Stock material or miscellaneous articles – Web or sheet containing structurally defined element or... – Adhesive outermost layer
Reexamination Certificate
2000-11-10
2002-10-22
Dawson, Robert (Department: 1712)
Stock material or miscellaneous articles
Web or sheet containing structurally defined element or...
Adhesive outermost layer
C428S337000, C428S515000, C525S186000
Reexamination Certificate
active
06468650
ABSTRACT:
The invention relates to an adhesive composition which is particularly suitable for use on protective films for glossy surfaces such as plastics, metals, glass and coating materials. This composition permits the production of long-lived surface protection films which are easy to unwind from the roll and which adhere reliably but may nevertheless be removed easily and without residue.
As well as its function, the commercial success of a product is nowadays also determined by its flawless appearance. An important design factor is the surface of the article, which is frequently decoratively polished or glossily coated or which for optical reasons must be free from scratches, such as glass surfaces in particular. In order to be able to sell the customer the product in flawless condition, therefore, surface protection is advantageous, particularly in the form of self-adhesive films. This method has become particularly well-established for a number of years in the automotive sector, where exposed paint surfaces such as the roof, engine hood and trunk lid are protected over large areas against environmental effects and mechanical damage using self-adhesive films.
The requirements imposed on a self-adhesive article applied over a large area are stringent. Thus, the film web must be able to be unwound easily from the roll without stretching. The requirements are for a sufficient initial bond strength and a final bond strength which should be achieved after a few days. If the film is exposed to outdoor weathering, a sufficient bond strength must be maintained even under high atmospheric humidity or even rain. The final bond strength must be balanced in such a way that the film is not detached by wind or slipstream but also does not require excessive effort to remove it. It must be detachable without deposit or residue and its light stability must be up to the task at hand. Moreover, the adhesive composition must not adversely affect the quality of the adhesion substrate being protected; such adverse effects are manifested in particular in irreversible deformations in the case of coating material.
The surface protection article must have a stretchability which allows ideally fold-free sticking even on curved surfaces. Especially in the case of transparent surface protection products, the article must be able to be applied to the surface without bubbles. An important component of these stringent requirements is critically influenced by the properties of the adhesive composition.
Frequent use is made of self-adhesive compositions based on polyisobutylene (PIB) or acrylate polymers. PIB has a very poor initial bond strength, which may lead to premature self-induced detachment, and also has only a very limited final bond strength. A particular observation with PIB is of “flaking effects”, i.e., a sudden reduction in bond strength at high removal speeds, so that complete detachment may occur even on fluttering in the wind.
PIB-treated products may be the cause of traffic hazard situations owing to fully detached films which drift onto the windshield of following vehicles.
Acrylate polymers tend to detract in particular from painted surfaces, by flattening the high-gloss surface.
DE 196 35 704 A1 describes a self-adhesive surface protection film made from polyolefins with an adhesive comprising polyethylene vinyl acetate (EVA) with a vinyl acetate content of from 40 mol % to 80 mol %, especially 70 mol %, and with a loss angle tan &dgr; of from 0.6 to 1.0, measured at a temperature of 60° C. and a frequency of 10
−2
Hz, and from 0.4 to 0.7, measured at a temperature of 60° C. and a frequency of 10 Hz. EVA in the claimed form possesses good initial bond strength to paint and good paint compatibility. The high final bond strength to paints and glass surfaces, although it permits highly reliable bonding, nevertheless necessitates a disproportionately great effort when removing the film, which may adversely affect the health of persons for whom the demasking is a daily task. Moreover, because of the high bond strength, tearing during the demasking operation is a frequent occurrence, and means that the film cannot be removed in one piece.
A known technique for reducing bond strength is to incorporate fillers or plasticizers into the adhesive compositions. Examples of suitable fillers are chalk, zinc oxide or silicates. Although these effectively reduce the bond strength, they cause deterioration on the sensitive substrate surfaces: for example, matt areas on glossy paint surfaces. Plasticizers such as waxes, oils or low molecular mass rubbers likewise, it is true, alter the bonding characteristics. Especially at high temperatures, however, these plasticizers may be exuded and form deposits or may reduce the cohesiveness of the composition, which can lead to residues of composition, predominantly at the edges and in folds. A particular risk originates from the low molecular mass substances, which are able to diffuse into the surfaces and cause swelling therein or even have a discoloring effect following insolation (UV light exposure).
It is an object of the invention to provide a self-adhesive composition for surface protection films, and to provide films coated with the self-adhesive composition of the invention, which do not exhibit the above-described disadvantages of the prior art, or not to the same extent. In particular, the adhesive composition should possess not only a pronounced initial bond strength but also a balanced final bond strength which prevents the film from detaching as a result of wind, for example, while allowing the film to be removed without extraordinary effort.
This object is achieved by means of an adhesive composition as laid down in the main claim. The subclaims relate to advantageous developments of the adhesive composition and to the use of the adhesive composition on surface protection films.
The invention accordingly provides the formulation of a self-adhesive composition for a surface protection, comprising a base polymer of polyethylene-vinyl acetate (EVA) having a vinyl acetate fraction of from 40 to 80% by weight and a melt index MFI in accordance with ISO 1133 (AN/4) of from 0.5 to 25 g/10 min at 190° C. and 2.16 kg, which is blended with a polyether having a fraction of from 1 to 35% by weight of the form
XO—[(CH
2
)
4
—O]—Y (1)
or
XO—[(CH(CH
3
)—CH
2
—O]—Y (2)
having a weight-average molecular weight M
w
of from 200 to 100,000 g/mol, X and Y being selected from the group consisting of H—, (C
n
H
2n+1
)— where n is from 1 to 20, CH
2
═CHCO—, CH
3
CH(NH
2
)CH
2
—, 2,3-epoxypropyl, C
6
H
5
—CO—, and CH
2
═C(CH
3
)—CO—.
In one preferred embodiment, the adhesive composition is made up as follows:
from 65 to 98% by weight, preferably from 75 to 95% by weight, of EVA,
where the EVA may in particular have a VA fraction of from 40 to 80% by weight, preferably from 50 to 65% by weight, and a melt index MFI of from 0.5 to 25 g/10 min at 190° C. and 2.16 kg, preferably from 1 to 5 g/10 min at 190° C. and 2.16 kg, or mixtures of different EVA grades within these limits, and
from 2 to 35% by weight, preferably from 5 to 20% by weight, of a polyether of type (1) or (2) having a weight-average molecular weight M
w
of from 200 to 100,000 g/mol, preferably from 1000 to 20,000 g/mol.
The EVA in the form described forms the polymer framework of the adhesive composition, with a moderately pronounced tack on polished and/or glossy metal, a plastics, glass and paint surfaces and a rapidly increasing bond strength thereon, which attains its ultimate value within a few days, this value being achieved more quickly under the action of heat.
Since the polymer framework in question is chemically uncrosslinked, and on the basis of its monomer proportion is only very slightly crystalline, the molecular weight, which correlates directly to the MFI, assumes a decisive position With regard to the cohesiveness of the adhesive composition. An MFI of from 1 to 5 has proven to be a favorable value. The addition of an EVA fraction h
Dawson Robert
Keehan Christopher M.
Norris & McLaughlin & Marcus
tesa AG
LandOfFree
Adhesive composition and surface protection films produced... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Adhesive composition and surface protection films produced..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Adhesive composition and surface protection films produced... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2938555