ABSTRACT:
The invention relates to a mulching paper degradation process as well as to the mulching paper for implementing the process. As will be described below, the invention also relates to an enzymatic solution for implementing the said process.
In the rest of the description, the degradation process and the mulching paper of the invention are more particularly described in relation to the mulching of lettuces.
However, the paper applies to the mulching of all types of plants, such as strawberry plants, vines, tomatoes, courgettes, aubergines, peppers, cucumbers, shallots, etc.
Several mulching materials have been proposed.
Firstly, black plastic sheeting is known which has the advantage of being strong, despite its low weight per unit area, and thus being weather-resistant. However, such plastic sheeting has a certain number of drawbacks, especially that of not being biodegradable. For obvious environmental reasons, plastic cannot be buried in the soil. Consequently, when the harvesting has been completed and the grower wishes to plough his land, he must completely remove the plastic. The cost of this operation is estimated to be 20% of the total cost of the mulching.
Moreover, since the plastic heats up very quickly when exposed to solar rays, the lettuce leaves close to the ground adhere and remain adhered to the mulching film and therefore can only be removed with removal of this film. It is estimated that the removal of one ton of plastic entails the removal of one ton of plants and earth that have remained attached to the said plastic. Consequently, the plastic is virtually unrecyclable, the cost of washing it being unacceptably high for such an operation.
To solve these various problems, mulching papers have been developed at the same time. Such papers, more particularly described in documents FR-A-2,016,071, are treated with urea-formaldehyde resins so as to increase their wet strength and thus decrease the risk of tearing when used on the ground.
However, despite this treatment, the paper can break due to the effect of the watering phases, which expand the paper, and of the drying phases which retighten the paper.
Moreover, and above all, the treatment of the paper with hydrophobic resins inevitably results in its biodegradability slowing down. It has in fact been found that complete biodegradation of these types of paper is achieved only after 2 years.
In other words, one is faced with the complex problem of using a mulching paper which is weather resistant over a defined period but which at the same time can be degraded in a minimum time after harvesting.
To solve this problem, the Applicant has developed a process for the accelerated degradation of mulching paper whose cellulose fibres are impregnated with a hydrophobic resin giving the said paper a weather-resistant character, in which an enzymatic solution capable of degrading both the resin and the cellulose is sprayed on to the paper.
In other words, the process of the invention consists in depositing over the growing area a paper whose fibres are impregnated with a resin providing it with wet strength, and therefore making it non-tearable, while being compatible with the period of use. Thus with regard to strawberry plants, for example, the paper must be kept in place over the growing area for 9 months, whereas this period is only 6 weeks in the case of lettuces. After harvesting, the paper is degraded by spraying an enzymatic solution, the said solution allowing not only the rate of degradation of the cellulose to be considerably accelerated but also preventing any accumulation of resin in the soil by degradation of the resin. To further accelerate the degradation of the paper, the ground is then ploughed so as to bury the paper in the soil.
According to a first characteristic of the process of the invention, the hydrophobic resin is chosen from the group comprising urea-formaldehyde resins, melamine-formaldehyde resins, polyamide-amine-epichlorohydrin resins, polyethyleneimine resins and starch derivatives, by themselves or as a mixture.
These resins are known to those skilled in the art and are specifically described in document “le point sur . . . ”, No. 11, January 1986 from Centre Technique du Papier de Grenoble [Grenoble Paper Technical Centre].
In one advantageous embodiment, the chosen resins are polyamide-amine-epichlorohydrin resins.
Moreover, in order to degrade not only the resin but also the cellulose, the enzymatic solution comprises enzymes capable of catalyzing the hydrolysis of resin-resin, resin-cellulose and cellulose-cellulose bonds.
In the rest of the description and in the claims, the expression “resin-resin bonds” should be understood to mean the hydrolyzable bonds between monomers of the resin.
Likewise, the expression “resin-cellulose bonds” should be understood to mean the ester bonds linking the resin to the cellulose.
Finally, the expression “cellulose-cellulose bonds” should be understood to mean the glycosidic bonds of the cellulose.
To catalyze the hydrolysis of the ester bonds linking the resin to the cellulose, the enzyme chosen will be an esterase.
Likewise, to catalyze the hydrolysis of the glycosidic bonds of the cellulose, the enzyme will be a cellulase chosen from the group comprising exocellobiohydrolases, endoglucanases and &bgr;-glucosidases, alone or as a mixture.
Finally, the choice of enzyme capable of catalyzing the hydrolysis of the bonds between monomers forming the resin will be chosen depending on the nature of the said bonds.
In practice, with regard to polyamide-amine-epichlorohydrin resins, the enzyme will be chosen from the group comprising amidases and aminases.
As already stated, the invention also relates to the mulching paper for implementing the process described above.
Apart from the fact that the mulching paper of the invention must have a composition such that it can be degraded according to the process described above, it must also have a certain number of properties allowing it to be used as mulching material.
Thus, the paper must be resistant to the weather, such as rain and wind, and to extreme temperature conditions, such as cold and hot conditions, and consequently must have excellent mechanical properties.
Consequently, the Applicant was set the objective of obtaining a paper having a bursting strength of between 150 and 250 kPa.
Another characteristic that the paper must have is that of being permeable to water in so far as the spraying water must be able to irrigate the soil and the roots of the plants. However, the pores in the paper must have a volume such that they limit the evaporation of water lying beneath the mulching so as to preserve'sufficient moisture in the soil.
To obtain such properties, the Applicant set the objective of obtaining a paper having an air permeability of between 1500 and 3500 cm
3
over an area of 10 cm
2
under a vacuum of 1 kPa in sixty seconds.
To achieve all these objectives, the mulching paper of the invention is characterized in that it comprises a fibrous composition containing, by weight:
from 40 to 60%, advantageously 50%, coniferous unbleached kraft paper pulp;
from 10 to 30%, advantageously 20%, deciduous unbleached kraft paper pulp;
from 20 to 40%, advantageously 30%, deinked packaging pulps.
The unbleached kraft paper pulps and their method of manufacture are well known to those skilled in the art. Likewise, the deinked packaging pulps are known as resulting from packaging residues.
According to another characteristic, the mulching paper furthermore contains from 0.5 to 15% resin, advantageously from 7 to 8%, resin by weight with respect to the weight of the paper.
For a resin concentration of less than 0.5% by weight, the paper does not have a sufficiently high wet strength and it tears during spraying or when it rains. For a resin concentration of greater than 15% by weight, a paper having optimized mechanical properties is not obtained, so that the paper becomes economically less advantageous.
Moreover, to avoid the development of microorganisms on the surface of the paper, the paper fu
Bouvier Léonie
Dussaud Joseph
Ahlstrom Paper Group Research & Competence Center
Gellner Jeffrey L.
Gioeni, Esq. Mary Louise
Heslin Rothenberg Farley & & Mesiti P.C.
Poon Peter M.
LandOfFree
Accelerated mulching paper degradation process and mulching... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Accelerated mulching paper degradation process and mulching..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Accelerated mulching paper degradation process and mulching... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3128773