ABSTRACT:
An aluminum-alloy main-starting powder for producing a sintered aluminum-alloy consists of from 0.1 to 3.0% of Cu, the balance being Al and unavoidable impurities. Mother alloy powder consists of from 4 to 20% of Mg, from 12 to 30% of Si, and Al and unavoidable impurities in balance.
REFERENCES:
patent: 2155651 (1939-04-01), Goetzpl
patent: 3331684 (1967-07-01), Storchheim
patent: 3359095 (1967-12-01), Foerster et al.
patent: 3366479 (1968-01-01), Storchheim et al.
patent: 3687657 (1972-08-01), Storchheim
patent: 3871877 (1975-03-01), Storchheim
patent: 4177069 (1979-12-01), Kobayashi et al.
patent: 4435213 (1984-03-01), Hildeman et al.
patent: 4460541 (1984-07-01), Singleton et al.
patent: 4592781 (1986-06-01), Cheney et al.
patent: 4702885 (1987-10-01), Odani et al.
patent: 4722751 (1988-02-01), Akechi et al.
patent: 4838936 (1989-06-01), Akechi
patent: 4937042 (1990-06-01), Perkins et al.
patent: 4943319 (1990-07-01), Yanagawa et al.
patent: 5061323 (1991-10-01), De Luccia
patent: 5067994 (1991-11-01), Brubak et al.
Hausner, Henry, "Handbook of PM", 1973, p. 83, 10, Chemical Publishing Co., Inc., NY, NY.
Hirose Youichi
Machida Yoshio
Miura Shin
Sato Mitsuaki
Jenkins Daniel
Showa Denko K.K.
Walsh Donald P.
LandOfFree
Aluminum-alloy powder, sintered aluminum-alloy, and method for p does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Aluminum-alloy powder, sintered aluminum-alloy, and method for p, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Aluminum-alloy powder, sintered aluminum-alloy, and method for p will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-18239