pure Al
2
O
3
is a relatively brittle material which cannot be spread in layers having a thickness of more than 0.8 mm without incurring the risk of cracking.
OBJECTS OF THE INVENTION
It is a primary object of the present invention to produce Al
2
O
3
based layers having a total thickness of more than 0.3 mm by plasma jet spraying, without generating macrofissures which would clearly reduce dielectric strength.
Another object of the present invention is to provide suitable alloy systems for producing said layers.
Still further objects of the invention will be evident from the following specification and claims.
SUMMARY OF THE INVENTION
The foregoing and other objects, advantages and features of the present invention can be attained by an Al
2
O
3
based layer having a total thickness of more than 0.3 mm produced on a substrate by plasma jet spraying, said Al
2
O
3
based layer having a laminar sandwiched structure wherein at least one Al
2
O
3
layer is interpolated between two intermediate layers, which are produced by plasma jet spraying as well, said intermediate layers consisting of a ceramic laminated material which is different from Al
2
O
3
and which on cooling increases in volume by phase transition.
This structure makes that the Al
2
O
3
layers are compressed by the adjacent intermediate layers increased in volume, thus avoiding generation of macrofissures.
Preferred materials for said intermediate layers are Al
2
O
3
/ZrO
2
and Al
2
O
3
/TiO
2
alloy systems.
In a Al
2
O
3
/ZrO
2
alloy system, on crystallization by phase transition, four crystalline phases are formed, i.e. &agr;-Al
2
O
3
, &ggr;-Al
2
O
3
, cubic ZrO
2
and monoclinic ZrO
2
, which together occupy an increased volume as compared with the original volume immediately after spraying. Thus, the intermediate layers pressurize the adjacent Al
2
O
3
layer. This alloy system normally comprises from 5 to 50 percent by weight, and preferably from 10 to 30 percent by weight, of ZrO
2
.
Similar conditions prevail when using the other alloy systems mentioned above and below. Thus, in a Al
2
O
3
/TiO
2
alloy system preferably the corresponding rutiles are formed. This alloy system normally comprises from 1 to 50 percent by weight, and preferably from 5 to 18 percent by weight, of TiO
2
.
Other alloy systems useful as intermediate layers in the present invention are e.g.:
ZrO
2
/Y
2
O
3
, preferably comprising from 8 to 22 percent by weight of Y
2
O
3
;
Y
2
O
3
/ZrO
2
, preferably from 5 to 15 percent by weight of ZrO
2
;
ZrO
2
/MgO, preferably comprising from 5 to 30 percent by weight of MgO;
ZrO
2
/CeO
2
, preferably comprising from 10 to 15 percent by weight of CeO
2
;
ZrO
2
/CaO, preferably comprising from 2 to 10 percent by weight of CaO.
Preferably, the thickness of said intermediate layers is from 0.1 to 1 mm and the thickness of said Al
2
O
3
layers is from 0.05 to 0.3 mm.
Said intermediate layers of the present invention show a greater tenacity than the Al
2
O
3
layers. This improves the toughness of the total layer. Moreover, they are electrically insulating, thus supporting an improved dielectric strength.
The layers of the present invention may be sealed on their surface with an organic or inorganic material.
Intermediate layers of the present invention consisting of the aforementioned alloy systems, and in particular of an Al
2
O
3
/ZrO
2
aforementioned alloy system, are particularly useful for coating so-called corona rollers.
REFERENCES:
patent: 4402888 (1983-09-01), Runck
patent: 5284698 (1994-02-01), Marshall et al.
patent: 5939219 (1999-08-01), Jansing et al.
patent: 19538034 (1997-01-01), None
Barbezat Gerard
Zimmermann Stefan
Jones Deborah
McNeil Jennifer
Sulzer Metco AG
Tarolli, Sundheim Covell & Tummino L.L.P.
LandOfFree
Aluminum oxide based thick layers produced by plasma jet... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Aluminum oxide based thick layers produced by plasma jet..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Aluminum oxide based thick layers produced by plasma jet... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3011925